High-temperature Hg anneal for HgCdTe
Assignee: Raytheon Co
•
Filing: 1984-03-21
•
Granted: 1984-11-06
•
Expires: 2004-03-21
Abstract
Abstract The dislocation density near the surface of Hg 1-x Cd x Te alloys is substantially reduced by annealing the material at around 600° C. in a mercury saturated ambient for periods of four hours or more, prior to post annealing at lower temperatures to control the metal vacancy concentration. This procedure allows dislocation reduction by climb, reduces the concentration of metal vacancies which can collapse to form dislocation loops or contribute to dislocation multiplication, and reduces tellurium precipitates which contribute to dislocation multiplication during subsequent post annealing.
Inventors
- 👤 Herbert F. Schaake
- 👤 John H. Tregilgas
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 06:28
CPC Classifications
C; C22; C22C; C22C1/00; C22C1/007; H; H10; H10P; H10P95/00; H10P95/90; Y; Y10; Y10S; Y10S438/00; Y10S438/971
Claims Analysis
Total Claims: 6
Claim 1
Independent Claim
124 words
A method for preparation of approximately stoichiometric alloys of (Hg, Cd) Te having a preselected proportion of mercury to cadmium, comprising the steps of: providing a bulk alloy of mercury, cadmium, and tellurium, said bulk alloy containing an excess of tellurium over said predetermined composition; annealing said bulk alloy, at an intermediate temperature which is greater than 350° C. and less than the melting point of said bulk alloy, in a saturated atmosphere of mercury, whereby the composition of said bulk alloy is converted to an intermediate alloy having a smaller excess of tellurium; and subsequently annealing said intermediate alloy at a second temperature, said second temperature being less than 325° C., to compositionally adjust said intermediate alloy to achieve a desired carrier concentration.
Claim 2
Independent Claim
124 words
A method for preparation of approximately stoichiometric alloys of (Hg, Cd) Te having a preselected proportion of mercury to cadmium, comprising the steps of: providing a bulk alloy of mercury, cadmium, and tellurium, said bulk alloy containing an excess of tellurium over said predetermined composition; annealing said bulk alloy, at an intermediate temperature which is greater than 350° C. and less than the melting point of said bulk alloy, in a saturated atmosphere of mercury, whereby the composition of said bulk alloy is converted to an intermediate alloy having a smaller excess of tellurium; and subsequently annealing said intermediate alloy at a second temperature, said second temperature being less than 325° C., to compositionally adjust said intermediate alloy to achieve a desired carrier concentration.
Claim 3
Dependent Claim
33 words
The process of claim 1, wherein a bulk recrystallization anneal is performed on an ingot to produce said bulk alloy, and wherein said ingot is sliced into wafers prior to said intermediate-temperature anneal.
Claim 4
Dependent Claim
25 words
The process of claim 2, wherein said wafers are etched to remove surface damage after said slicing step and prior to said intermediate-temperature anneal step.
Claim 5
Dependent Claim
17 words
The process of claim 3 wherein said intermediate temperature anneal is performed for at least 4 hours.
Claim 6
Dependent Claim
21 words
The process of claim 3, wherein said intermediate temperature anneal is performed at a temperature in the neighborhood of 600° C.
References Cited (Backward Citations)
US3723190A
Cited
US3954518A
Cited
US3963540A
Cited
US3979232A
Cited
US4028145A
Cited
US4116725A
Cited
US4374684A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-11-06 | 1988-05-07 | 1988-11-06 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-11-06 | 1992-05-07 | 1992-11-06 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-11-06 | 1996-05-07 | 1996-11-06 | $7700.00 | Window Closed / Lapsed |