Arc and track resistant articles utilizing photosensitive sag resistant cycloaliphatic epoxy resin coating compositions
Assignee: Westinghouse Electric Corp
•
Filing: 1982-07-30
•
Granted: 1984-10-30
•
Expires: 2002-07-30
Abstract
Abstract A photosensitive sag resistant composition is made containing cycloaliphatic epoxy resin, a flexibilizing agent, arc and track resistant filler, thixotroping agent, and an amount of a photosensitive compound effective to initiate gelation with ultraviolet light exposure, where the composition is resistant to sag upon application to a surface, and has chemical and physical resistance to arced SF6 upon cure.
Inventors
- 👤 George D. Dixon
- 👤 Howard E. Saunders
- 👤 Smith A. Gause
- 👤 Newton N. Goldberg
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 12:09
CPC Classifications
H; H01; H01B; H01B3/00; H01B3/18; H01B3/30; H01B3/40; C; C08; C08G; C08G59/00; C08G59/02; C08G59/12; C08G59/18; C08G59/40; C08G59/42; C08G59/4207; C08G59/68; C08L; C08L63/00; G; G03; G03F; G03F7/00; G03F7/004; G03F7/038; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/139; Y10T428/1393; Y10T428/31504; Y10T428/31511
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
288 words
A photosensitive, sag resistant, arc and track resistant composition consisting essentially of the admixture of: (1) 100 parts by weight of a coating composition consisting essentially of: (A) 100 parts by weight of a cycloaliphatic epoxy resin, (B) about 30 to about 150 parts by weight of a flexibilizing agent for the epoxy resin, selected from the group consisting of polyazelaic polyanhydride, hexahydrophthalic anhydride and mixtures thereof, (C) about 150 to about 290 parts by weight of a filler promoting arc and track resistance, and (D) about 10 parts to about 75 parts by weight of Al 2 O 3 as sole thixotroping agent, to which is added, (2) an amount of a photosensitive compound effective to initiate gelation within the admixture with ultraviolet light exposure where the photosensitive compound is selected from the group consisting of: (a) from about 1.0 part to about 4.0 parts by weight of acrylic resin, containing an effective amount of free radical photoinitiator, (b) from 1.0 part to 3.0 parts by weight of polyester resin, containing an effective amount of free radical photoinitiator, (c) from 1.0 part to 5.0 parts by weight of acrylourethane resin, containing an effective amount of free radical photoinitiator, (d) from 0.05 part to 8.0 parts by weight of polythiolene resin, containing an effective amount of free radical photoinitiator, (e) from about 1.0 part to about 15.0 parts by weight of a non-reactive plasticizer, containing an effective amount of cationic photoinitiator, and (f) from about 0.05 part to about 3.0 parts by weight of cationic photoinitiator; said photosensitive, sag resistant composition being characterized as resistant to sag upon application to a surface, and as having crack resistance and chemical and physical resistance to arced SF 6 upon cure.
Claim 2
Dependent Claim
288 words
A photosensitive, sag resistant, arc and track resistant composition consisting essentially of the admixture of: (1) 100 parts by weight of a coating composition consisting essentially of: (A) 100 parts by weight of a cycloaliphatic epoxy resin, (B) about 30 to about 150 parts by weight of a flexibilizing agent for the epoxy resin, selected from the group consisting of polyazelaic polyanhydride, hexahydrophthalic anhydride and mixtures thereof, (C) about 150 to about 290 parts by weight of a filler promoting arc and track resistance, and (D) about 10 parts to about 75 parts by weight of Al 2 O 3 as sole thixotroping agent, to which is added, (2) an amount of a photosensitive compound effective to initiate gelation within the admixture with ultraviolet light exposure where the photosensitive compound is selected from the group consisting of: (a) from about 1.0 part to about 4.0 parts by weight of acrylic resin, containing an effective amount of free radical photoinitiator, (b) from 1.0 part to 3.0 parts by weight of polyester resin, containing an effective amount of free radical photoinitiator, (c) from 1.0 part to 5.0 parts by weight of acrylourethane resin, containing an effective amount of free radical photoinitiator, (d) from 0.05 part to 8.0 parts by weight of polythiolene resin, containing an effective amount of free radical photoinitiator, (e) from about 1.0 part to about 15.0 parts by weight of a non-reactive plasticizer, containing an effective amount of cationic photoinitiator, and (f) from about 0.05 part to about 3.0 parts by weight of cationic photoinitiator; said photosensitive, sag resistant composition being characterized as resistant to sag upon application to a surface, and as having crack resistance and chemical and physical resistance to arced SF 6 upon cure.
Claim 3
Dependent Claim
110 words
The sag resistant composition of claim 1, where the photosensitive compound is selected from the group consisting of non-reactive plasticizer containing an effective amount of a cationic photoinitiator, polyester resin containing an effective amount of a free radical photoinitiator, acrylourethane resin containing an effective amount of a free radical photoinitiator and polythiolene resin containing an effective amount of a free radical photoinitiator, the gelation is essentially instantaneous, to provide a chain matrix shell on the outside surface of the sag resistant composition to contain the rest of the resin, and the filler promoting arc and track resistance is selected from the group consisting of aluminum trihydrate, magnesite and mixtures thereof.
Claim 4
Dependent Claim
15 words
The sag resistant composition of claim 1, where the photosensitive compound is a cationic photoinitiator.
Claim 5
Dependent Claim
41 words
The sag resistant composition of claim 1, where the photosensitive compound is a non-reactive plasticizer selected from the group consisting of aromatic esters and aromatic phosphates containing from about 20 wt. % to about 70 wt. % of a cationic photoinitiator.
Claim 6
Dependent Claim
31 words
The sag resistant composition of claim 1, where the photosensitive compound is an acrylic resin containing from about 0.05 wt. % to about 15 wt. % of a free radical photoinitiator.
Claim 7
Dependent Claim
31 words
The sag resistant composition of claim 1, where the photosensitive compound is a polyester resin containing from about 0.05 wt. % to about 15 wt. % of a free radical photoinitiator.
Claim 8
Dependent Claim
31 words
The sag resistant composition of claim 1, where the photosensitive compound is an acrylourethane resin containing from about 0.05 wt. % to about 15 wt. % of a free radical photoinitiator.
Claim 9
Dependent Claim
31 words
The sag resistant composition of claim 1, where the photosensitive compound is a polythiolene resin containing from about 0.05 wt. % to about 15 wt. % of a free radical photoinitiator.
Claim 10
Dependent Claim
21 words
The sag resistant composition of claim 1, wherein the flexibilizing agent is a mixture of the polyazelaic polyanhydride and hexahydrophthalic anhydride.
Claim 11
Dependent Claim
26 words
The sag resistant composition of claim 1, characterized in that said cycloaliphatic epoxy resin is one having a backbone structure containing a pair of cycloaliphatic rings.
Claim 12
Dependent Claim
37 words
The sag resistant composition of claim 1, characterized in that said filler material is aluminum trihydrate and said Al 2 O 3 thixotroping agent has a surface area of from about 40 sq.m/g to about 300 sq.m/g.
Claim 13
Dependent Claim
62 words
The sag resistant composition of claim 10, characterized in that said epoxy has a backbone structure that contains a bridge containing not more than about 5 atoms in the direct chain between said rings and the filler which promotes arc and track resistance in moist SF 6 gas has an average particle size of between about 0.5 micron and about 450 microns.
Claim 14
Dependent Claim
41 words
The sag resistant composition of claim 12, characterized in that said filler material is aluminum trihydrate and the sole thixotroping agent is Al 2 O 3 having an average particle size of between about 0.0005 micron to about 0.10 micron diameter.
Claim 15
Dependent Claim
11 words
A feed tube made from the cured composition of claim 1.
Claim 16
Dependent Claim
43 words
An insulated article in an environment of SF 6 gas subject to arcing, said article having a flexible insulating surface adapted to be exposed to said gas, said insulating surface consisting essentially of the cured reaction product of the admixture of claim 1.
Claim 17
Dependent Claim
119 words
The insulated article of claim 15 where the photosensitive compound is selected from the group consisting of cationic photoinitiator, non-reactive plasticizer containing an effective amount of a cationic photoinitiator, acrylic resin containing an effective amount of a free radical phototinitiator, polyester resin containing an effective amount of a free radical photoinitiator, acrylourethane resin containing an effective amount of free radical photoinitiator and polythiolene resin containing an effective amount of free radical photoinitiator, the flexibilizing agent is selected from the group consisting of polyazelaic polyanhydride, hexahydrophthalic anhydride and mixtures thereof, the filler promoting arc and track resistance is selected from the group consisting of aluminum trihydrate magnesite and mixtures thereof, and the thixotroping agent is Al 2 O 3 .
Claim 18
Dependent Claim
25 words
The article of claim 15, wherein the flexibilizing agent is a mixture of the polyazelaic polyanhydride and hexahydrophthalic anhydride, and the filler is aluminum trihydrate.
Claim 19
Dependent Claim
22 words
The article of claim 15, wherein said cycloaliphatic epoxy resin is one having a backbone structure containing a pair of cycloaliphatic rings.
Claim 20
Dependent Claim
20 words
An article as defined in claim 15, characterized in that said article comprises a part of an extra-high-voltage circuit breaker.
Claim 21
Dependent Claim
16 words
An article as defined in claim 18, characterized in that said article is a feed tube.
References Cited (Backward Citations)
US3449274A
Cited
US3505426A
Cited
US3828000A
Cited
US3817906A
Cited
US4020306A
Cited
US3937855A
Cited
US4104238A
Cited
US4102851A
Cited
US4206066A
Cited
US4404355A
Cited
US4412048A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |