Deep trench etching process using CCl2 F2 /Ar and CCl2 F.sub. /O2 RIE
Assignee: International Business Machines Corp
•
Filing: 1983-12-12
•
Granted: 1984-10-09
•
Expires: 2003-12-12
Abstract
Abstract This invention relates to a process for forming deep trenches in semiconductor substrates by Reactive Ion Etching and more particularly relates to an etching process which prevents lateral etching or "blooming" in a heavily doped semiconductor region which is sandwiched by upper and lower lightly doped regions of semiconductor. Still more particularly it relates to an RIE process wherein the upper region is reactively ion etched in an atmosphere of CCl2F2 and argon to at least a portion of the thickness of the upper region and wherein any remaining thickness of the upper region, the heavily doped region and at least a portion of the lower region are reactively ion etched in an atmosphere of CCl2F2 and oxygen to provide a trench with uniform sidewalls.
Inventors
- 👤 Fang-shi J. Lai
- 👤 Ronald N. Schulz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-28 17:24
CPC Classifications
H; H10; H10P; H10P50/00; H10P50/20; H10P50/24; H10P50/242
Claims Analysis
Total Claims: 22
Claim 1
Independent Claim
100 words
A method of forming deep trenches with uniform sidewalls in a semiconductor structure wherein said structure includes a heavily doped region sandwiched between upper and lower lightly doped regions comprising the steps of: reactively ion etching said upper lightly doped region in an atmosphere of CCl 2 F 2 and argon to at least a portion of the thickness of said upper region, and, subsequently reactively ion etching any remaining thickness of said upper region and said heavily doped region and at least a portion of said lower lightly doped region in an atmosphere CCl 2 F 2 and oxygen.
Claim 2
Independent Claim
100 words
A method of forming deep trenches with uniform sidewalls in a semiconductor structure wherein said structure includes a heavily doped region sandwiched between upper and lower lightly doped regions comprising the steps of: reactively ion etching said upper lightly doped region in an atmosphere of CCl 2 F 2 and argon to at least a portion of the thickness of said upper region, and, subsequently reactively ion etching any remaining thickness of said upper region and said heavily doped region and at least a portion of said lower lightly doped region in an atmosphere CCl 2 F 2 and oxygen.
Claim 3
Dependent Claim
31 words
A method according to claim 1 further including the step of masking the surface of said upper region to provide at least an exposed surface portion prior to reactive ion etching.
Claim 4
Dependent Claim
94 words
A method according to claim 1 wherein the step of reactively ion etching in an atmosphere of CCl 2 F 2 and argon includes the steps of: introducing said atmosphere of CCl 2 F 2 and argon into an evacuated reactive ion etching reactor at a pressure in the range of 18-23 microns, at a flow in the range of 20-25 standard cubic centimeters per minute and at a gas ratio (by volume) of CCl 2 F 2 to argon of 1, and, applying power in a range of 90-110 watts to said reactor.
Claim 5
Dependent Claim
94 words
A method according to claim 1 wherein the step of reactively ion etching in an atmosphere of CCl 2 F 2 and oxygen includes the step of: introducing said atmosphere of CCl 2 F 2 and oxygen into said evacuated reactive ion etching reactor at a pressure in the range of 18-23 microns, at a flow in the range of 20-25 standard cubic centimeters per minute and at a gas ratio (by volume) of CCl 2 F 2 to oxygen of 1, and, applying power in a range of 90-110 watts to said reactor.
Claim 6
Dependent Claim
37 words
A method according to claim 1 wherein said semiconductor is silicon, said heavily doped region and said upper region are doped with an n-conductivity type dopant and said lower region is doped with a p-conductivity type dopant.
Claim 7
Dependent Claim
37 words
A method according to claim 1 wherein said semiconductor is silicon, said heavily doped region and said upper region are doped with a p-conductivity type dopant and said lower region is doped with an n-conductivity type dopant.
Claim 8
Dependent Claim
28 words
A method according to claim 1 wherein said semiconductor is silicon, said heavily doped region and said upper and lower regions are doped with an n-conductivity type dopant.
Claim 9
Dependent Claim
28 words
A method according to claim 1 wherein said semiconductor is silicon, said heavily doped region and said upper and lower regions are doped with a p-conductivity type dopant.
Claim 10
Dependent Claim
18 words
A method according to claim 1 wherein said heavily doped region is an ion implanted or diffused region.
Claim 11
Dependent Claim
19 words
A method according to claim 1 wherein said upper region is formed from an epitaxially deposited layer of semiconductor.
Claim 12
Dependent Claim
80 words
A method according to claim 2 wherein the step of masking includes the steps of forming at least a layer of masking material on said surface of said upper region, forming a layer of photoresist on said at least a layer of masking material and exposing at least a portion of said resist to radiation, and, developing said photoresist to remove said at least a portion of said layer of photoresist to provide said at least an exposed surface portion.
Claim 13
Dependent Claim
35 words
A method according to claim 11 wherein the step of forming at least a layer of masking material includes the step of depositing a layer of silicon nitride on said surface of said upper region.
Claim 14
Dependent Claim
35 words
A method according to claim 11 wherein the step of forming at least a layer of masking material includes the step of depositing a layer of silicon oxide on said surface of said upper region.
Claim 15
Dependent Claim
23 words
A method according to claim 12 further including the step of depositing a layer of silicon oxide on said layer of silicon nitride.
Claim 16
Independent Claim
189 words
A method of forming deep trenches with uniform sidewalls in a semiconductor structure wherein said structure includes a heavily doped region sandwiched between upper and lower lightly doped regions comprising the steps of: placing at least one of said structures in a reactive ion etching reactor, introducing an atmosphere of CCl 2 F 2 and argon into said reactor at a pressure of 20 microns, at a flow of 20 standard cubic centimeters per minute and at a gas ratio (by volume) of CCl 2 F 2 to argon of 1, applying power of 100 watts to said reactor, reactively ion etching said upper lightly doped region to a depth up to the thickness of said upper region, evacuating said reactor, introducing an atmosphere of CCl 2 and oxygen into said reactor at a pressure of 20 microns, at a flow of 20 standard cubic centimeters per minute and at a gas ratio (by volume) of CCl 2 F 2 to oxygen of 1, applying power of 100 watts to said reactor, and, reactively ion etching said heavily doped region and at least a portion of said lower region.
Claim 17
Independent Claim
189 words
A method of forming deep trenches with uniform sidewalls in a semiconductor structure wherein said structure includes a heavily doped region sandwiched between upper and lower lightly doped regions comprising the steps of: placing at least one of said structures in a reactive ion etching reactor, introducing an atmosphere of CCl 2 F 2 and argon into said reactor at a pressure of 20 microns, at a flow of 20 standard cubic centimeters per minute and at a gas ratio (by volume) of CCl 2 F 2 to argon of 1, applying power of 100 watts to said reactor, reactively ion etching said upper lightly doped region to a depth up to the thickness of said upper region, evacuating said reactor, introducing an atmosphere of CCl 2 and oxygen into said reactor at a pressure of 20 microns, at a flow of 20 standard cubic centimeters per minute and at a gas ratio (by volume) of CCl 2 F 2 to oxygen of 1, applying power of 100 watts to said reactor, and, reactively ion etching said heavily doped region and at least a portion of said lower region.
Claim 18
Dependent Claim
31 words
A method according to claim 15 further including the step of masking the surface of said upper region prior to reactively ion etching to provide at least an exposed surface portion.
Claim 19
Dependent Claim
45 words
A method according to claim 16 wherein said semiconductor is silicon, said upper region is a layer of epitaxially deposited, n-conductivity type silicon, said lower region is a region of p-conductivity type silicon and said heavily doped region is a region of n-conductivity type silicon.
Claim 20
Dependent Claim
45 words
A method according to claim 16 wherein said semiconductor is silicon, said upper region is a layer of epitaxially deposited, p-conductivity type silicon, said lower region is a region of n-conductivity type silicon and said heavily doped region is a region of p-conductivity type silicon.
Claim 21
Dependent Claim
28 words
A method according to claim 16 wherein said semiconductor is silicon, said heavily doped region and said upper and lower regions are all regions of n-conductivity type silicon.
Claim 22
Dependent Claim
28 words
A method according to claim 16 wherein said semiconductor is silicon, said heavily doped region and said upper and lower regions are all regions of p-conductivity type silicon.
References Cited (Backward Citations)
No citation records indexed.
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |