Pulsed in etching of aluminum foil for use in electrolytic capacitors
Assignee: US Philips Corp
•
Filing: 1981-12-09
•
Granted: 1984-11-20
•
Expires: 2001-12-09
Abstract
Abstract Low-voltage aluminium foil for electrolytic capacitors having an enlarged effective surface, characterized by narrow long channels which repeatedly change their directions. The overall length of the channels, which have a diameter of approximately 0.2 micron is more than 5 microns. The zones on both sides of the foil, which zones have been provided with channels, extend to substantially equal depth over the entire surface, a zone of at least 15 microns in the middle of the cross-section being of compact aluminium. This foil can be obtained by means of pulsed direct current etching.
Inventors
- 👤 Rudolphus P. T. Ruijgrok
- 👤 Gerrit Tempelman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:49
CPC Classifications
H; H01; H01G; H01G9/00; H01G9/004; H01G9/04; H01G9/048; H01G9/055; C; C25; C25F; C25F3/00; C25F3/02; C25F3/04
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
144 words
Aluminum foil for electrolyte capacitors which has an enlarged effective surface due to the provision of channels opening at the surface, characterized in that the channels have an average diameter of 0.2 μm and repeatedly, after a distance of less than approximately 1 μm, change their direction while the overall length of a channel is on an average more than 5 μm and that the zones on either side of the foil, which are provided with said channels, extend to a substantially equal depth over the entire surface, so that a zone of not less than 15 μm thick in the middle of the foil cross-section remains free of channels, the foil having a value of d 2 =loss of volume of aluminum per square cm of at least 25 μm and a product of CV of more than 1000 μF Volt after forming.
Claim 2
Dependent Claim
144 words
Aluminum foil for electrolyte capacitors which has an enlarged effective surface due to the provision of channels opening at the surface, characterized in that the channels have an average diameter of 0.2 μm and repeatedly, after a distance of less than approximately 1 μm, change their direction while the overall length of a channel is on an average more than 5 μm and that the zones on either side of the foil, which are provided with said channels, extend to a substantially equal depth over the entire surface, so that a zone of not less than 15 μm thick in the middle of the foil cross-section remains free of channels, the foil having a value of d 2 =loss of volume of aluminum per square cm of at least 25 μm and a product of CV of more than 1000 μF Volt after forming.
Claim 3
Dependent Claim
123 words
A method of producing aluminum foil as claimed in claim 1, by means of anodic etching in an electrolyte solution with a pulsed direct current having a pulse repetition rate between 35 and 300 Hz and a pulse spacing between 500 and 2000 μsec at a temperature between 60° and 95° C., characterized in that the etching is carried out in an electrolyte solution containing a chloride and having a conductivity of at least 100 mS/cm with an etching current density, related to the direct current portion of between 0.5 and 3 A/dm 2 for such a long period of time that a loss in volume of each cm 2 foil surface (d s ) of at least 25 μm has been attained.
Claim 4
Dependent Claim
52 words
An electrolytic capacitor comprising an etched cathode foil, an etched and formed anode foil and an interposed electrolyte characterized in that the anode foil consists of the aluminum foil as claimed in claim 1 provided with a dielectric layer produced by forming at a voltage of not more than approximately 120 volts.
References Cited (Backward Citations)
US3997339A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-20 | 1988-05-21 | 1988-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-20 | 1992-05-21 | 1992-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-20 | 1996-05-21 | 1996-11-20 | $7700.00 | Window Closed / Lapsed |