Abstract A silicon carbide fiber reinforced glass-ceramic matrix composite is disclosed having high strength, fracture toughness, and improved oxidative stability even at high temperature use, e.g., in excess of 1000° C. The composite is made up of a plurality of glass-ceramic layers, each layer reinforced with a plurality of unidirectional continuous length silicon carbide or discontinuous SiC fibers. The composite is formed by starting with the matrix material (preferably lithium aluminosilicate) in the glassy state and converting it from the glassy state to the crystalline state after densification of the composite. Ta or Nb compounds are added to the matrix composition prior to consolidation to form a reaction or diffusion barrier around the SiC fiber, resulting in composites with high temperature oxidation stability. Substitution of at least part of the Li 2 O in the matrix with MgO results in an even higher temperature stable composite, e.g., up to about 1200° C.
A silicon carbide fiber reinforced glass-ceramic composite exhibiting use temperatures in excess of 1000° C. consisting essentially of about 15% to about 70% by volume silicon carbide fibers implanted within a glass-ceramic matrix consisting essentially of, expressed in terms of weight percent on the oxide basis, about ______________________________________
Li.sub.2 O 1.5-5
Al.sub.2 O.sub.3 15-25
SiO.sub.2 60-75
As.sub.2 O.sub.3 0.5-3
Ta.sub.2 O.sub.5 0-10
Nb.sub.2 O.sub.5 0-10
Ta.sub.2 O.sub.5 and/or Nb.sub.2 O.sub.5
1-10
ZrO.sub.2 1-3
MgO 0-10
______________________________________ said fibers having a reaction-inhibiting, diffusion barrier coating of niobium carbide and/or tantalum carbide thereon.
Claim 2
Dependent Claim
91 words
A silicon carbide fiber reinforced glass-ceramic composite exhibiting use temperatures in excess of 1000° C. consisting essentially of about 15% to about 70% by volume silicon carbide fibers implanted within a glass-ceramic matrix consisting essentially of, expressed in terms of weight percent on the oxide basis, about ______________________________________
Li.sub.2 O 1.5-5
Al.sub.2 O.sub.3 15-25
SiO.sub.2 60-75
As.sub.2 O.sub.3 0.5-3
Ta.sub.2 O.sub.5 0-10
Nb.sub.2 O.sub.5 0-10
Ta.sub.2 O.sub.5 and/or Nb.sub.2 O.sub.5
1-10
ZrO.sub.2 1-3
MgO 0-10
______________________________________ said fibers having a reaction-inhibiting, diffusion barrier coating of niobium carbide and/or tantalum carbide thereon.
Claim 3
Dependent Claim
33 words
A composite according to claim 1 exhibiting use temperatures up to 1200° C., wherein Li 2 O is present in an amount of 2-3.5%, and MgO is present in an amount of 1.5-6%.