Prepreg for making a composite having high elongation and heat resistance and process for making such composite with the prepreg
Assignee: NIPPON GIJUTSU BOEKI CO Ltd
•
Filing: 1983-01-14
•
Granted: 1984-11-13
•
Expires: 2003-01-14
Abstract
Abstract A prepreg for making a composite is disclosed. The prepreg comprising reinforcing fibers impregnated with a resin composition comprising (A) an epoxy resin, (B) a reaction product of an epoxy resin and a butadiene-acrylonitrile copolymer having carboxyl groups on at least both terminals of the molecular chain of the copolymer, and (C) 4,4'-diaminodiphenylsulfone as a curing agent. A composite produced by curing this prepreg is high in both tensile elongation and heat resistance and is used with advantage as primary and secondary structural materials in aircraft.
Inventors
- 👤 Tsuyoshi Minamisawa
- 👤 Masato Andoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 15:11
CPC Classifications
B; B32; B32B; B32B5/00; B32B5/22; B32B5/24; B32B5/26; C; C08; C08G; C08G59/00; C08G59/02; C08G59/12; C08G59/18; C08G59/40; C08G59/50; C08G59/504; C08J; C08J5/00; C08J5/24; C08J5/241; C08J5/243; B32B2260/00; B32B2260/02; B32B2260/021; B32B2260/023; B32B2260/04; B32B2260/046; B32B2305/00; B32B2305/07; B32B2305/076; C08J2363/00
Claims Analysis
Total Claims: 32
Claim 1
Independent Claim
118 words
A prepreg for making a composite having reinforcing fibers impregnated with a resin composition comprising (A) an epoxy resin wherein said epoxy resin of component (A) consists of 50 to 80 wt% based on the total epoxy resin of at least one glycidylamine epoxy resin selected from the group consisting N,N,N',N'-tetraglycidyldiaminodiphenylmethane, and N,N-diglycidylmethane aminophenol glycidyl ether, (B) a reaction product of an epoxy resin and a butadiene-acrylonitrile copolymer having carboxyl groups on at least both terminals of the molecular chain of the copolymer, and (C) 4,4'-diaminodiphenylsulfone as a curing agent and wherein component (B) is used in an amount of 3 to 25 parts by weight, per 100 parts by weight of the epoxy resin as component (A).
Claim 2
Dependent Claim
118 words
A prepreg for making a composite having reinforcing fibers impregnated with a resin composition comprising (A) an epoxy resin wherein said epoxy resin of component (A) consists of 50 to 80 wt% based on the total epoxy resin of at least one glycidylamine epoxy resin selected from the group consisting N,N,N',N'-tetraglycidyldiaminodiphenylmethane, and N,N-diglycidylmethane aminophenol glycidyl ether, (B) a reaction product of an epoxy resin and a butadiene-acrylonitrile copolymer having carboxyl groups on at least both terminals of the molecular chain of the copolymer, and (C) 4,4'-diaminodiphenylsulfone as a curing agent and wherein component (B) is used in an amount of 3 to 25 parts by weight, per 100 parts by weight of the epoxy resin as component (A).
Claim 3
Dependent Claim
31 words
A prepreg according to claim 1 wherein the reinforcing fibers are selected from the group consisting carbon fibers having an elongation of 1.5% or more, glass fibers and aromatic polyamide fibers.
Claim 4
Dependent Claim
54 words
A prepreg according to claim 1 or 2 wherein the epoxy resin as component (A) is at least one resin selected from the group consisting a glycidylamine epoxy resin, a novolak epoxy resin, bisphenol A epoxy resin, a brominated bisphenol A epoxy resin, an urethane-modified bisphenol A epoxy resin, and an alicyclic epoxy resin.
Claim 5
Dependent Claim
33 words
A prepreg according to claim 3 wherein the novolak epoxy resin is at least one resin selected from the group consisting a phenolic novolak epoxy resin and a cresol novolak type epoxy resin.
Claim 6
Dependent Claim
21 words
A prepreg according to claim 3 wherein the glycidylamine epoxy resin has an average epoxy equivalent of from 110 to 150.
Claim 7
Dependent Claim
21 words
A prepreg according to claim 4 wherein the phenolic novolak resin has an average epoxy equivalent of from 160 to 200.
Claim 8
Dependent Claim
21 words
A prepreg according to claim 4 wherein the cresol novolak epoxy resin has an epoxy equivalent of from 180 to 260.
Claim 9
Dependent Claim
22 words
A prepreg according to claim 3 wherein the bisphenol A epoxy resin has an average epoxy equivalent of from 150 to 1,000.
Claim 10
Dependent Claim
22 words
A prepreg according to claim 3 wherein the brominated bisphenol A epoxy resin has an average epoxy equivalent of 200 to 600.
Claim 11
Dependent Claim
22 words
A prepreg according to claim 3 wherein the urethane-modified bisphenol A epoxy resin has an average epoxy equivalent of 200 to 1,000.
Claim 12
Dependent Claim
20 words
A prepreg according to claim 3 wherein the alicyclic epoxy resin has an average epoxy equivalent of 110 to 300.
