Claim 2

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains having at least 12% nominal iodide mole percent dispersed in gelatin characterized by having said grains including at least three different iodo-bromide phases having different iodide contents, the most external phase having an iodide content lower than the nominal iodide content.

Claim 3

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains dispersed in gelatin of claim 1 characterized by having said grains including four phases having different iodide contents, the first of said grain phases having an iodide content lower than the nominal iodide content and the fourth of said phases being hundred percent iodide, the second and third phases having iodide contents higher than the nominal iodide content.

Claim 4

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains dispersed in gelatin of claims 1 or 2, wherein the silver iodo-bromide emulsion nominally contains 12 to 25 moles percent of iodide.

Claim 5

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains dispersed in gelatin of claims 1 or 2, wherein the first silver iodo-bromide phase contains 5 to 15 moles percent of iodide.

Claim 6

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains dispersed in gelatin of claims 1 or 2 wherein the second silver iodo-bromide phase contains 15 to 25 moles percent of iodide.

Claim 7

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains dispersed in gelatin of claims 1 or 2 wherein the third silver iodo-bromide phase contains 30 to 70 moles percent of iodide.

Claim 8

High-sensitivity photographic emulsion consisting of high-iodide silver iodo-bromide grains dispered in gelatin of claim 3 wherein the percent iodide content of the first silver iodo-bromide phase is 50 to 70 percent of the nominal percent iodide content of the silver iodobromide emulsion.

Claim 9

High-sensitivity photographic emulsion consisting of high-iodide silver iodo-bromide grains dispersed in gelatin of claim 4 wherein the percent iodide content of the first silver iodo-bromide phase is 50 to 70 percent of the nominal percent iodide content of the silver iodo-bromide emulsion.

Claim 10

High-sensitivity photographic emulsion consisting of silver iodo-bromide grains dispersed in gelatin of claim 2, wherein the percent iodide content of the first silver iodo-bromide phase is 50 to 70 percent of the nominal percent iodide content of the silver iodo-bromide emulsion, the second silver iodo-bromide phase contains 15 to 25 moles percent of iodide and the third silver iodobromide phase contains 30 to 70 moles percent of iodide.

Claim 11

A light-sensitive photographic element comprising a support having coated thereon at least one layer comprising the silver iodo-bromide emulsion of claims 1 or 2 associated with color-forming couplers.

Claim 12

A light-sensitive photographic element comprising a support having coated thereon at least one layer comprising the silver iodo-bromide emulsion of claim 4 associated with color-forming couplers.

Claim 13

A light-sensitive photographic element comprising support having coated thereon at least one layer comprising the silver iodo-bromide emulsion of claim 5 associated with color-forming couplers.

Claim 14

A light-sensitive photographic element comprising a support having coated thereon at least one layer comprising the silver iodo-bromide emulsion of claim 9 associated with color forming couplers.

Claim 15

A photographic color reversal film comprising a support having coated thereon at least one red-sensitive silver halide emulsion layer including cyan-image forming couplers, at least one green-sensitive silver halide emulsion layer including magenta-image forming couplers, a yellow filter layer and at least one blue-sensitive silver halide emulsion layer including yellow-image forming couplers, wherein the blue-sensitive silver halide emulsion is the high-iodide silver iodo-bromide emulsion of claims 1 or 2.

Claim 16

A photographic color reversal film comprising a support having coated thereon at least one red-sensitive silver halide emulsion layer including cyan-image forming couplers, at least one green-sensitive silver halide emulsion layer including magenta-image forming couplers, a yellow filter layer and at least one blue-sensitive silver halide emulsion layer including yellow-image forming couplers, wherein the blue-sensitive silver halide emulsion is the high-iodide silver iodo-bromide emulsion of claim 4.

Claim 17

A photographic color reversal film comprising a support having coated thereon at least one red-sensitive silver halide emulsion layer including cyan-image forming couplers, at least one green-sensitive silver halide emulsion layer including magenta-image forming couplers, a yellow filter layer and at least one blue-sensitive silver halide emulsion layer including yellow-image forming couplers, wherein the blue-sensitive silver halide emulsion is the high-iodide silver iodo-bromide emulsion of claim 5.

Claim 18

A photographic color reversal film comprising a support having coated thereon at least one red-sensitive silver halide emulsion layer including cyan-image forming couplers, at least one green-sensitive silver halide emulsion layer including magenta-image forming couplers, a yellow filter layer and at least one blue-sensitive silver halide emulsion layer including yellow image forming couplers, wherein the blue-sensitive silver halide emulsion is the high-iodide silver iodo-bromide emulsion of claim 9.

Claim 19

A process for preparing a high-sensitivity high-iodide silver iodo-bromide photographic emulsion which comprises the following sequential steps: (1) adding an aqueous ammoniacal water-soluble silver salt solution into an aqueous alkali metal or ammonium bromide and iodide gelatin solution to precipitate a minor quantity of total iodide; (2) digesting at pH higher than 9 and pAg higher than 8 to obtain coarse silver iodide nuclei; (3) continuing the addition of the water-soluble silver salt solution to the alkali metal or ammonium bromide and iodide solution in low-ammoniacal and high temperature conditions to precipitate all silver halide in finer silver bromide and iodo-bromide grains; (4) digesting at pAg and pH near neutrality to obtain coarse silver iodo-bromide grains; (5) removing any water-soluble salts from the emulsion; and (6) chemically sensitizing the emulsion.

Claim 20

A process for preparing a high-sensitivity high-iodide silver iodo-bromide photographic emulsion which comprises the following sequential steps: (1) adding an aqueous ammoniacal water-soluble silver salt solution into an aqueous alkali metal or ammonium bromide and iodide gelatin solution to precipitate a minor quantity of total iodide; (2) digesting at pH higher than 9 and pAg higher than 8 to obtain coarse silver iodide nuclei; (3) continuing the addition of the water-soluble silver salt solution to the alkali metal or ammonium bromide and iodide solution in low-ammoniacal and high temperature conditions to precipitate all silver halide in finer silver bromide and iodo-bromide grains; (4) digesting at pAg and pH near neutrality to obtain coarse silver iodo-bromide grains; (5) removing any water-soluble salts from the emulsion; and (6) chemically sensitizing the emulsion.

Claim 21

A high-sensitivity photographic emulsion comprising silver iodo-bromide grains having at least 12% nominal iodide mole percent dispersed in gelatin characterized by said grains having at least three different iodo-bromide phases having different iodide contents, the most external phase having an iodide content lower than the nominal iodide content and the innermost phase consisting of pure silver iodide.

Claim 22

A high-sensitivity photographic emulsion comprising silver iodo-bromide grains having at least 12% nominal iodide mole percent dispersed in gelatin characterized by said grains having at least three different iodo-bromide phases having different iodide contents, the most external phase having an iodide content lower than the nominal iodide content and the innermost phase consisting of pure silver iodide.