Blended pressure-sensitive asphaltic based adhesives
Assignee: Owens Corning Fiberglas Technology Inc
•
Filing: 1982-08-12
•
Granted: 1984-10-23
•
Expires: 2002-08-12
Abstract
Abstract A pressure-sensitive adhesive is disclosed which is prepared by hot melt blending paving grade asphalt, a depolymerized virgin rubber, a terpene resin, and a vulcanizable, non-depolymerized styrene-butadiene copolymer. These adhesives are especially useful in forming membranes by coating one side of an asphaltic based coated reinforcement with these adhesives. They are useful for highway repair and maintenance purposes and for waterproofing and show good adhesion to cementitious, for example asphaltic concrete or Portland cement concrete, substrates.
Inventors
- 👤 William E. Uffner
- 👤 Robert N. White
- 👤 Edward R. Harrington
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 19:18
CPC Classifications
E; E01; E01C; E01C11/00; E01C11/005; C; C09; C09J; C09J195/00; C08; C08L; C08L2666/00; C08L2666/02; C08L2666/04; Y; Y10; Y10T; Y10T428/00; Y10T428/14; Y10T428/141; Y10T428/28; Y10T428/2813; Y10T428/2817; Y10T428/2826; Y10T428/31504; Y10T428/31815; Y10T428/31826
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
84 words
In an article comprising a laminate of an asphaltic based composition coated on a reinforcement and including a pressure sensitive asphaltic based adhesive coated on one side of said laminate, the improvement wherein said adhesive is a hot melt blended composition consisting essentially of paving grade asphalt, effective tacky amounts of a depolymerized virgin rubber having a molecular weight of about 10,000 to about 110,000, effective viscosity depressing amounts of a terpene resin and effective cold flow resisting amounts of a non-depolymerized styrene-butadiene copolymer.
Claim 2
Dependent Claim
84 words
In an article comprising a laminate of an asphaltic based composition coated on a reinforcement and including a pressure sensitive asphaltic based adhesive coated on one side of said laminate, the improvement wherein said adhesive is a hot melt blended composition consisting essentially of paving grade asphalt, effective tacky amounts of a depolymerized virgin rubber having a molecular weight of about 10,000 to about 110,000, effective viscosity depressing amounts of a terpene resin and effective cold flow resisting amounts of a non-depolymerized styrene-butadiene copolymer.
Claim 3
Dependent Claim
46 words
The improvement of claim 1 wherein said asphalt has a penetration of about 40 to about 65 and a viscosity of about 160,000 to about 240,000 cps at 140° F., said adhesive having a viscosity of about 7800 cps to about 9200 cps at 250° F.
Claim 4
Dependent Claim
64 words
The improvement of claim 2 wherein said depolymerized rubber is present in an amount of about 8% to about 12% by weight, said terpene in an amount of about 18% to about 24%, said copolymer in an amount of about 6% to about 8% and said asphalt in an amount of about 56% to about 68%, said adhesive substantially instantaneously sticking to cementitious substrates.
References Cited (Backward Citations)
US2610162A
Cited
US2578001A
Cited
US2884400A
Cited
US3338849A
Cited
US3741856A
Cited
US4008095A
Cited
US3900102A
Cited
US4169822A
Cited
US3932341A
Cited
US3919148A
Cited
US4174992A
Cited
US4113799A
Cited
US4021393A
Cited
US4064082A
Cited
US4074948A
Cited
US4175978A
Cited
US4105612A
Cited
US4217259A
Cited
US4273685A
Cited
US4440816A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |