US4479293A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for fabricating integrally bladed bimetallic rotors
Assignee: RTX Corp
•
Filing: 1981-11-27
•
Granted: 1984-10-30
•
Expires: 2001-11-27
Abstract
Abstract An integrally bladed bimetallic rotor for high temperature operation having airfoils with good stress rupture and creep strength and a hub with high tensile strength and good low cycle fatigue resistance is made from a preform of two concentric cylinders of different superalloy metals metallurgically bonded to each other at their interface, both materials being in such a condition that they exhibit superplastic behavior at a certain, controlled strain rate and temperature without incurring substantial grain growth. The metal of the outer cylinder is selected such that it has a lower gamma prime solvus temperature than the metal of the inner cylinder. The preform is isothermally forged at the controlled strain rate and temperature to form the airfoils from the alloy of the outer cylinder and to form the hub from the alloy of the inner cylinder. A sharp, reproducible interface is created between the two alloys. After forging, the rotor is heated to a temperature between the gamma prime solvus temperatures of the alloys and under conditions which cause full gamma prime solutioning of the airfoils up to the interface but only partial gamma prime solutioning of the rotor hub. The resulting airfoils have coarse grains and the hub has fine equiaxed grains.
Inventors
- 👤 John A. Miller
- 👤 Ralph E. Anderson
- 👤 Marvin M. Allen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 14:19
CPC Classifications
B; B21; B21K; B21K1/00; B21K1/28; B21K1/36; B21J; B21J5/00; B23; B23P; B23P15/00; B23P15/006; Y; Y10; Y10T; Y10T29/00; Y10T29/49; Y10T29/49316; Y10T29/4932; Y10T29/49325
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
211 words
A process for fabricating an integrally bladed bimetallic rotor having coarse grained airfoils and an equiaxed fine grained hub portion, comprising the steps of: (1) forming a bimetallic preform having an axis and comprising a first cylinder of a first superalloy metal surrounded by a second cylinder of a second superalloy metal, said second superalloy metal being selected to have a gamma prime solvus temperature at least 25° F. lower than the gamma prime solvus temperature of said first superalloy metal, said step of forming a bimetallic preform including the step of metallurgically bonding said second cylinder along its entire inner surface to said first cylinder, and including imparting to said first and second superalloys the property of exhibiting superplastic behavior at a first strain rate and first forging temperature without incurring substantial grain growth; (2) isothermally forging, at said first temperature and first strain rate, said bimetallic preform, said step of forging comprising forging said first cylinder into the shape of said hub portion and said second cylinder into the shape of said airfoils; and (3) heat treating the forged article to effect full gamma prime solutioning in the airfoils and partial gamma prime solutioning in the tub portion and to restore essentially normal strength and hardness to both superalloys.
Claim 2
Dependent Claim
211 words
A process for fabricating an integrally bladed bimetallic rotor having coarse grained airfoils and an equiaxed fine grained hub portion, comprising the steps of: (1) forming a bimetallic preform having an axis and comprising a first cylinder of a first superalloy metal surrounded by a second cylinder of a second superalloy metal, said second superalloy metal being selected to have a gamma prime solvus temperature at least 25° F. lower than the gamma prime solvus temperature of said first superalloy metal, said step of forming a bimetallic preform including the step of metallurgically bonding said second cylinder along its entire inner surface to said first cylinder, and including imparting to said first and second superalloys the property of exhibiting superplastic behavior at a first strain rate and first forging temperature without incurring substantial grain growth; (2) isothermally forging, at said first temperature and first strain rate, said bimetallic preform, said step of forging comprising forging said first cylinder into the shape of said hub portion and said second cylinder into the shape of said airfoils; and (3) heat treating the forged article to effect full gamma prime solutioning in the airfoils and partial gamma prime solutioning in the tub portion and to restore essentially normal strength and hardness to both superalloys.
Claim 3
Dependent Claim
64 words
The process according to claim 1 wherein during said step of isothermal forging but prior to forging said second cylinder into said airfoils, said isothermal forging includes upsetting said preform along the axis of the cylinders to effect a reduction in the thickness of the preform of at least 50% and to increase the area of contact between the first and second superalloy metals.
Claim 4
Dependent Claim
45 words
The process according to claim 2 wherein the initial area of the interface between the first and second superalloy metals in the cylindrical bimetallic preform from which the rotor is forged is increased by at least a factor of two during fabrication of the rotor.
Claim 5
Dependent Claim
57 words
The process according to claim 3 wherein in said step of heat treating, the airfoils and hub portion are heat treated simultaneously under the same conditions, including heating the entire rotor to a temperature above the gamma prime solvus temperature of said second superalloy metal but below the gamma prime solvus temperature of said first superalloy metal.
Claim 6
Dependent Claim
77 words
The process according to claims 2 or 4 wherein in the step of heat treating, the second superalloy metal is heated to a temperature above its gamma prime solvus temperature but less than gamma prime solvus temperature of said first superalloy metal, and said first superalloy metal is heated to a temperature less than its gamma prime solvus temperature, but within 150° F. thereof to effect a partial gamma prime solution heat treatment of said first metal.
Claim 7
Dependent Claim
36 words
The process according to claim 5 wherein the step of effecting grain growth in the airfoils includes directionally recrystallizing the airfoils to form columnar grains from the airfoil tips to the interface between the two superalloys.
Claim 8
Dependent Claim
39 words
The process according to claim 3 wherein said step of isothermally forging includes forming an interlocking configuration at the bond interface between the superalloys such that the hub material mechanically restrains the surrounding airfoil material from moving radially outwardly.
Claim 9
Dependent Claim
106 words
The process according to claim 3 wherein the step of upsetting includes forming a substantially U-shaped interface between the two alloys in cross-section taken along a plane containing the axis of the cylinders, said step of upsetting further including the step of necking down the preform between the radially outermost and radially innermost location of the said U-shaped interface and increasing the thickness of the preform at its periphery to create an interface between the two superalloys which has the appearance of a dovetail-like attachment between the first and second superalloys when viewed in cross section taken in any plane containing the axis of the cylinders.
Claim 10
Dependent Claim
61 words
The process according to claim 5 wherein the grain size throughout the rotor after the step of isothermally forging and before the step of heat treating is no greater than ASTM 12, and, after heat treating, the grain size throughout the airfoils is no less than ASTM 1 and the grain size throughout the hub is no greater than ASTM 10.
References Cited (Backward Citations)
US3122823A
Cited
US3519503A
Cited
US3574004A
Cited
US3795970A
Cited
US4063939A
Cited
US3975219A
Cited
US4074559A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-30 | 1988-04-30 | 1988-10-30 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-30 | 1992-04-30 | 1992-10-30 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-30 | 1996-04-30 | 1996-10-30 | $7700.00 | Window Closed / Lapsed |