Annealing method for amorphous magnetic alloy
Assignee: Sony Corp
•
Filing: 1983-07-07
•
Granted: 1984-10-09
•
Expires: 2003-07-07
Abstract
Abstract Annealing method for an amorphous magnetic alloy including the steps of preparing an amorphous magnetic alloy film, and annealing the amorphous magnetic alloy film at an elevated temperature lower than Curie temperature and crystallization temperature of the amorphous magnetic alloy film under an application of a repetition of alternately applied a first magnetic field and a second magnetic field, in which the first magnetic field is applied along one direction in a major surface of the amorphous magnetic alloy film for a predetermined period, and the second magnetic field is applied along a second direction perpendicular to the one direction in the major surface of the amorphous magnetic alloy film for the predetermined period.
Inventors
- 👤 Masatoshi Hayakawa
- 👤 Koichi Aso
- 👤 Satoru Uedaira
- 👤 Yoshitaka Ochiai
- 👤 Hideki Matsuda
- 👤 Kazuhide Hotai
- 👤 Kazuhiko Hayashi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 10:55
CPC Classifications
H; H01; H01F; H01F1/00; H01F1/01; H01F1/03; H01F1/12; H01F1/14; H01F1/147; H01F1/153; H01F1/15341; C; C21; C21D; C21D1/00; C21D1/04
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
116 words
Annealing method for an amorphous magnetic alloy comprising the steps of: (a) preparing an amorphous magnetic alloy film; (b) annealing said amorphous magnetic alloy film at an elevated temperature lower than Curie temperature and crystallization temperature of said amorphous magnetic alloy film under a application of a cyclically applied first magnetic field and second magnetic field, said first magnetic field being applied along one direction in a major surface of said amorphous magnetic alloy film for a predetermined period, and said second magnetic field being applied after termination of said first magnetic field along a second direction perpendicular to said one direction in said major surface of said amorphous magnetic alloy film for said predetermined period.
Claim 2
Dependent Claim
116 words
Annealing method for an amorphous magnetic alloy comprising the steps of: (a) preparing an amorphous magnetic alloy film; (b) annealing said amorphous magnetic alloy film at an elevated temperature lower than Curie temperature and crystallization temperature of said amorphous magnetic alloy film under a application of a cyclically applied first magnetic field and second magnetic field, said first magnetic field being applied along one direction in a major surface of said amorphous magnetic alloy film for a predetermined period, and said second magnetic field being applied after termination of said first magnetic field along a second direction perpendicular to said one direction in said major surface of said amorphous magnetic alloy film for said predetermined period.
Claim 3
Dependent Claim
144 words
Annealing method for an amorphous alloy comprising annealing an amorphous magnetic alloy film at an elevated temperature lower than Curie temperature and crystallization temperature of said amorphous magnetic alloy sheet under application of magnetic field of a combination of the following manners I and II, said manner I being an application of a cyclically applied first magnetic field and second magnetic field, said first magnetic field being applied along one direction in a major surface of said amorphous magnetic alloy film for a predetermined period, and said second magnetic field being applied after termination of said first magnetic field along a second direction perpendicular to said one direction in said major surface of said amorphous magnetic alloy film for said predetermined period, and said manner II being an application of a magnetic field perpendicular to said major surface of said amorphous magnetic alloy sheet.
Claim 4
Dependent Claim
144 words
Annealing method for an amorphous alloy comprising annealing an amorphous magnetic alloy film at an elevated temperature lower than Curie temperature and crystallization temperature of said amorphous magnetic alloy sheet under application of magnetic field of a combination of the following manners I and II, said manner I being an application of a cyclically applied first magnetic field and second magnetic field, said first magnetic field being applied along one direction in a major surface of said amorphous magnetic alloy film for a predetermined period, and said second magnetic field being applied after termination of said first magnetic field along a second direction perpendicular to said one direction in said major surface of said amorphous magnetic alloy film for said predetermined period, and said manner II being an application of a magnetic field perpendicular to said major surface of said amorphous magnetic alloy sheet.
Claim 5
Dependent Claim
22 words
Annealing method for an amorphous magnetic alloy according to claim 1, wherein said elevated temperature is selected as 200° C. or more.
Claim 6
Dependent Claim
22 words
Annealing method for an amorphous magnetic alloy according to claim 2, wherein said elevated temperature is selected as 200° C. or more.
Claim 7
Dependent Claim
24 words
Annealing method for an amorphous magnetic alloy according to claim 1, wherein said Curie temperature is selected to be higher than said crystallization temperature.
Claim 8
Dependent Claim
24 words
Annealing method for an amorphous magnetic alloy according to claim 2, wherein said Curie temperature is selected to be higher than said crystallization temperature.
Claim 9
Dependent Claim
50 words
Annealing method for an amorphous magnetic alloy according to claim 1, wherein a switching at which said first magnetic field is changed to said second magnetic field is carried out in time shorter than a relaxation time during which induced magnetic anisotropy of said amorphous magnetic alloy increases or decreases.
Claim 10
Dependent Claim
50 words
Annealing method for an amorphous magnetic alloy according to claim 2, wherein a switching at which said first magnetic field is changed to said second magnetic field is carried out in time shorter than a relaxation time during which induced magnetic anisotropy of said amorphous magnetic alloy increases or decreases.
References Cited (Backward Citations)
US4116728A
Cited
US4116728B1
Cited
US4268325A
Cited
US4379004A
Cited
US4312683A
Cited
JPS5644746A
Cited
JPS5669360A
Cited
GB2088415A
Cited
JPS57114646A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-09 | 1988-04-09 | 1988-10-09 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-09 | 1992-04-09 | 1992-10-09 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-09 | 1996-04-09 | 1996-10-09 | $7700.00 | Window Closed / Lapsed |