Catalytic process for the production of sulphur from a gas containing H.sub. S
Assignee: Societe Nationale Elf Aquitaine Production SA
•
Filing: 1982-08-19
•
Granted: 1984-10-30
•
Expires: 2002-08-19
Abstract
Abstract Catalytic process for the production of sulphur from an acid gas containing H 2 S, in which a part of H 2 S is catalytically oxidized in order to form an effluent containing H 2 S and SO 2 in a molar ratio of 2:1 and a given quantity of sulphur. The effluent is then contacted with a CLAUS catalyst to form a further quantity of sulphur. Said process involves: an oxidation reactor with a fixed bed an indirect gas/gas heat exchanger deoxygenation reactor having a fixed bed a catalyst conversion battery a thermal incinerator.
Inventors
- 👤 Robert Voirin
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 15:14
CPC Classifications
C; C01; C01B; C01B17/00; C01B17/02; C01B17/04; C01B17/0404; C01B17/046; C01B17/0465; C01B17/0456
Claims Analysis
Total Claims: 29
Claim 1
Independent Claim
203 words
A catalytic process for the production of sulphur from an acid gas containing H 2 S, which comprises: contacting said acid gas at a temperature from about 200° to 900° C. in the presence of an oxidation catalyst, with a controlled quantity of a gas containing free oxygen to form a gaseous effluent containing H 2 S and SO 2 in a H 2 S/SO 2 molar ratio substantially equal to 2/1 and a proportion of sulphur; and cooling and contacting said effluent with a CLAUS catalyst to form a further quantity of sulphur, wherein the H 2 S oxidation catalyst consists essentially of a refractory porous matrix having a surface area of at least 5 m 2 /g comprising 50 to 100% by weight of at least one composition selected from the group consisting of silica, titanium oxide, expressed as TiO 2 , zirconium oxide, expressed as ZrO 2 and zeolites and 0 to 50% by weight of alumina and containing about 0.5 to 15% by weight of the calcined catalyst, expressed as percent by weight of of metal, of at least one metal compound selected from the group consisting of Fe, Cu, Zn, Cd, Cr, Mo, W, Co, Ni, and Bi.
Claim 2
Dependent Claim
203 words
A catalytic process for the production of sulphur from an acid gas containing H 2 S, which comprises: contacting said acid gas at a temperature from about 200° to 900° C. in the presence of an oxidation catalyst, with a controlled quantity of a gas containing free oxygen to form a gaseous effluent containing H 2 S and SO 2 in a H 2 S/SO 2 molar ratio substantially equal to 2/1 and a proportion of sulphur; and cooling and contacting said effluent with a CLAUS catalyst to form a further quantity of sulphur, wherein the H 2 S oxidation catalyst consists essentially of a refractory porous matrix having a surface area of at least 5 m 2 /g comprising 50 to 100% by weight of at least one composition selected from the group consisting of silica, titanium oxide, expressed as TiO 2 , zirconium oxide, expressed as ZrO 2 and zeolites and 0 to 50% by weight of alumina and containing about 0.5 to 15% by weight of the calcined catalyst, expressed as percent by weight of of metal, of at least one metal compound selected from the group consisting of Fe, Cu, Zn, Cd, Cr, Mo, W, Co, Ni, and Bi.
Claim 3
Dependent Claim
16 words
A process according to claim 1, wherein the catalysts contains at least one precious metal compound.
Claim 4
Dependent Claim
26 words
A process according to claim 1, wherein the porous matrix of the oxidation catalyst has a surface area ranging from 20 to 800 m 2 /g.
Claim 5
Dependent Claim
22 words
A process according to claim 3, wherein the oxidation catalyst has a surface area of from 50 to 600 m 2 /g.
Claim 6
Dependent Claim
79 words
A process according to claim 1 or 2, wherein the catalyst contains at least one metal compound selected from the group consisting of Fe, Cu, Zn, Cd, Cr, Mo, W, Co, Ni, and Bi and at least one precious metal compound selected from the group consisting of Pd, Pt, Ir and Rh, wherein the ratio of the total number of atoms of the at least one metal to the number of precious metal atoms being between 20 and 1000.
Claim 7
Dependent Claim
14 words
A process according to claim 5, wherein said ratio is between 50 and 400.
Claim 8
Dependent Claim
64 words
A process according to claim 1, wherein the oxidation catalyst comprises a porous matrix comprising at least one composition selected from the group consisting of silica, titanium oxide and zirconium oxide having a surface area of at least 5 m 2 /g, and a metal component selected from the group consisting of an iron compound, and an iron compound and a precious metal compound.
Claim 9
Dependent Claim
18 words
A process according to claim 7, wherein the surface area is between 20 and 800 m 2 /g.
Claim 10
Dependent Claim
18 words
A process according to claim 7, wherein the surface area is between 50 and 600 m 2 /g.
