US4477536A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for preparing a multilayer coating
Assignee: BASF Corp
•
Filing: 1983-05-11
•
Granted: 1984-10-16
•
Expires: 2003-05-11
Abstract
Abstract Multilayer coatings having at least one base coating containing pigments and at least one transparent top coating are applied from coating compositions on the substrates and cured together. The coating composition contains: (a) a film-forming synthetic resin; (b) an organic solvent in which the synthetic resin is soluble; and (c) polymer microparticles having polar and/or ionic groups on their surfaces and a diameter of about 0.01 to 5 microns obtained by emulsion polymerization of ethylene unsaturated monomers, these monomers having a portion comprising 2 or more double bonds per molecule and the microparticles are insoluble in the solution of (a) and (b). The base coat(s) have (d) pigments and the top coats are free of pigments.
Inventors
- 👤 Howard J. Wright
- 👤 David P. Leonard
- 👤 Roger A. Etzell
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 13:50
CPC Classifications
B; B05; B05D; B05D7/00; B05D7/50; B05D7/52; B05D7/53; B05D7/532; C; C09; C09D; C09D5/00; C09D5/38; Y; Y10; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31678; Y10T428/31681; Y10T428/31688; Y10T428/31692; Y10T428/31699; Y10T428/31786; Y10T428/31797; Y10T428/31855; Y10T428/31859; Y10T428/31935
Claims Analysis
Total Claims: 28
Claim 1
Independent Claim
343 words
A process for preparing a multilayer coating on a substrate consisting of at least one base coating containing pigments on said substrate and at least one transparent top coating on said base coating with improved pigment settling on storage of said base coating material, and excellent pigment orientation in said multilayer coating, comprising: (1) applying a coating composition as said base coating consisting essentially of (a) 10 to 60% by weight of a film-forming synthetic resin; (b) 40 to 80% by weight of an organic solvent in which said synthetic resin is soluble; (c) 2.5 to 25% by weight of polymer microparticles having ionic or a mixture of polar and ionic groups on their surfaces and having a diameter of 0.01 to 5 microns prepared by emulsion-polymerizing ethylene-unsaturated monomers in an aqueous phase, at least one of said monomers selected from the group consisting of acrylic acid, methacrylic acid, and substituted alkyl esters thereof and containing a polar functional group and at least another of said monomers selected from the group consisting of an alkyl ester of acrylic acid, an alkyl ester of methacrylic acid, styrene and methyl styrene, said another of said monomers free of polar functional groups and a multi-functional crosslinking agent present in an amount of 5 to 70% by weight of the total weight of said ethylenically unsaturated monomers and said crosslinking agent, said crosslinking agent crosslinking said microparticles to a degree that said polar and said ionic groups are fixed on the surface of said microparticles, and subsequently removing water from said aqueous phase, said microparticles being insoluble in the solution of said synthetic resin in said organic solvent, and having said polar and ionic groups fixed on the surfaces, rearrangement of said polar and ionic groups into the particle interior being prevented by the crosslinking from said crosslinking agent; and (d) 2 to 40 weight percent pigments (2) applying said transparent top coating on said base coating; and (3) curing (1) and (2) together to form a crosslinked transparent top coat film upon a base coat film.
Claim 2
Dependent Claim
343 words
A process for preparing a multilayer coating on a substrate consisting of at least one base coating containing pigments on said substrate and at least one transparent top coating on said base coating with improved pigment settling on storage of said base coating material, and excellent pigment orientation in said multilayer coating, comprising: (1) applying a coating composition as said base coating consisting essentially of (a) 10 to 60% by weight of a film-forming synthetic resin; (b) 40 to 80% by weight of an organic solvent in which said synthetic resin is soluble; (c) 2.5 to 25% by weight of polymer microparticles having ionic or a mixture of polar and ionic groups on their surfaces and having a diameter of 0.01 to 5 microns prepared by emulsion-polymerizing ethylene-unsaturated monomers in an aqueous phase, at least one of said monomers selected from the group consisting of acrylic acid, methacrylic acid, and substituted alkyl esters thereof and containing a polar functional group and at least another of said monomers selected from the group consisting of an alkyl ester of acrylic acid, an alkyl ester of methacrylic acid, styrene and methyl styrene, said another of said monomers free of polar functional groups and a multi-functional crosslinking agent present in an amount of 5 to 70% by weight of the total weight of said ethylenically unsaturated monomers and said crosslinking agent, said crosslinking agent crosslinking said microparticles to a degree that said polar and said ionic groups are fixed on the surface of said microparticles, and subsequently removing water from said aqueous phase, said microparticles being insoluble in the solution of said synthetic resin in said organic solvent, and having said polar and ionic groups fixed on the surfaces, rearrangement of said polar and ionic groups into the particle interior being prevented by the crosslinking from said crosslinking agent; and (d) 2 to 40 weight percent pigments (2) applying said transparent top coating on said base coating; and (3) curing (1) and (2) together to form a crosslinked transparent top coat film upon a base coat film.
Claim 3
Dependent Claim
48 words
The process of claim 1, wherein said microparticles (c) are prepared in the form of an aqueous dispersion, and as such are added to a solution of said synthetic resin (a) in said organic solvent (b) and thereupon water from said aqueous dispersion is removed by azeotropic distillation.
Claim 4
Dependent Claim
42 words
The process of claim 1, wherein said microparticles (c) are prepared by spray drying, freeze drying, centrifuging, salting out or freezing out of the aqueous phase and thereupon are added to a solution of said synthetic resin (a) in said solvent (b).
Claim 5
Dependent Claim
66 words
The process of claim 1, wherein said microparticles (c) are obtained in the form of an aqueous dispersion and as such are added to the components for the preparation of said synthetic resin (a), said synthetic resin (a) is prepared in the presence of said microparticles (c) and water is removed from said aqueous dispersion by azeotropic distillation during the preparation of said synthetic resin (a).
Claim 6
Dependent Claim
36 words
The process of claim 1, wherein said synthetic resin (a) is a homo- or co-polymer prepared by polymerizing ethylene-unsaturated monomers having at least a portion of said synthetic resin as alkylesters of acrylic or methacrylic acid.
Claim 7
Dependent Claim
18 words
The process of claim 1, wherein said synthetic resin (a) is an alkyd resin or a polyester resin.
Claim 8
Dependent Claim
14 words
The process of claim 1, wherein said synthetic resin (a) is an aminoplastic resin.
Claim 9
Dependent Claim
29 words
The process of claim 1, wherein said microparticles (c) are prepared by homo- or co-polymerizing ethylene-unsaturated monomers having at least a portion of alkylesters of acrylic or methacrylic acid.
Claim 10
Dependent Claim
20 words
The process of claim 1, wherein said top coating is applied as a film-forming synthetic resin in an organic solvent.
Claim 11
Dependent Claim
111 words
The process of claim 1, wherein said top coating is deposited in the form of a coating composition containing: (a) a film-forming synthetic resin; (b) an organic solvent in which said synthetic resin is soluble; and (c) polymer microparticles having polar, ionic or a mixture of polar and ionic groups on their surfaces and having a diameter from about 0.01 to 5 microns prepared by emulsion-polymerizing ethylene-unsaturated monomers, said monomers having one portion comprising 2 or more double bonds per molecule, in an aqueous phase and by subsequent removal of water from said aqueous phase, and said microparticles being insoluble in the solution of said synthetic resin in said organic solvent.
Claim 12
Dependent Claim
14 words
The process of claim 1, wherein said top coating is a pulverulent coating composition.
Claim 13
Dependent Claim
12 words
The process of claim 1, wherein said pigments (d) are metallic pigments.
Claim 14
Dependent Claim
36 words
The process of claim 1, wherein the concentration of said microparticles (c) in said coating composition amounts to about 2-60% by weight referred to the total weight of said synthetic resin (a) and said microparticles (c).
Claim 15
Dependent Claim
15 words
A coated substrate having a multilayer coating thereon prepared by the process of claim 12.
Claim 16
Dependent Claim
17 words
The process of claim 1, wherein said polymer microparticles have a diameter of 0.05 to 0.5 microns.
Claim 17
Dependent Claim
21 words
The process of claim 1, wherein said polar functional groups are selected from hydroxy groups, tertiary amine, and sulfonic acid groups.
Claim 18
Dependent Claim
74 words
The process of claim 16, wherein the amount of ethylenically unsaturated monomer containing said hydroxy, tertiary amine or sulfonic acid groups used in the preparation of the polymeric microparticles ranges from 10 to 50 weight percent and the amount of said ethylenically unsaturated monomer free from said hydroxy, tertiary amine or sulfonic acid groups ranges from 70 to 10 percent by weight of the total weight of said ethylenically unsaturated monomers and crosslinking agent.
Claim 19
Dependent Claim
41 words
The process of claim 1, wherein the amount of the multifunctional crosslinking agent used for the preparation of the polymer microparticles amounts to 10 percent to 50 percent by weight of the total weight of ethylenically unsaturated monomers and crosslinking agent.
Claim 20
Dependent Claim
46 words
The process of claim 1, wherein the concentration of said microparticles (c) in said base coat composition amounts to about 5 to 50 percent and preferably 10 to 35 percent by weight referred to the total weight of said synthetic resins (a) and said microparticles (c).
Claim 21
Dependent Claim
133 words
The process of claim 1, wherein said film-forming synthetic resins (a) are a combination of an aminoplast resin and a copolymer of a mixture of ethylenically unsaturated monomers, at least one of said monomers selected from the group consisting of acrylic acid, methacrylic acid, a substituted alkyl ester of acrylic acid containing a free hydroxy group, a substituted alkyl ester of methacrylic acid containing a free hydroxy group, a substituted alkyl ester of acrylic acid containing a free epoxy group and a substituted alkyl ester of methacrylic acid containing a free epoxy group and at least another of said monomers selected from the group consisting of unsubstituted alkyl ester of acrylic acid, unsubstituted alkyl ester of methacrylic acid, styrene and methyl styrene aminoplast resin to copolymer being from 50:50 to 16:84 weight percent.
Claim 22
Dependent Claim
49 words
The process of claim 1, wherein said film-forming synthetic resins (a) are a combination of an aminoplast resin and a second resin selected from the group consisting of alkyd resins and polyester resins and the weight ratio of aminoplast resin to said second resin is from 50:50 to 16:84.
Claim 23
Dependent Claim
27 words
The process of claim 1, wherein said transparent coating is deposited in the form of a coating composition containing: (a) film-forming synthetic resins; and (b) organic solvents.
Claim 24
Dependent Claim
22 words
The process of claim 22, wherein said film-forming synthetic resins are a combination of a thermosetting acrylic copolymer and an aminoplast resin.
Claim 25
Dependent Claim
31 words
The process of claim 22, where said film-forming resins are a combination of an alkyd resin and a second resin selected from the group consisting of polyester resins and aminoplast resins.
Claim 26
Dependent Claim
34 words
The process of claim 22, where said film-forming resins are a combination of an alkyd resin and a second resin selected from the group consisting of polyester resins, thermosetting acrylic copolymers, and aminoplast resins.
Claim 27
Dependent Claim
171 words
The process of claim 22, wherein said transparent coating is deposited in the form of a coating composition consisting essentially of (a) film-forming synthetic resins; (b) organic solvents; and (c) polymeric microparticles having a diameter of 0.01 to 5 microns, prepared by emulsion polymerization in water of a mixture of ethylenically unsaturated monomers, at least one of said monomers selected from the group consisting of acrylic acid, methacrylic acid, and substituted alkyl esters thereof and containing polar functional groups and at least another of said monomers being selected from the group consisting of alkyl esters of acrylic acid, alkyl esters of methacrylic acid, styrene and methyl styrene and being free of polar functional groups, and a multifunctional crosslinking agent present in an amount of at least 5 and up to 50 percent by weight of the total weight of said ethylenically unsaturated monomers and crosslinking agent, and by subsequent removal of water from said aqueous phase, said microparticles being insoluble in the solution of said synthetic resin in said organic solvent.
Claim 28
Dependent Claim
37 words
The process of claim 26, wherein the concentration of said microparticles in said transparent top coating composition amounts to from 2 to 15 percent by weight referred to the total weight of said synthetic resins and microparticles.
References Cited (Backward Citations)
US4220679A
Cited
US4403003A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-16 | 1988-04-16 | 1988-10-16 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-16 | 1992-04-16 | 1992-10-16 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-16 | 1996-04-16 | 1996-10-16 | $7700.00 | Window Closed / Lapsed |