Claim 13
Dependent Claim
43 words
A prepreg according to claim 1 wherein glycidylamine epoxy resin is combined with at least one epoxy resin selected from the group consisting of a novolak epoxy resin, bisphenol A epoxy resin, a brominated bisphenol A epoxy resin and an urethane-modified epoxy resin.
Claim 14
Dependent Claim
15 words
A prepreg according to claim 1 wherein the butadiene-acrylonitrile copolymer in component (B) is liquid.
Claim 15
Dependent Claim
21 words
A prepreg according to claim 13 wherein said copolymer has a viscosity of from 500 to 8,000 poise at 27° C.
Claim 16
Dependent Claim
23 words
A prepreg according to claim 1 wherein the butadiene-acrylonitrile copolymer in component (B) has an acrylonitrile content of from 10 to 35 wt%.
Claim 17
Dependent Claim
18 words
A prepreg according to claim 1 wherein a nitrile rubber is used as a part of component (B).
Claim 18
Dependent Claim
30 words
A prepreg according to claim 16 wherein the nitrile rubber has a Mooney viscosity of 40 to 110 at 100° C. and an acrylonitrile content of 20 to 45 wt%.
Claim 19
Dependent Claim
36 words
A prepreg according to claim 17 wherein the nitrile rubber is a carboxyl-modified nitrile rubber having not more than 2 wt% of at least one acid selected from the group consisting acrylic acid and methacrylic acid.
Claim 20
Dependent Claim
35 words
A prepreg according to claim 16 wherein the nitrile rubber as component (B) is used in an amount of from 20 to 130 parts by weight, per 100 parts by weight of the butadiene-acrylonitrile copolymer.
Claim 21
Dependent Claim
21 words
A prepreg according to claim 1 wherein the 4,4'-diaminodiphenylsulfone as component (C) is used in combination with a curing accelerator thereof.
Claim 22
Dependent Claim
30 words
A prepreg according to claim 20 wherein the accelerator is used in an amount of from 0.05 to 3.0 parts by weight per 100 parts by weight of component (A).
Claim 23
Dependent Claim
20 words
A prepreg according to claim 1 wherein the 4,4'-diaminodiphenylsulfone is used in combination with a dicyandiamide and an accelerator thereof.
Claim 24
Dependent Claim
29 words
A prepreg according to claim 22 wherein said dicyandiamide is used in an amount of 0.3 to 1.2 parts by weight per 100 parts by weight of component (A).
Claim 25
Dependent Claim
24 words
A prepreg according to claim 1 wherein the total amount of component (C) is from 20 to 45 parts by weight of component (A).
Claim 26
Dependent Claim
26 words
A prepreg according to claim 1 wherein the resin content of the prepreg is from 30 to 50 wt% based on the weight of the prepreg.
Claim 27
Dependent Claim
25 words
A prepreg according to claim 1 which contains fine particles of at least one material selected from the group consisting of silica and glass particles.
Claim 28
Dependent Claim
12 words
A prepreg according to claim 1 which contains fine antimony trioxide particles.
Claim 29
Dependent Claim
115 words
A process for producing a composite by curing a prepreg having reinforcing fibers impregnated with a resin composition comprising (A) an epoxy resin, wherein said epoxy resin of component (A) consists of 50 to 80 wt%, based on the total epoxy resin, of at least one glycidylamine epoxy resin selected from the group consisting N,N,N',N'-tetraglycidyldiaminodiphenylmethane and N,N-diglycidylmethane aminophenol glycidyl ether, (B) a reaction product of an epoxy resin and a butadiene-acrylonitrile copolymer having carboxyl groups on at least both terminals, and (C) 4,4'-diaminodiphenylsulfone as a curing agent and wherein component (B) is used in an amount of 3 to 25 parts by weight, per 100 parts by weight of the epoxy resin as component (A).
Claim 30
Dependent Claim
115 words
A process for producing a composite by curing a prepreg having reinforcing fibers impregnated with a resin composition comprising (A) an epoxy resin, wherein said epoxy resin of component (A) consists of 50 to 80 wt%, based on the total epoxy resin, of at least one glycidylamine epoxy resin selected from the group consisting N,N,N',N'-tetraglycidyldiaminodiphenylmethane and N,N-diglycidylmethane aminophenol glycidyl ether, (B) a reaction product of an epoxy resin and a butadiene-acrylonitrile copolymer having carboxyl groups on at least both terminals, and (C) 4,4'-diaminodiphenylsulfone as a curing agent and wherein component (B) is used in an amount of 3 to 25 parts by weight, per 100 parts by weight of the epoxy resin as component (A).
Claim 31
Dependent Claim
22 words
A process for producing a composite according to claim 28 wherein a nitrile rubber is used as a part of component (B).
Claim 32
Dependent Claim
23 words
A process for producing a composite according to claim 28 wherein the 4,4'-diaminodiphenylsulfone is used in combination with dicyandiamide and an accelerator thereof.
References Cited (Backward Citations)
JPS5120998A
Cited
US4107128A
Cited
JPS5258799A
Cited
JPS5274655A
Cited
JPS53102996A
Cited
US4269759A
Cited
JPS5721450A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-13 | 1988-05-14 | 1988-11-13 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-13 | 1992-05-14 | 1992-11-13 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-13 | 1996-05-14 | 1996-11-13 | $7700.00 | Window Closed / Lapsed |