US4484988A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for providing metallic articles and the like with wear-resistant coatings
Assignee: RICHMOND METAL FINISHERS Inc dba RMF TECHNOLOGIES A CORP OF VA
•
Filing: 1981-12-09
•
Granted: 1984-11-27
•
Expires: 2001-12-09
Abstract
Abstract This disclosure is concerned with providing metallic articles, such as cutting and drilling tools, gears, bearings and other structures subject to wear in use, with wear-resisting coatings adhered at desired surfaces thereof, preferably in the form of a thin, generally fractional mil, nickel-boron porous deposit within the voids and over the surface of which a molten mixture of soft metal and organic plastic material of low friction coefficient has been adhered. Improved properties are imparted by cryogenic treatment.
Inventors
- 👤 W. W. Robinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-06 02:38
CPC Classifications
C; C23; C23C; C23C18/00; C23C18/16; C23C18/31; C23C18/32; C25; C25D; C25D5/00; C25D5/34; C25D5/48; F; F16; F16C; F16C33/00; F16C33/02; F16C33/04; F16C33/06; F16C33/12; Y; Y10; Y10S; Y10S205/00; Y10S205/917
Claims Analysis
Total Claims: 19
Claim 1
Independent Claim
194 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises, immersing an article surface in a catalytic nucleation plating bath containing a nickel salt and a borohydride reducing agent and controlling the plating to effect a nickel-boron coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heat-treating said surface; electrodepositing upon the said porous surface a deposit of a metal that is substantially softer than said coating and of thickness less than said coating; applying a dry lubricant material to the porous surface; further heat-treating the same to diffuse the softer metal therethrough and to cause the lubricant material and softer metal to flow in molten combined form within the voids of and over the total area of the porous surface, merging therewith; and cooling the article.
Claim 2
Dependent Claim
194 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises, immersing an article surface in a catalytic nucleation plating bath containing a nickel salt and a borohydride reducing agent and controlling the plating to effect a nickel-boron coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heat-treating said surface; electrodepositing upon the said porous surface a deposit of a metal that is substantially softer than said coating and of thickness less than said coating; applying a dry lubricant material to the porous surface; further heat-treating the same to diffuse the softer metal therethrough and to cause the lubricant material and softer metal to flow in molten combined form within the voids of and over the total area of the porous surface, merging therewith; and cooling the article.
Claim 3
Dependent Claim
35 words
A process as claimed in claim 1 and in which said surface is cooled by cryogenic cooling before the deposition of the nickel-boron coating to relieve stresses for improving the load base of the article.
Claim 4
Dependent Claim
24 words
A process as claimed in claim 2 and in which cryogenic cooling is effected at a temperature of the order of about -320° F.
Claim 5
Dependent Claim
36 words
A process as claimed in claim 1 and in which said cooling step is a cryogenic cooling effected after said further heat-treating step to improve the properties of the combined nickel-boron and softer metal lubricant coating.
Claim 6
Dependent Claim
63 words
A process as claimed in claim 1 and in which the further heat-treating is effected first at a relatively low temperature to melt and diffuse the softer metal into the said porous surface and then at a relatively high temperature sufficient to melt the lubricant material to cause a merging of the softer metal and lubricant material together and with the porous surface.
Claim 7
Dependent Claim
22 words
A process as claimed in claim 5 and in which said softer metal is indium and said organic lubricant material is polytetrafluoroethylene.
Claim 8
Dependent Claim
35 words
A process as claimed in claim 6 and in which said relatively low temperature is of the order of about 325° F. and said relatively high temperature is of the order of about 580° F.
Claim 9
Dependent Claim
28 words
A process as claimed in claim 5 and in which said relatively low temperature is applied for about an hour before running up to said relatively high temperature.
Claim 10
Dependent Claim
26 words
A process as claimed in claim 1 and in which said first-named heat-treating step is effected at a temperature of the order of about 650° F.
Claim 11
Dependent Claim
202 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises immersing an article surface in a catalytic nucleation plating bath containing a salt selected from nickel and cobalt and a reducing agent sleected from borohydride and phosphorus salts and controlling the plating to effect a coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heat-treating said surface; electrodepositing upon the said porous surface a deposit of a metal that is substantially softer than said coating and of thickness less than said coating; applying a dry lubricant material to the porous surface; further heat-treating the same to diffuse the softer metal therethrough and to cause the lubricant material and softer metal to flow in molten combined form within the voids of and over the total area of the porous surface, merging therewith; and cooling the article.
