Method for directly joining metal pieces to oxide-ceramic substrates
Assignee: BROWN BOVERI and CIE AG
•
Filing: 1983-02-04
•
Granted: 1984-11-20
•
Expires: 2003-02-04
Abstract
Abstract Method for the direct joining of metal pieces which have a surface metal oxide layer, to oxide ceramic substrates by heating the ceramic substrates covered with the metal pieces in an oxygen-containing atmosphere to a temperature above the eutectic temperature of the metal and the metal oxide, but below the melting temperature of the metal. The heating is carried out in a continuous heating furnace in a nitrogen atmosphere with an addition of oxygen of 20 to 50 vpm. The cooling-down in the continuous heating furnace takes place after the solidification of the eutectic melt, in a nitrogen atmosphere which has an oxygen content well below the 20 vpm.
Inventors
- 👤 Klaus Bunk
- 👤 Arno Neidig
- 👤 Georg Wahl
- 👤 Helmut Keser
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 19:45
CPC Classifications
C; C04; C04B; C04B37/00; C04B37/02; C04B37/023; C04B37/026; B; B23; B23K; B23K35/00; B23K35/22; B23K35/38; C04B37/021; C04B2235/00; C04B2235/65; C04B2235/656; C04B2235/6567; C04B2235/658; C04B2235/6581; C04B2235/6583; C04B2235/6584; C04B2237/00; C04B2237/02; C04B2237/12; C04B2237/124; C04B2237/126; C04B2237/30; C04B2237/32; C04B2237/34; C04B2237/343; C04B2237/40; C04B2237/407; H; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/38
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
128 words
A method for the direct joining of metal pieces to ceramic oxide substrates which comprises covering the ceramic substrate with a metal piece having an oxide coating on the side facing the ceramic substrate, heating the substrate covered by the metal piece with an oxide coating to a temperature above the eutectic temperature of the metal and the oxide but below the melting point of the metal to form a eutectic melt in an atmosphere of an inert gas and 20 to 50 volume parts per million oxygen, reducing the temperature to cool and solidify the eutectic melt and after solidification of the eutectic melt continuing cooling while maintaining the ceramic substrate with covering metal piece in an atmosphere of an inert gas in the absence of oxygen.
Claim 2
Independent Claim
128 words
A method for the direct joining of metal pieces to ceramic oxide substrates which comprises covering the ceramic substrate with a metal piece having an oxide coating on the side facing the ceramic substrate, heating the substrate covered by the metal piece with an oxide coating to a temperature above the eutectic temperature of the metal and the oxide but below the melting point of the metal to form a eutectic melt in an atmosphere of an inert gas and 20 to 50 volume parts per million oxygen, reducing the temperature to cool and solidify the eutectic melt and after solidification of the eutectic melt continuing cooling while maintaining the ceramic substrate with covering metal piece in an atmosphere of an inert gas in the absence of oxygen.
Claim 3
Dependent Claim
11 words
Method according to claim 1, wherein the inert gas is nitrogen.
Claim 4
Dependent Claim
12 words
Method according to claim 1, wherein the metal pieces are copper sheets.
Claim 5
Dependent Claim
42 words
Method according to claim 1, wherein the substrate covered by the metal pieces is heated from a temperature of 960° C. to above said eutectic temperature and reduced in temperature to 960° C. in a period of less than about four minutes.
Claim 6
Dependent Claim
42 words
Method according to claim 3, wherein the substrate covered by the metal pieces is heated from a temperature of 960° C. to above said eutectic temperature and reduced in temperature to 960° C. in a period of less than about four minutes.
Claim 7
Dependent Claim
44 words
Method according to claim 1, wherein the atmosphere containing an inert gas with 20-50 vpm oxygen around the metal covered ceramic substrate after the eutectic melt has solidified is changed to an inert gas before the temperature is further reduced to below 900° C.
Claim 8
Dependent Claim
44 words
Method according to claim 2, wherein the atmosphere containing an inert gas with 20-50 vpm oxygen around the metal covered ceramic substrate after the eutectic melt has solidified is changed to an inert gas before the temperature is further reduced to below 900° C.
Claim 9
Dependent Claim
44 words
Method according to claim 3, wherein the atmosphere containing an inert gas with 20-50 vpm oxygen around the metal covered ceramic substrate after the eutectic melt has solidified is changed to an inert gas before the temperature is further reduced to below 900° C.
Claim 10
Dependent Claim
39 words
Method according to claim 1, wherein the atmosphere around the metal covered ceramic substrate is controlled by the introduction into said atmosphere of oxygen and inert gas at spaced points in amounts regulated to maintain the desired oxygen concentration.
Claim 11
Dependent Claim
39 words
Method according to claim 2, wherein the atmosphere around the metal covered ceramic substrate is controlled by the introduction into said atmosphere of oxygen and inert gas at spaced points in amounts regulated to maintain the desired oxygen concentration.
Claim 12
Dependent Claim
39 words
Method according to claim 3, wherein the atmosphere around the metal covered ceramic substrate is controlled by the introduction into said atmosphere of oxygen and inert gas at spaced points in amounts regulated to maintain the desired oxygen concentration.
Claim 13
Dependent Claim
143 words
Method according to claim 1, wherein the metal covered ceramic substrate is conveyed through a continuous heating furnace having a tunnel enclosure with a first entrance preheating zone, a second, a third and a fourth heating zones in which said substrate is rapidly heated above the eutectic to form a eutectic melt and reduced in temperature to solidify the eutectic melt and a fifth exit cooling zone to further cool said substrate, flaps and nitrogen inlets at both ends of the tunnel to prevent ambient air from entering the tunnel, a nitrogen inlet and an oxygen inlet at the entrance of the second heating zone to provide an atmosphere of desired oxygen concentration in the heating zones, and a nitrogen inlet at the outlet of the fourth heating zone to provide a nitrogen atmosphere without significant oxygen content in the fifth cooling zone.
Claim 14
Dependent Claim
12 words
Method according to claim 1, wherein the ceramic oxide is aluminum oxide.
Claim 15
Dependent Claim
12 words
Method according to claim 2, wherein the ceramic oxide is aluminum oxide.
Claim 16
Dependent Claim
12 words
Method according to claim 3, wherein the ceramic oxide is aluminum oxide.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-20 | 1988-05-21 | 1988-11-20 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-20 | 1992-05-21 | 1992-11-20 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-20 | 1996-05-21 | 1996-11-20 | $7700.00 | Window Closed / Lapsed |