(Meth)acrylic acid/itaconic acid copolymers, their preparation and use as antiscalants
Assignee: Pfizer Inc
•
Filing: 1982-07-22
•
Granted: 1984-11-27
•
Expires: 2002-07-22
Abstract
Abstract Substantially homogeneous (meth)acrylic acid/itaconic acid copolymers of number average molecular weight of 500 to 7000 are prepared by copolymerizing in aqueous solution 5 to 90 mole percent acrylic or methacrylic acid monomer with 95 to 10 mole percent itaconic acid monomer at 80 DEG to 120 DEG C. in the presence of a polymerization initiator, the acrylic or methacrylic acid monomer and at least half of the initiator being added separately and continuously to the itaconic acid monomer throughout the polymerization period. The copolymers are employed at a level of from about 0.1 to 100 ppm for prevention of alkaline calcium and magnesium scale formation, such as during seawater evaporative desalination.
Inventors
- 👤 Stanley W. Walinsky
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:40
CPC Classifications
C; C02; C02F; C02F5/00; C02F5/08; C02F5/10; C08; C08F; C08F222/00; C08F222/02; C08F220/00; C08F220/02; C08F220/04; C08F220/06; Y; Y10; Y10S; Y10S525/00; Y10S525/902
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
123 words
A process for preparing a substantially homogeneous (meth)acrylic acid/itaconic acid copolymer of number average molecular weight from about 500 to 7000, which comprises: contacting in aqueous medium from about 95 to 10 mole percent itaconic acid monomer with from about 5 to 90 mole percent acrylic or methacrylic acid monomer over a period of from about 2 to 8 hours at a temperature of from about 80° to 120° C. in the presence of from about 5 to 20 mole percent polymerization initiator, based on the total amount of said monomers, said acrylic or methacrylic acid monomer and at least half of said initiator being added separately and essentially continuously throughout said period to said itaconic acid monomer in solution in said medium.
Claim 2
Dependent Claim
123 words
A process for preparing a substantially homogeneous (meth)acrylic acid/itaconic acid copolymer of number average molecular weight from about 500 to 7000, which comprises: contacting in aqueous medium from about 95 to 10 mole percent itaconic acid monomer with from about 5 to 90 mole percent acrylic or methacrylic acid monomer over a period of from about 2 to 8 hours at a temperature of from about 80° to 120° C. in the presence of from about 5 to 20 mole percent polymerization initiator, based on the total amount of said monomers, said acrylic or methacrylic acid monomer and at least half of said initiator being added separately and essentially continuously throughout said period to said itaconic acid monomer in solution in said medium.
Claim 3
Dependent Claim
36 words
The process of claim 1 wherein said itaconic acid monomer and from about 2 to 25 percent of said initiator are dissolved in said medium and the remainder of said initiator is introduced over said period.
Claim 4
Dependent Claim
27 words
The process of claim 1 or 2 wherein the resulting copolymer solution is maintained at said temperature for from about 10 to 120 minutes following said addition.
Claim 5
Dependent Claim
12 words
The process of claim 1 wherein said initiator is a redox system.
Claim 6
Dependent Claim
29 words
The process of claim 1 wherein from about 95 to 60 mole percent itaconic acid monomer is copolymerized with from about 5 to 40 mole percent methacrylic acid monomer.
Claim 7
Dependent Claim
95 words
The process of claim 3 wherein from about 5 to 40 mole percent methacrylic acid monomer, from about 1 to 2 mole percent sodium persulfate and from about 6 to 12 mole percent sodium bisulfite are added separately over a period of from about 3 to 5 hours to an aqueous solution of from about 95 to 60 mole percent itaconic acid monomer and from about 0.02 to 0.04 mole percent ferrous sulfate at atmospheric reflux temperature, and said solution is held at that temperature for from about 45 to 75 minutes following said addition.
References Cited (Backward Citations)
US2547815A
Cited
US2783217A
Cited
US3308067A
Cited
US3366509A
Cited
US3507647A
Cited
US3738972A
Cited
GB2054548A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-27 | 1988-05-28 | 1988-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-27 | 1992-05-28 | 1992-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-27 | 1996-05-28 | 1996-11-27 | $7700.00 | Window Closed / Lapsed |