Fiber board composition
Assignee: MOGUL TRUST A MO BUSINESS TRUST
•
Filing: 1982-09-22
•
Granted: 1984-10-30
•
Expires: 2002-09-22
Abstract
Abstract A fiber board composition and a fiber board composite formed therefrom is capable of consolidation into a variety of structural building products ranging from flat sheets and panels which may interlock for modular housing to 2×4's through 2×12's, etc. Fiber boards comprised of the fiber board composition of the present invention are characterized by high strength, fire resistance, water resistance and insect and rot resistance. The fiber board composition comprises lignocellulosic particles, such as softwood or hardwood waste particles, which have been pressure treated to resist insects and rot with a chemical compound, such as chromated copper arsenate, before board consolidation; a vegetable matter derivative for increased strength, such as hominy feed; a fire retardant chemical, such as alumina tri-hydrate; and a water retardant chemical, such as casco wax, which are then consolidated into the formed fiber board structure by means of about 4 to about 10% by weight of a phenolic-type resin, pressures of about 400 to about 600 psi, heat of about 320° to about 360° F. and ultrasonic sound with a frequency of about 3.6 to 3.7 mega hertz (million cycles per second). The amount of chemicals and/or other components to be added to the composite mixture will vary according to the desired result in each of the specified categories characterized by strength, fire resistance, water resistance and insect and rot resistance.
Inventors
- 👤 Ralph Bullock
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-25 03:28
CPC Classifications
C; C08; C08L; C08L97/00; C08L97/02; C08L2201/00; C08L2201/02; C08L61/00; C08L61/04; C08L61/06; Y; Y10; Y10S; Y10S428/00; Y10S428/92; Y10T; Y10T428/00; Y10T428/25; Y10T428/253
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
122 words
A process for making an improved fiber board product consisting of pressure impregnation of lignocellulosic woody particles with chromated copper arsenate to resist insects and rot; mixing a special vegetable matter derivative, hominey feed, in combination with phenol formaldehyde resin with the lignocellulosic woody particles to increase strength and adhesion; mixing a low viscosity form of alumina tri-hydrate to the mixture as a fire retardant; mixing casco wax and a penetrating type of petroleum distillate to the mixture as water retardants; forming a mat from the mixture; pressing the mat into a fiber board product under heat and pressure while subjecting the mat to ultrasonic sound to speed curing time and create a more uniform structural density in the fiber board product.
Claim 2
Dependent Claim
122 words
A process for making an improved fiber board product consisting of pressure impregnation of lignocellulosic woody particles with chromated copper arsenate to resist insects and rot; mixing a special vegetable matter derivative, hominey feed, in combination with phenol formaldehyde resin with the lignocellulosic woody particles to increase strength and adhesion; mixing a low viscosity form of alumina tri-hydrate to the mixture as a fire retardant; mixing casco wax and a penetrating type of petroleum distillate to the mixture as water retardants; forming a mat from the mixture; pressing the mat into a fiber board product under heat and pressure while subjecting the mat to ultrasonic sound to speed curing time and create a more uniform structural density in the fiber board product.
Claim 3
Dependent Claim
87 words
The process of claim 1, in which individual lignocellulosic woody particles are pressure impregnated with chromated copper arsenate prior to board fabrication by pressures of from 120-125 psi, for about 10 minutes, and kiln drying the mixture for 48 hours or less at a maximum drying temperature of about 180° F., with the small size particles enabling elimination of concern over warping and twisting of such small size particles, which allows a maximum drying temperature of 180° F. to be reached in a shorter period of time.
Claim 4
Dependent Claim
57 words
The process of claim 1, in which the vegetable matter derivative, hominy feed, and the phenol formaldehyde resin are combined in the presence of temperatures in excess of 300° F. which forms a very high viscosity liquid which forms a secondary adhesive binder, thereby creating an increased adhesion effect which increases the strength of the final product.
Claim 5
Dependent Claim
50 words
The process of claim 1, wherein the alumina tri-hydrate possesses a relatively low temperature release point of about 400° F. and mixes thoroughly and evenly with the other components of the composite mix, thereby creating a higher level of fire retardance than can be found in conventional fiber board products.
Claim 6
Dependent Claim
44 words
The process of claim 1 wherein the water retardants are applied externally after pressing is completed; the phenol formaldehyde resin working in combination with the water retardants to produce a higher level of water retardance than can be found in conventional fiber board products.
Claim 7
Dependent Claim
60 words
The process of claim 1 wherein the ultrasonic sound has extremely high frequencies, in the 3.6 to 3.7 mega hertz range, which allows the use of reduced pressing temperatures and press duration time savings of from 300 to 500%, which allows the resin to cure more evenly and quickly, thereby creating a more uniform structural density and increased product strength.
Claim 8
Independent Claim
86 words
The method of making a fiber board comprising the steps of: (a) pressure impregnating lignocellulosic woody particles with chromated copper arsenate; (b) kiln drying the impregnated lignocellulosic woody particles; (c) mixing of vegetable matter; alumina tri-hydrate and wax with the dried impregnated lignocellulosic woody particles; (d) adding phenol formaldehyde resin to the mixture; (e) forming a mat from the mixture; and (f) pressing the mat under heat and pressure while subjecting the mat to high frequency ultrasonic sound to cure the mat into a fiber board.
Claim 9
Independent Claim
86 words
The method of making a fiber board comprising the steps of: (a) pressure impregnating lignocellulosic woody particles with chromated copper arsenate; (b) kiln drying the impregnated lignocellulosic woody particles; (c) mixing of vegetable matter; alumina tri-hydrate and wax with the dried impregnated lignocellulosic woody particles; (d) adding phenol formaldehyde resin to the mixture; (e) forming a mat from the mixture; and (f) pressing the mat under heat and pressure while subjecting the mat to high frequency ultrasonic sound to cure the mat into a fiber board.
Claim 10
Dependent Claim
61 words
The method of claim 7 wherein the woody particles have a maximum outside dimension not in excess of approximate 1/16 inch, said pressure impregnating step being under a pressure of approximately 120 to 125 psi for about 10 minutes, said kiln drying step reducing the moisture of the mixture to about 5 to 12% under a temperature of about 180° F.
Claim 11
Dependent Claim
92 words
The method of claim 8 wherein the vegetable matter is a derivative in the form of hominy feed and the mixing step includes tumbling the materials to form a uniform mixture, said addition of resin includes spraying of resin onto the mixture while tumbling slowly until saturated, said pressing step being conducted at a temperature of about 320° to 360° F. with pressure of about 400 to 600 psi, said high frequency sound being in the 3.6 to 3.7 mega hertz range with the press time being about 3 to 5 minutes.
Claim 12
Dependent Claim
39 words
The method of claim 9 wherein the cured fiber board is allowed to cool to a temperature below 100° F. and spraying a penetrating type petroleum distillate onto at least one surface of the fiber board for exterior use.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |