US4478610A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of preparing flexible backing material for use in coated abrasives
Assignee: Saint Gobain Abrasives Inc
•
Filing: 1984-02-06
•
Granted: 1984-10-23
•
Expires: 2004-02-06
Abstract
Abstract A flexible sheet material particularly suitable as a backing for coated abrasive products and method of making same are described. The flexible sheet material is of that type employing a straight warp fabric. The yarns of the straight warp fabric are coated and at least partially impregnated with a flexible polymeric material, such as polyvinyl alcohol, having thereover an intermediate filling coat of a phenol formaldehyde resin/latex and an outer filling coat of phenol formaldehyde resin. Alternatively, the straight warp fabric includes a penetrating base coating of flexible polymeric material and thereover a backfilling including approximately equal parts by weight of calcium carbonate and magnesium carbonate dispersed in a flexible synthetic polymeric resin which backfilling fills the interstices and encapsulates the yarns of one of the yarn arrays that form the straight warp fabric. The straight warp fabric may include a non-woven web located between adjacent arrays of warp and weft yarns. The flexible sheet material described herein may be thereafter coated in conventional manner with abrasive grains to form a coated abrasive sheet material that is particularly suitable for use in the formation of endless abrasive belts.
Inventors
- 👤 Dhan N. Parekh
- 👤 Paul R. Schweyen
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 02:36
CPC Classifications
B; B24; B24D; B24D11/00; B24D11/02; B24D3/00; B24D3/001; B24D3/002; B24D3/02; B24D3/20; B24D3/28; B24D3/285; D; D06; D06N; D06N3/00; D06N3/0002; D06N3/0015; D06N3/0036; D06N3/0056; D06N3/0063; D06N2205/00; D06N2205/02; D06N2205/023; D06N2205/10; D06N2209/00; D06N2209/10; D06N2209/106; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24033; Y10T428/24058; Y10T428/24074; Y10T428/24091; Y10T428/24355; Y10T428/24372; Y10T428/25; Y10T442/00; Y10T442/20; Y10T442/2041; Y10T442/2098; Y10T442/2107; Y10T442/2115
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
80 words
A method of preparing flexible sheet material of the type including a straight warp fabric, including the steps of: (a) wetting all exposed surfaces of the fabric with an aqueous solution of polyvinyl alcohol; (b) drying the polyvinyl alcohol wetted fabric under tension to produce a polyvinyl alcohol dipsized fabric; (c) applying a filling of phenolic formaldehyde resin/latex mixture to the polyvinyl alcohol dipsized fabric; (d) applying an outer coating of phenol formaldehyde resin including an inorganic pigment dispersed therein.
Claim 2
Independent Claim
80 words
A method of preparing flexible sheet material of the type including a straight warp fabric, including the steps of: (a) wetting all exposed surfaces of the fabric with an aqueous solution of polyvinyl alcohol; (b) drying the polyvinyl alcohol wetted fabric under tension to produce a polyvinyl alcohol dipsized fabric; (c) applying a filling of phenolic formaldehyde resin/latex mixture to the polyvinyl alcohol dipsized fabric; (d) applying an outer coating of phenol formaldehyde resin including an inorganic pigment dispersed therein.
Claim 3
Dependent Claim
17 words
The method of claim 1 further including between steps (b) and (c) heat setting the dipsized fabric.
Claim 4
Dependent Claim
39 words
The method of claim 1 wherein a sufficient amount and distribution of polyvinyl alcohol exists to reduce the air permeability of the fabric from about 10 to about 40 percent when compared to the fabric in its greige state.
Claim 5
Dependent Claim
70 words
The method of claim 1 wherein the fabric is formed of polyester warp yarns further comprising stretching the dried fabric, maintaining lengthwise tension on the fabric while the fabric is exposed in an oven at about 445° F. (229.5° C.) for a period of about 2.2 minutes and thereafter quenching the heated fabric with forced ambient air while maintaining lengthwise tension on the fabric to prevent further lengthwise shrinkage thereof.
Claim 6
Dependent Claim
30 words
The process of claim 1 further comprising prior to step (d) reducing the width of the heat set fabric by removal of a predetermined amount from each longitudinally extending edge.
Claim 7
Dependent Claim
44 words
The process of claim 5 further comprising after heat setting and removal of a predetermined amount from each longitudinally extending edge of the fabric, dipping the fabric in a phenolic resin/latex mixture having a resin to latex dry weight basis ratio of about 1:1.
Claim 8
Dependent Claim
44 words
The process of claim 6 wherein the fabric is twice dipped in a phenolic resin/latex mixture to achieve a total dry weight basis add on of about 7.8 to 12.4 percent of phenolic resin/latex mixture by weight based on the heat treated fabric weight.
Claim 9
Independent Claim
158 words
A method of preparing a flexible sheet material of the type including a straight warp fabric having a planar array of warp yarns juxtaposed to a planar array of weft yarns, including the steps of: (a) wetting all exposed surfaces of the fabric with an aqueous solution of polyvinyl alcohol, (b) drying the polyvinyl alcohol wetted fabric under tension to produce a PVA dipsized fabric, (c) heat setting the dipsized fabric, (d) forming a backfilling including approximately equal parts of calcium carbonate, magnesium carbonate and poly vinyl alcohol dispersed in water (e) filling one of said arrays of yarns while leaving the other array unfilled with said backfilling material and setting the filling, (f) applying a backsize over that array of yarns of the fabric that has been filled, (g) filling the unbackfilled array of the fabric with a phenolic resin/calcium carbonate filler mixture having a resin to filler ratio of about 1.1:1 on a dry weight basis.
Claim 10
Independent Claim
158 words
A method of preparing a flexible sheet material of the type including a straight warp fabric having a planar array of warp yarns juxtaposed to a planar array of weft yarns, including the steps of: (a) wetting all exposed surfaces of the fabric with an aqueous solution of polyvinyl alcohol, (b) drying the polyvinyl alcohol wetted fabric under tension to produce a PVA dipsized fabric, (c) heat setting the dipsized fabric, (d) forming a backfilling including approximately equal parts of calcium carbonate, magnesium carbonate and poly vinyl alcohol dispersed in water (e) filling one of said arrays of yarns while leaving the other array unfilled with said backfilling material and setting the filling, (f) applying a backsize over that array of yarns of the fabric that has been filled, (g) filling the unbackfilled array of the fabric with a phenolic resin/calcium carbonate filler mixture having a resin to filler ratio of about 1.1:1 on a dry weight basis.
Claim 11
Dependent Claim
70 words
The method of claim 8 wherein the fabric is formed of polyester warp yarns further comprising stretching the dried fabric, maintaining lengthwise tension on the fabric while the fabric is exposed in an oven at about 445° F. (229.5° C.) for a period of about 2.2 minutes and thereafter quenching the fabric with forced ambient air while maintaining sufficient lengthwise tension on the fabric to prevent further lengthwise shrinkage thereof.
Claim 12
Dependent Claim
32 words
The method of claim 8 wherein subsequent to heat setting of the encapsulated fabric the width of the fabric is reduced by removal of a predetermined amount from each longitudinally extending edge.
Claim 13
Dependent Claim
14 words
The method of claim 1 further comprising bonding abrasive grains to said sheet material.
Claim 14
Dependent Claim
15 words
The method of claim 11 further comprising forming the sheet material into an endless belt.
Claim 15
Dependent Claim
30 words
The process of claim 4 further comprising prior to step (d) reducing the width of the heat set fabric by removal of a predetermined amount from each longitudinally extending edge.
Claim 16
Dependent Claim
14 words
The method of claim 8 further comprising bonding abrasive grains to said sheet material.
References Cited (Backward Citations)
CA722882A
Cited
US2130944A
Cited
US2288649A
Cited
US2890579A
Cited
US3030743A
Cited
GB1016484A
Cited
US3972161A
Cited
US3732652A
Cited
GB1410153A
Cited
US3991593A
Cited
US4215516A
Cited
EP0045408A1
Cited
US4396657A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-23 | 1988-04-23 | 1988-10-23 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-23 | 1992-04-23 | 1992-10-23 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-23 | 1996-04-23 | 1996-10-23 | $7700.00 | Window Closed / Lapsed |