Thick film resistor inks
Assignee: RCA Corp
•
Filing: 1982-10-05
•
Granted: 1984-10-30
•
Expires: 2002-10-05
Abstract
Abstract An improved ink composition suitable for the formation of thick film resistor inks which can be terminated directly to copper foil conductors. The subject compositions comprise an epoxy resin, conductive carbon particles, a suitable solvent and particulate alumina, wherein the alumina is present in an amount at least equal to the resin content on a weight basis.
Inventors
- 👤 Ashok N. Prabhu
- 👤 Simon M. Boardman
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 01:17
CPC Classifications
H; H01; H01C; H01C17/00; H01C17/06; H01C17/065; H01C17/06506; H01C17/06513; H01C17/0652; H01C7/00; H01C7/003; H01C7/005
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
119 words
In a process of terminating a thick film resistor to a copper foil conductor on a circuit board comprising: (a) applying directly to selected sites on the copper conductor a thick film resistor ink composition comprising an epoxy resin, alumina conductive carbon particles and a suitable solvent; and (b) curing the ink composition by heating to a temperature between about 100° and 250° for from 15 to 120 minutes thereby forming a thick film resistor, the improvement wherein said ink composition contains particulate alumina having an average particle size of from above about 0.5 micrometer to about 5.0 micrometers, and the weight percent ratio of the particulate alumina to the epoxy resin is between about 1:1 and about 2:1.
Claim 2
Dependent Claim
119 words
In a process of terminating a thick film resistor to a copper foil conductor on a circuit board comprising: (a) applying directly to selected sites on the copper conductor a thick film resistor ink composition comprising an epoxy resin, alumina conductive carbon particles and a suitable solvent; and (b) curing the ink composition by heating to a temperature between about 100° and 250° for from 15 to 120 minutes thereby forming a thick film resistor, the improvement wherein said ink composition contains particulate alumina having an average particle size of from above about 0.5 micrometer to about 5.0 micrometers, and the weight percent ratio of the particulate alumina to the epoxy resin is between about 1:1 and about 2:1.
Claim 3
Dependent Claim
64 words
A process in accordance with claim 1, wherein said ink comprises from about 20 to about 30 percent by weight of the epoxy resin; from about 30 to about 40 percent by weight of particulate alumina; from about 1 to about 7 percent by weight of particulate conductive carbon black; and from about 25 to about 50 percent by weight of a suitable solvent.
Claim 4
Dependent Claim
57 words
A process in accordance with claim 2, wherein said ink composition comprises: from about 23 to about 25 percent by weight of the epoxy resin; about 35 percent by weight of alumina; from about 1 to about 3 percent by weight of carbon black and from about 35 to about 40 percent by weight of the solvent.
Claim 5
Dependent Claim
20 words
A process in accordance with claim 1, wherein the particulate alumina has an average particle size of about one micrometer.
Claim 6
Dependent Claim
21 words
A process in accordance with claim 1, wherein the ratio in weight percent of alumina to the resin is about 1.4:1.
Claim 7
Dependent Claim
17 words
A process in accordance with claim 1, wherein the epoxy resin is a modified bisphenol A resin.
Claim 8
Dependent Claim
19 words
A process in accordance with claim 6, wherein said resin is an epichlorohydrin-bisphenol A resin containing an urea-formaldehyde resin.
Claim 9
Dependent Claim
138 words
In an ink composition suitable for forming a thick film resistor on a circuit board comprising an epoxy resin, conductive particles and a suitable solvent, the improvement wherein said ink contains a sufficient amount of particulate alumina having an average particle size of from above about 0.5 micrometer to about 5.0 micrometers so that the ink can be applied directly to a copper foil conductor on the board, the weight ratio of the alumina to the epoxy resin being between about 1:1 and 1:2, said ink comprising: from about 20 to about 30 percent by weight of said resin; from about 30 to about 40 percent by weight of the alumina, from about 1 to about 7 percent by weight of conductive carbon particle and from about 25 to about 50 percent by weight of a suitable solvent.
Claim 10
Dependent Claim
138 words
In an ink composition suitable for forming a thick film resistor on a circuit board comprising an epoxy resin, conductive particles and a suitable solvent, the improvement wherein said ink contains a sufficient amount of particulate alumina having an average particle size of from above about 0.5 micrometer to about 5.0 micrometers so that the ink can be applied directly to a copper foil conductor on the board, the weight ratio of the alumina to the epoxy resin being between about 1:1 and 1:2, said ink comprising: from about 20 to about 30 percent by weight of said resin; from about 30 to about 40 percent by weight of the alumina, from about 1 to about 7 percent by weight of conductive carbon particle and from about 25 to about 50 percent by weight of a suitable solvent.
Claim 11
Dependent Claim
57 words
An ink composition in accordance with claim 8, wherein said composition comprises from about 23 to about 25 percent by weight of the epoxy resin; about 35 percent by weight of alumina; from about 1 to about 3 percent by weight of carbon black and from about 35 to about 40 percent by weight of the solvent.
Claim 12
Dependent Claim
21 words
An ink composition in accordance with claim 8, wherein the particulate alumina has an average particle size of about one micrometer.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |