Stable dispersions for use in photographic film having an opaque backing layer
Assignee: EIDP Inc
•
Filing: 1982-08-02
•
Granted: 1984-10-30
•
Expires: 2002-08-02
Abstract
Abstract In preparing an opaque backing layer for a photographic film, superior covering power and coating dispersion stability are obtained by (1) dispersing carbon black in a minor phase of polyvinyl pyrrolidone/vinyl acetate copolymer before addition of a major phase of polyvinyl alcohol, and (2) delaying the addition of surfactant or coating aids until after complete mixing of the polyvinyl alcohol with the solid carbon black dispersion. This coating dispersion is particularly useful for the preparation of a dischargeable opaque backing layer for a diffusion transfer film element.
Inventors
- 👤 Robert W. Ashcraft
- 👤 Rusty E. Koenigkramer
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 23:01
CPC Classifications
G; G03; G03C; G03C1/00; G03C1/76; G03C1/825; G03C1/835
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
102 words
A photographic element prepared by coating a support on one side with a photosensitive silver halide emulsion layer and on the other side with an opaque backing layer containing an opacifying agent, characterized in that the coating composition for the backing layer is prepared by this sequence: (1) polyvinyl pyrrolidone/vinyl acetate copolymer is two-roll milled with carbon black which has been prewetted with a liquid which will swell or tackify the copolymer to produce a solid dispersion; (2) the solid dispersion is added to and mixed with a polyvinyl alcohol solution, and (3) suitable plasticizers, surfactants and coating aids are then added.
Claim 2
Dependent Claim
102 words
A photographic element prepared by coating a support on one side with a photosensitive silver halide emulsion layer and on the other side with an opaque backing layer containing an opacifying agent, characterized in that the coating composition for the backing layer is prepared by this sequence: (1) polyvinyl pyrrolidone/vinyl acetate copolymer is two-roll milled with carbon black which has been prewetted with a liquid which will swell or tackify the copolymer to produce a solid dispersion; (2) the solid dispersion is added to and mixed with a polyvinyl alcohol solution, and (3) suitable plasticizers, surfactants and coating aids are then added.
Claim 3
Dependent Claim
128 words
A process for preparing a photographic support wherein a base is coated with a dispersion comprising PVA, carbon black, polyvinyl pyrrolidone/vinyl acetate copolymer, plasticizer and surfactant, and the coating is dried to produce an opaque layer, characterized in that the aforesaid dispersion is prepared by the steps of: (1) mixing a polyvinyl pyrrolidone/vinyl acetate copolymer with carbon black which has been prewetted with a nonaqueous liquid which will swell or tackify the copolymers; (2) two-roll milling the mixture to form an extruded sheet, and breaking up the dried sheet into carbon black chips; (3) adding said carbon black chips to an aqueous polyvinyl alcohol solution, with stirring, to form an aqueous dispersion; and (4) subsequently adding one or more surfactants, plasticizers, or coating aids to stabilize the dispersion.
Claim 4
Dependent Claim
128 words
A process for preparing a photographic support wherein a base is coated with a dispersion comprising PVA, carbon black, polyvinyl pyrrolidone/vinyl acetate copolymer, plasticizer and surfactant, and the coating is dried to produce an opaque layer, characterized in that the aforesaid dispersion is prepared by the steps of: (1) mixing a polyvinyl pyrrolidone/vinyl acetate copolymer with carbon black which has been prewetted with a nonaqueous liquid which will swell or tackify the copolymers; (2) two-roll milling the mixture to form an extruded sheet, and breaking up the dried sheet into carbon black chips; (3) adding said carbon black chips to an aqueous polyvinyl alcohol solution, with stirring, to form an aqueous dispersion; and (4) subsequently adding one or more surfactants, plasticizers, or coating aids to stabilize the dispersion.
Claim 5
Dependent Claim
35 words
The process of claim 2 in which the carbon black is prewetted with a liquid comprising one or more members of the group consisting of methanol, ethanol, isopropanol, acetone, methylene chloride, and methyl ethyl ketone.
Claim 6
Dependent Claim
24 words
The process of claim 3 wherein a portion of the liquid comprises an inert diluent selected from the group consisting of hexane and heptane.
Claim 7
Dependent Claim
18 words
The process of claim 2 wherein step 3 is conducted at a temperature of not exceeding 65° C.
Claim 8
Dependent Claim
65 words
A storage-stable coating solution prepared by the steps of: (1) prewetting carbon black with a nonaqueous liquid which will swell or tackify polyvinyl pyrrolidone/vinylacetate copolymer, (2) two-roll milling the prewetted carbon black with the copolymer to produce storage-stable carbon chips, (3) dispersing the carbon chips in a polyvinyl alcohol solution, and (4) adding one or more surfactants, plasticizers, or coating aids to stabilize the dispersion.
Claim 9
Dependent Claim
65 words
A storage-stable coating solution prepared by the steps of: (1) prewetting carbon black with a nonaqueous liquid which will swell or tackify polyvinyl pyrrolidone/vinylacetate copolymer, (2) two-roll milling the prewetted carbon black with the copolymer to produce storage-stable carbon chips, (3) dispersing the carbon chips in a polyvinyl alcohol solution, and (4) adding one or more surfactants, plasticizers, or coating aids to stabilize the dispersion.
References Cited (Backward Citations)
US2271234A
Cited
US3677790A
Cited
US3790653A
Cited
US3993486A
Cited
US3900323A
Cited
US4254208A
Cited
US4211837A
Cited
US4088487A
Cited
US4233392A
Cited
US4272594A
Cited
US4357416A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |