Method for production of magnetic recording media
Assignee: Fujifilm Holdings Corp
•
Filing: 1983-12-08
•
Granted: 1984-11-06
•
Expires: 2003-12-08
Abstract
Abstract A method for the production of a magnetic recording medium is disclosed. The method involves coating a support base with a magnetic coating composition. The support base has a percent thermal shrinkage in the direction corresponding to the longitudinal direction of the support base of not more than 0.15%. The magnetic coating composition contains a compound having not less than two acrylate groups or methacrylate groups in the molecule and includes ferromagnetic fine powder dispersed therein. After coating the magnetic coating composition on the support base it is irradiated with an electron beam. The resulting medium has excellent electromagnetic properties, durability and improved tape skew characteristics. Further, the composition has good storage stability.
Inventors
- 👤 Hiroshi Hashimoto
- 👤 Tsutomu Okita
- 👤 Noburo Hibino
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 09:32
CPC Classifications
G; G11; G11B; G11B5/00; G11B5/62; G11B5/68; G11B5/70; G11B5/702; G11B5/7023; G11B5/7026
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
86 words
A method for producing a magnetic recording medium, comprising the steps of: coating a support base with a magnetic coating composition, wherein the support base has a percent thermal shrinkage in the direction corresponding to the longitudinal direction of the support base of not more than 0.15% and further wherein the magnetic coating composition contains a compound having not less than two acrylate groups or methacrylate groups per molecule, and a ferromagnetic fine powder dispersed therein; and irradiating the coated support base with an electron beam.
Claim 2
Independent Claim
86 words
A method for producing a magnetic recording medium, comprising the steps of: coating a support base with a magnetic coating composition, wherein the support base has a percent thermal shrinkage in the direction corresponding to the longitudinal direction of the support base of not more than 0.15% and further wherein the magnetic coating composition contains a compound having not less than two acrylate groups or methacrylate groups per molecule, and a ferromagnetic fine powder dispersed therein; and irradiating the coated support base with an electron beam.
Claim 3
Dependent Claim
48 words
A method as claimed in claim 1, wherein the magnetic coating composition includes a compound selected from the group consisting of diethylene glycol diacrylate, triethylene glycol diacrylate, tetraethylene glycol diacrylate, trimethylolpropane triacrylate, pentaerythritol tetraacrylate, diethylene glycol dimethacrylate, triethylene glycol trimethacrylate, tetraethylene glycol dimethacrylate, trimethylolpropane trimethacrylate and pentaerythritol tetramethacrylate.
Claim 4
Dependent Claim
52 words
A method as claimed in claim 1, wherein the ferromagnetic fine powder is ferromagnetic alloy powder having a metallic content of not less than 75 wt% and the metallic portion contains 80 wt% or more of a metal selected from the group consisting of Fe, Co, Ni, Fe-Co, Fe-Ni, Co-Ni and Fe-Co-Ni.
Claim 5
Dependent Claim
34 words
A method as claimed in claim 1, wherein the electron beam has an acceleration voltage of from 100 to 1,000 kv and applies an absorption dose in the range of 0.5 to 20 megarads.
Claim 6
Dependent Claim
36 words
A method as claimed in claim 4, wherein the electron beam has an acceleration voltage in the range of 150 to 300 kv and applies an absorption dose in the range of 3 to 15 megarads.
Claim 7
Dependent Claim
39 words
The method of claim 1 wherein to achieve the percent thermal shrinkage the support base is heated for 2 to 20 seconds at a temperature of 100° to 140° C. under a tension of 0 to 8 kg/100 cm·width.
Claim 8
Dependent Claim
29 words
The method of claim 6 wherein said heating is for 3 to 10 seconds at 110° to 130° C. at a tension of 0 to 4 kg/100 cm· width.
Claim 9
Dependent Claim
23 words
The method of claim 1 wherein the magnetic coating composition yields a magnetic layer having a thickness of from 1 to 50 μm.
Claim 10
Dependent Claim
23 words
The method of claim 7 wherein the magnetic coating composition yields a magnetic layer having a thickness of from 2 to 10 μm.
Claim 11
Dependent Claim
19 words
The method of claim 9 wherein the magnetic recording medium exhibits a skew of not more than 17 μsec.
References Cited (Backward Citations)
JPS5431937A
Cited
US4343831A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |