Stabilized slurries of isoolefin polymers
Assignee: ExxonMobil Technology and Engineering Co
•
Filing: 1983-01-27
•
Granted: 1984-10-02
•
Expires: 2003-01-27
Abstract
Abstract Polymerization slurries of elastomeric isoolefin homopolymers and copolymers, such as butyl rubber, in diluents such as methyl chloride are effectively stabilized against agglomeration of polymer particles through addition of minor proportions of an hydrogenated preformed copolymer stabilizer having both a lyophobic and a lyophilic portion. The chemical and structural nature of the lyophobic and lyophilic portions which comprise the copolymer stabilizer are significant in determining the extent and method of hydrogenation for production of the most effective stabilizer. Agglomeration of polymer products is effectively prevented, yielding a number of significant processing advantages. The process is especially adaptable to the production of isobutylene-isoprene butyl rubber.
Inventors
- 👤 Kenneth W. Powers
- 👤 Hsien C. Wang
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 21:15
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/04; C08F6/00; C08F6/24; C08L; C08L23/00; C08L23/02; C08L23/18; C08L23/20; C08L23/22; Y; Y10; Y10S; Y10S524/00; Y10S524/923
Claims Analysis
Total Claims: 41
Claim 1
Independent Claim
261 words
An improved method of stabilizing a polymerization slurry against agglomeration, said slurry being formed in a cationic Lewis Acid catalyzed polymerization process, and containing as product polymers, polymerized C 4 -C 7 isoolefin homopolymers or butyl rubber copolymers in a polymerization diluent selected from the group consisting of methyl chloride, methylene chloride, vinyl chloride or ethyl chloride diluents, which comprises incorporating into the reaction mixture, said reaction mixture comprising monomers, catalyst and diluent, or into the polymerization product slurry about 0.05% to 20% by weight, based upon the weight of product polymers, of a stabilizing agent, said stabilizing agent being a preformed copolymer having a lyophilic; polymerization diluent soluble portion and a lyophobic; polymerization diluent insoluble portion, said lyophobic portion being soluble in or adsorbable by said product polymer and said stabilizing agent being capable of forming an adsorbed solubilized polymer coating around the precipitated isoolefin homopolymer or butyl rubber copolymer to stabilize said slurry, wherein the improvement comprises utilizing as said preformed copolymer stabilizing agent, an hydrogenated block copolymer wherein cationically active unsaturation initially present in said stabilizing agent has been reduced and stabilizing effectiveness has been increased by said hydrogenation without causing said stabilizing agent to become insoluble in said reaction mixture, wherein the lyophobic portion of the preformed copolymer prior to hydrogenation is a member of the group consisting of polymerized C 4 -C 7 isoolefins, butyl rubber copolymers, polybutadiene, polyisoprene, EPDM terpolymers, styrene/butadiene random copolymers of low styrene content (SBR rubbers), and mixtures thereof, the lyophobic portion having a degree of polymerization of at least about 10.
Claim 2
Dependent Claim
261 words
An improved method of stabilizing a polymerization slurry against agglomeration, said slurry being formed in a cationic Lewis Acid catalyzed polymerization process, and containing as product polymers, polymerized C 4 -C 7 isoolefin homopolymers or butyl rubber copolymers in a polymerization diluent selected from the group consisting of methyl chloride, methylene chloride, vinyl chloride or ethyl chloride diluents, which comprises incorporating into the reaction mixture, said reaction mixture comprising monomers, catalyst and diluent, or into the polymerization product slurry about 0.05% to 20% by weight, based upon the weight of product polymers, of a stabilizing agent, said stabilizing agent being a preformed copolymer having a lyophilic; polymerization diluent soluble portion and a lyophobic; polymerization diluent insoluble portion, said lyophobic portion being soluble in or adsorbable by said product polymer and said stabilizing agent being capable of forming an adsorbed solubilized polymer coating around the precipitated isoolefin homopolymer or butyl rubber copolymer to stabilize said slurry, wherein the improvement comprises utilizing as said preformed copolymer stabilizing agent, an hydrogenated block copolymer wherein cationically active unsaturation initially present in said stabilizing agent has been reduced and stabilizing effectiveness has been increased by said hydrogenation without causing said stabilizing agent to become insoluble in said reaction mixture, wherein the lyophobic portion of the preformed copolymer prior to hydrogenation is a member of the group consisting of polymerized C 4 -C 7 isoolefins, butyl rubber copolymers, polybutadiene, polyisoprene, EPDM terpolymers, styrene/butadiene random copolymers of low styrene content (SBR rubbers), and mixtures thereof, the lyophobic portion having a degree of polymerization of at least about 10.
Claim 3
Dependent Claim
32 words
The method of claim 1 wherein the structure of said block copolymer is a member of the group consisting of diblock, radial block, taper block, star block, linear triblock and multidiblock copolymers.
Claim 4
Dependent Claim
58 words
The method of claim 1 wherein said lyophilic portion is a member of the group consisting of polystyrene, polyvinyl chloride, polyvinyl bromide, neoprene and mono-, di- and trisubstituted polystyrenes, and mixtures thereof, the substituents being halogen or C 1 -C 5 alkyl groups, said lyophilic portion having a degree of polymerization of from about 20 to about 6,000.
Claim 5
Dependent Claim
23 words
The method of claim 1 wherein said preformed copolymer stabilizing agent is selected from the group consisting of styrene/diene block and graft copolymers.
Claim 6
Dependent Claim
17 words
The method of claim 3 wherein said lyophobic portion is polybutadiene and said lyophilic portion is polystyrene.
Claim 7
Dependent Claim
17 words
The method of claim 3 wherein said lyophobic portion is polyisoprene and said lyophilic portion is polystyrene.
Claim 8
Dependent Claim
32 words
The method of claim 3 wherein said lyophilic portion is polystyrene and said polystyrene block content is present in said stabilizing agent at a level of more than about 45 weight percent.
Claim 9
Dependent Claim
14 words
The method of claim 7 wherein the lyophobic portion prior to hydrogenation is polybutadiene.
Claim 10
Dependent Claim
14 words
The method of claim 7 wherein the lyophobic portion prior to hydrogenation is polyisoprene.
Claim 11
Dependent Claim
31 words
The method of claim 8 wherein the initial concentration of vinyl unsaturation in said polybutadiene portion of said block copolymer prior to hydrogenation is about 5 to about 50 mole percent.
Claim 12
Dependent Claim
12 words
The method of claim 1 wherein hydrogenation is accomplished by chemical means.
Claim 13
Dependent Claim
12 words
The method of claim 1 wherein hydrogenation is accomplished by catalytic means.
Claim 14
Dependent Claim
26 words
The method of claim 11 wherein said chemical means includes the use of a reagent selected from the group consisting of diisobutyl aluminum hydride and p-toluene-sulfonyl-hydrazide.
Claim 15
Dependent Claim
15 words
The method of claim 12 wherein said catalytic means include homogeneous and heterogeneous hydrogenation catalysts.
Claim 16
Dependent Claim
33 words
The method of claim 14 wherein said homogeneous catalyst includes soluble complexes of nickel, rhodium, irridium, platinum, osmium, iron, or ruthenium and nickel or cobalt carboxylates in combination with lithium or aluminum alkyls.
Claim 17
Dependent Claim
23 words
The method of claim 14 wherein said heterogeneous catalyst includes supported platinum, palladium or rhodium, and promoted and supported nickel, and Raney nickel.
Claim 18
Dependent Claim
28 words
The method of claim 8 wherein said stabilizer is hydrogenated by chemical means to the extent of about 40 to about 90 percent of the original unsaturation present.
Claim 19
Dependent Claim
20 words
The method of claim 9 wherein more than about 80% of the original unsaturation present in said stabilizer is hydrogenated.
Claim 20
Dependent Claim
20 words
The method of claim 10 wherein said vinyl unsaturation prior to hydrogenation is about 10 to about 48 mole percent.
Claim 21
Dependent Claim
24 words
The method of claim 10 wherein the initial concentration of said vinyl unsaturation is about 20 to about 46 mole percent prior to hydrogenation.
Claim 22
Dependent Claim
27 words
The method of claim 10 wherein hydrogenation is by homogeneous catalytic means to the extent of about 50 to about 100 percent of the original unsaturation present.
Claim 23
Dependent Claim
23 words
The method of claim 10 wherein homogeneous catalytic means are used to hydrogenate about 60 to about 95 percent of said vinyl unsaturation.
Claim 24
Dependent Claim
21 words
The method of claim 22 wherein said stabilizer has a viscosity average molecular weight of from about 45,000 to about 200,000.
Claim 25
Dependent Claim
62 words
The method of claim 10 wherein homogeneous catalytic means are used to hydrogenate about 70 to about 90 percent of the total unsaturation wherein said vinyl unsaturation is originally present at a level of about 32 to about 44 mole percent and wherein said stabilizer has a linear triblock structure and a viscosity average molecular weight of from about 70,000 to 140,000.
Claim 26
Dependent Claim
11 words
The method of claim 1 wherein the diluent is methyl chloride.
Claim 27
Dependent Claim
15 words
The method of claim 1 wherein the product polymer is butyl rubber or polyisobutylene homopolymer.
Claim 28
Dependent Claim
25 words
The method of claim 26 wherein the product polymer is isobutylene-isoprene butyl rubber having a viscosity average molecular weight of about 100,000 to about 800,000.
Claim 29
Dependent Claim
28 words
The method of claim 26 wherein the isobutylene-isoprene butyl rubber has a viscosity average molecular weight of about 250,000 to about 600,000 and the diluent is methyl chloride.
Claim 30
Dependent Claim
10 words
A stabilized slurry produced by the method of claim 1.
Claim 31
Dependent Claim
186 words
An improved method of preparing non-agglomerating homopolymers of C 4 -C 7 isoolefins or butyl rubber copolymers by Lewis Acid cationic polymerization of corresponding monomers in a polymerization slurry diluent selected from the group consisting of methyl chloride, methylene chloride, vinyl chloride and ethyl chloride diluents in the presence of a stabilizer copolymer, the stabilizer copolymer being a preformed copolymer having a lyophilic diluent soluble portion and a lyophobic diluent insoluble but isoolefin or butyl rubber soluble or adsorbable portion, wherein the improvement comprises utilizing as said preformed copolymer stabilizing agent an hydrogenated block copolymer wherein cationically active unsaturation initially present in said stabilizing agent has been reduced and stabilizing effectiveness has been increased by said hydrogenation without causing said stabilizing agent to become insoluble in said reaction mixture, wherein the lyophobic portion of the preformed copolymer prior to hydrogenation is a member of the group consisting of polymerized C 4 -C 7 isoolefins, butyl rubber copolymers, polybutadiene, polyisoprene, EPDM terpolymers, styrene/butadiene random copolymers of low styrene content (SBR rubbers), and mixtures thereof, the lyophobic portion having a degree of polymerization of at least about 10.
Claim 32
Dependent Claim
186 words
An improved method of preparing non-agglomerating homopolymers of C 4 -C 7 isoolefins or butyl rubber copolymers by Lewis Acid cationic polymerization of corresponding monomers in a polymerization slurry diluent selected from the group consisting of methyl chloride, methylene chloride, vinyl chloride and ethyl chloride diluents in the presence of a stabilizer copolymer, the stabilizer copolymer being a preformed copolymer having a lyophilic diluent soluble portion and a lyophobic diluent insoluble but isoolefin or butyl rubber soluble or adsorbable portion, wherein the improvement comprises utilizing as said preformed copolymer stabilizing agent an hydrogenated block copolymer wherein cationically active unsaturation initially present in said stabilizing agent has been reduced and stabilizing effectiveness has been increased by said hydrogenation without causing said stabilizing agent to become insoluble in said reaction mixture, wherein the lyophobic portion of the preformed copolymer prior to hydrogenation is a member of the group consisting of polymerized C 4 -C 7 isoolefins, butyl rubber copolymers, polybutadiene, polyisoprene, EPDM terpolymers, styrene/butadiene random copolymers of low styrene content (SBR rubbers), and mixtures thereof, the lyophobic portion having a degree of polymerization of at least about 10.
Claim 33
Dependent Claim
26 words
The method of claim 30 wherein the butyl rubber is isobutylene-isoprene butyl rubber, the Lewis Acid catalyst is AlCl 3 and the diluent is methyl chloride.
Claim 34
Dependent Claim
22 words
The method of claim 30 wherein the isoolefin homopolymer is polyisobutylene, the catalyst is AlCl 3 and the diluent is methyl chloride.
Claim 35
Dependent Claim
22 words
The method of claim 30 in which the slurry contains up to about 50% by weight butyl rubber copolymer or isoolefin homopolymer.
Claim 36
Dependent Claim
23 words
The product produced by the method of claim 33 wherein the butyl rubber is isobutylene-isoprene butyl rubber and the diluent is methyl chloride.
Claim 37
Dependent Claim
21 words
The product produced by the method of claim 33 wherein the isoolefin homopolymer is polyisobutylene and the diluent is methyl chloride.
Claim 38
Dependent Claim
23 words
The method of claim 18 comprising styrene on the periphery and hydrogenated isoprene in the central portion of a structurally complex block copolymer.
Claim 39
Dependent Claim
23 words
The method of claim 17 comprising styrene on the periphery and hydrogenated butadiene in the central portion of a structurally complex block copolymer.
Claim 40
Dependent Claim
23 words
The method of claim 14 comprising styrene on the periphery and hydrogenated butadiene in the central portion of a structurally complex block copolymer.
Claim 41
Dependent Claim
23 words
The method of claim 30, where said preformed copolymer stabilizing agent is selected from the group consisting of styrene/diene block and graft copolymers.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-02 | 1988-04-02 | 1988-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-02 | 1992-04-02 | 1992-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-02 | 1996-04-02 | 1996-10-02 | $7700.00 | Window Closed / Lapsed |