Claim 12
Dependent Claim
202 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises immersing an article surface in a catalytic nucleation plating bath containing a salt selected from nickel and cobalt and a reducing agent sleected from borohydride and phosphorus salts and controlling the plating to effect a coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heat-treating said surface; electrodepositing upon the said porous surface a deposit of a metal that is substantially softer than said coating and of thickness less than said coating; applying a dry lubricant material to the porous surface; further heat-treating the same to diffuse the softer metal therethrough and to cause the lubricant material and softer metal to flow in molten combined form within the voids of and over the total area of the porous surface, merging therewith; and cooling the article.
Claim 13
Dependent Claim
164 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises, immersing an article surface in a catalytic nucleation plating bath containing a nickel salt and a borohydride reducing agent and controlling the plating to effect a nickel-boron coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heating-treating said surface; electrodepositing upon said porous surface a metal that is substantially softer than said coating and of a thickness less than that of said coating; further heat-treating the porous surface to diffuse the softer metal therethrough and to cause the softer metal to merge therewith; and cooling the article.
Claim 14
Dependent Claim
164 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises, immersing an article surface in a catalytic nucleation plating bath containing a nickel salt and a borohydride reducing agent and controlling the plating to effect a nickel-boron coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heating-treating said surface; electrodepositing upon said porous surface a metal that is substantially softer than said coating and of a thickness less than that of said coating; further heat-treating the porous surface to diffuse the softer metal therethrough and to cause the softer metal to merge therewith; and cooling the article.
Claim 15
Dependent Claim
39 words
A process as claimed in claim 11, further comprising applying to said porous surface, prior to said further heat-treating, a dry lubricant material that forms a layer of a thickness less than the thickness of the softer metal deposit.
Claim 16
Dependent Claim
39 words
A process as claimed in claim 12 and in which said nickel-boron coating is of a thickness of about 0.07 mils, and said softer metal-dry lubricant forms a layer of a thickness of from about 0.01 to 0.04 mils.
Claim 17
Dependent Claim
171 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises immersing an article surface in a catalytic nucleation bath containing a salt selected from nickel and cobalt and a reducing agent selected from borohydride and phosphorus and controlling the plating to effect a coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heat-treating said surface; electrodepositing upon the said porous surface a metal that is substantially softer than said coating and of a thickness less than that of said coating; further heat-treating the porous surface to diffuse the softer metal therethrough and to cause the softer metal to merge therewith; and cooling the article.
Claim 18
Dependent Claim
171 words
A process for imparting improved wearing and friction-resistant surfaces to metallic articles and the like, that comprises immersing an article surface in a catalytic nucleation bath containing a salt selected from nickel and cobalt and a reducing agent selected from borohydride and phosphorus and controlling the plating to effect a coating at a deposition rate of the order of about half to a few mils per hour; discontinuing the plating nucleation at a fraction of an hour where the coating has adhered to said article surface as a coating of thickness not exceeding 0.09 mil, and still retains voids that provide a porosity of the order of about 20% to 50% more or less to provide a porous surface; heat-treating said surface; electrodepositing upon the said porous surface a metal that is substantially softer than said coating and of a thickness less than that of said coating; further heat-treating the porous surface to diffuse the softer metal therethrough and to cause the softer metal to merge therewith; and cooling the article.
Claim 19
Dependent Claim
39 words
A process as claimed in claim 14, further comprising applying to said porous surface, prior to said further heat-treating, a dry lubricant material that forms a layer of a thickness less than the thickness of the softer metal deposit.
References Cited (Backward Citations)
US3123505A
Cited
US29285A
Cited
US1849293A
Cited
US1965251A
Cited
US2197365A
Cited
US2287948A
Cited
US2358029A
Cited
US2412058A
Cited
US2497988A
Cited
US2532283A
Cited
US2621988A
Cited
US2567791A
Cited
US2658841A
Cited
US2691814A
Cited
US2990296A
Cited
US3096182A
Cited
US3045334A
Cited
US3338726A
Cited
US2949392A
Cited
US3052590A
Cited
US3088889A
Cited
US2978319A
Cited
US3073761A
Cited
US3091549A
Cited
US3128175A
Cited
GB912793A
Cited
US3234031A
Cited
US3211325A
Cited
US3185600A
Cited
US3373054A
Cited
US3254011A
Cited
US3389060A
Cited
US3279936A
Cited
US3490924A
Cited
US3485683A
Cited
US3347760A
Cited
US3674447A
Cited
US3716348A
Cited
US3819428A
Cited
US3726773A
Cited
US3891477A
Cited
USRE29285E
Cited
USRE29285F1
Cited
US4114505A
Cited
US4259409A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-27 | 1988-05-28 | 1988-11-27 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-27 | 1992-05-28 | 1992-11-27 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-27 | 1996-05-28 | 1996-11-27 | $7700.00 | Window Closed / Lapsed |