Claim 11
Dependent Claim
39 words
A process according to claim 1 or 2, wherein the overall quantity of the metal compound contained in the catalyst is between 4 and 12%, expressed as percent by weight of metal, of the weight of the calcined catalyst.
Claim 12
Dependent Claim
32 words
A process according to claim 7, wherein the quantity of iron or iron and precious metal contained in the oxidation catalyst is 0.5 to 12% by weight of the said calcined catalyst.
Claim 13
Dependent Claim
31 words
A process according to claim 11, wherein the quantity of iron or iron and precious metal contained in the oxidation catalyst is 4 to 12% by weight of the calcined catalyst.
Claim 14
Dependent Claim
91 words
A process according to claim 1, wherein the oxidation catalyst comprises silica having a specific surface area in the range of from 50 to 6000 M 2 /g said catalyst containing an iron compound, or an iron compound and a palladium compound, the quantity of iron or iron and palladium, expressed as percent by weight of metal, being 4 to 12% by weight of the calcined catalyst and, when palladium is present, the ratio of the number of iron atoms to the number of palladium atoms is between 20 and 1000.
Claim 15
Dependent Claim
13 words
A process according to claim 13, wherein the iron compound is iron sulfate.
Claim 16
Dependent Claim
28 words
A process according to claim 13 or 14, wherein the ratio of the number of iron atoms to the number of palladium atoms is between 50 and 400.
Claim 17
Dependent Claim
19 words
A process according to claim 1, wherein the acid gas contains 0.5 to 20% H 2 S by volume.
Claim 18
Dependent Claim
26 words
A process according to claim 16, wherein the acid gas contains up to 1% H 2 S by volume of at least one organic sulphur compound.
Claim 19
Dependent Claim
16 words
A process according to claim 16 or 17, wherein the organic sulphur compound is a mercaptan.
Claim 20
Dependent Claim
28 words
A process according to claim 1, wherein the oxidation of H 2 S in the acid gas is achieved at a temperature between 300° C. and 700° C.
Claim 21
Dependent Claim
96 words
A process according to claim 1 wherein the gaseous effluent has a H 2 S content below 2% by volume, and the contacting of the said effluent with the CLAUS catalyst is achieved at a temperature lower than the dew point of sulphur contained in the said effluent, the temperature being between 80° and 160° C. wherein the sulfur condenses and loads the CLAUS catalyst, and the CLAUS catalyst that is loaded with the sulphur is periodically regenerated by sweeping with a gas devoid of free oxygen at a temperature between 200° C. and 400° C.
Claim 22
Dependent Claim
89 words
A process according to claim 20, wherein the contacting with the CLAUS catalyst is achieved in a series of catalytic converters operating in such a way that at least one of the converters is in the regeneration phase when the others are in the CLAUS reaction phase, and the effluent from the oxidation zone passes, first, into the converter (s) in the regeneration phase, to remove the sulfur from the sulphur loaded catalyst contained therein, then, after separation of the sulphur, into the converters in the CLAUS reaction phase.
Claim 23
Dependent Claim
49 words
A process according to claim 1, wherein the oxidation effluent has an H 2 S content at least equal to 2% by volume and the contacting of said effluent with the CLAUS catalyst is carried out at temperatures higher than the dew point of sulphur contained in the effluent.
Claim 24
Dependent Claim
16 words
A process according to claim 22, wherein the temperature is between 200° C. and 450° C.
Claim 25
Dependent Claim
55 words
A process according to claim 22, wherein the contacting of the oxidation effluent with the CLAUS catalyst at temperatures higher than the dew-point of sulphur contained in the oxidation effluent forms a gas stream which is then contacted with a CLAUS catalyst at temperatures below the dew point of the sulphur in the gas stream.
Claim 26
Dependent Claim
21 words
A process according to claim 20, wherein the oxidation effluent is contacted with a deoxygenation catalyst before contacting the CLAUS catalyst.
Claim 27
Dependent Claim
37 words
A process according to claim 21 or 25, wherein the deoxygenation catalyst is contained in a reactor placed upstream from a series of catalytic converters, some of which operate as regenerators and the others as CLAUS reactors.
Claim 28
Dependent Claim
41 words
A process according to claim 23, 24 or 25, wherein the deoxygenation catalyst is a layer or the totality of a single catalytic converter operating above the dew-point of sulphur or of the first converters of several catalytic converters in series.
Claim 29
Dependent Claim
29 words
A process according to claim 1, wherein the gases issuing from the contacting of the oxidation effluent with the CLAUS catalyst are subjected to a thermal or catalytic incineration.
References Cited (Backward Citations)
US2697064A
Cited
US3939250A
Cited
US4141962A
Cited
US4192857A
Cited
US4399112A
Cited
GB2087373A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |