US4474915A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Modified vinyl acetate adhesive compositions containing low temperature fusion aids
Assignee: Ingredion Inc
•
Filing: 1983-05-27
•
Granted: 1984-10-02
•
Expires: 2003-05-27
Abstract
Abstract Modified vinyl acetate aqueous adhesive compositions containing acidic metal salt curing agents, which are suitable for exterior applications where water resistance is required, contain selected solvents as low temperature fusion aids. The adhesives are characterized by their film forming properties at temperatures as low as -1° C., increased closed assembly times of at least up to 40 minutes, improved storage stability, and their satisfactory cold and hot water resistance. They consist essentially of a mixture of (a) an aqueous emulsion of a stabilized vinyl acetate/N-methylol acrylamide polymer; (b) a metal salt curing agent; (c) optionally a cross-linking inhibitor; and (d) 1-7%, based on the polymer solids, of ethylene glycol monomethyl ether acetate, ethylene glycol diacetate, or tetrahydrofurfuryl alcohol as the fusion aid.
Inventors
- 👤 Ernest J. Grinacoff
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 18:42
CPC Classifications
C; C09; C09J; C09J131/00; C09J131/02; C09J131/04; C08; C08L; C08L2666/00; C08L2666/28; C08L2666/54; Y; Y10; Y10T; Y10T428/00; Y10T428/28; Y10T428/2852; Y10T428/2878; Y10T428/2887; Y10T428/31504; Y10T428/31855; Y10T428/3188; Y10T428/31895; Y10T428/31906; Y10T428/31935
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
218 words
A water-resistant vinyl acetate aqueous adhesive composition, characterized by its reduced low temperature fusion, which consists essentially of a mixture of: (a) an aqueous emulsion of a emulsion-stabilized vinyl acetate polymer of 80-99% vinyl acetate, 1-16% N-alkylol acrylamide or methacrylamide, and 0-19% of an ethylenically unsaturated monomer selected from the group consisting of acrylic acid, methacrylic acid, the alkyl esters of acrylic or methacrylic acid, α,β-unsaturated dicarboxylic acids, mono- or dialkyl esters of α,β-unsaturated dicarboxylic acids, vinyl halides, and vinylidene halides, and amides of α,β-unsaturated carboxylic acids, the percentages being by weight and totaling 100%; (b) a metal salt curing agent selected from the group consisting of chromic nitrate, chromic perchlorate, chromic chloride, aluminum nitrate, and aluminum chloride, which is present in a concentration of from about 0.003 to 0.12 gram equivalents per each 100 grams of the total weight of the adhesive composition; and (c) a cross-linking inhibitor selected from the group consisting of ammonia, alkyl amines, and alkylol amines, wherein the mole ratio of the cross-linking inhibitor to the curing agent ranges from 0-1.7; and (d) a low temperature fusion aid selected from the group consisting of ethylene glycol monomethyl ether acetate, ethylene glycol diacetate, and tetrahydrofurfuryl alcohol which is present in a concentration of from about 1 to 7% by weight of the polymer solids.
Claim 2
Dependent Claim
218 words
A water-resistant vinyl acetate aqueous adhesive composition, characterized by its reduced low temperature fusion, which consists essentially of a mixture of: (a) an aqueous emulsion of a emulsion-stabilized vinyl acetate polymer of 80-99% vinyl acetate, 1-16% N-alkylol acrylamide or methacrylamide, and 0-19% of an ethylenically unsaturated monomer selected from the group consisting of acrylic acid, methacrylic acid, the alkyl esters of acrylic or methacrylic acid, α,β-unsaturated dicarboxylic acids, mono- or dialkyl esters of α,β-unsaturated dicarboxylic acids, vinyl halides, and vinylidene halides, and amides of α,β-unsaturated carboxylic acids, the percentages being by weight and totaling 100%; (b) a metal salt curing agent selected from the group consisting of chromic nitrate, chromic perchlorate, chromic chloride, aluminum nitrate, and aluminum chloride, which is present in a concentration of from about 0.003 to 0.12 gram equivalents per each 100 grams of the total weight of the adhesive composition; and (c) a cross-linking inhibitor selected from the group consisting of ammonia, alkyl amines, and alkylol amines, wherein the mole ratio of the cross-linking inhibitor to the curing agent ranges from 0-1.7; and (d) a low temperature fusion aid selected from the group consisting of ethylene glycol monomethyl ether acetate, ethylene glycol diacetate, and tetrahydrofurfuryl alcohol which is present in a concentration of from about 1 to 7% by weight of the polymer solids.
Claim 3
Dependent Claim
60 words
The adhesive composition of claim 1, wherein the vinyl acetate polymer is a copolymer containing about 1-5% by weight of N-methylol acrylamide prepared by emulsion polymerization in the presence of a hydrophilic protective colloid as the stabilizer; wherein the curing agent is aluminum chloride; and wherein the fusion aid is present in a concentration of from about 2 to 6.5%.
Claim 4
Dependent Claim
25 words
The adhesive composition of claim 2, wherein the crosslinking inhibitor is ammonia, triethyl amine, triethanol amine, or N-methylethanol amine in a mole ratio of 0.1-0.7.
Claim 5
Dependent Claim
73 words
The adhesive composition of claim 3, wherein the vinyl acetate copolymer contains about 1-2% by weight of N-methylol acrylamide and is prepared by emulsion polymerization in the presence of 2-12% of polyvinyl alcohol based on the weight of the copolymer solids, the polyvinyl alcohol being from about 80-90% hydrolyzed and having a Hoeppler viscosity in the range of about 5-25 centipoises, as determined with a 4% by weight aqueous solution at 20° C.
Claim 6
Dependent Claim
28 words
The adhesive composition of claim 2, characterized by the low temperature fusion of -1° C. or less and a closed assembly time of at least about 40 minutes.
Claim 7
Dependent Claim
27 words
The adhesive composition of claim 3, characterized by the low temperature fusion of -1° C. or less and closed assembly time of at least about 40 minutes.
Claim 8
Dependent Claim
28 words
The adhesive composition of claim 4, characterized by the low temperature fusion of -4° C. or less and a closed assembly time of at least about 40 minutes.
Claim 9
Dependent Claim
22 words
The adhesive composition of claim 5, wherein the low temperature fusion aid is ethylene glycol monomethyl ether acetate or ethylene glycol diacetate.
Claim 10
Dependent Claim
22 words
The adhesive composition of claim 6, wherein the low temperature fusion aid is ethylene glycol monomethyl ether acetate or ethylene glycol diacetate.
Claim 11
Dependent Claim
29 words
The adhesive composition of claim 7, wherein the low temperature fusion aid is ethylene glycol monomethyl ether acetate or ethylene glycol diacetate present in an amount of about 2-5%.
Claim 12
Dependent Claim
15 words
The adhesive composition of claim 5, wherein the low temperature fusion aid is tetrahydrofurfuryl alcohol.
Claim 13
Dependent Claim
15 words
The adhesive composition of claim 6, wherein the low temperature fusion aid is tetrahydrofurfuryl alcohol.
Claim 14
Dependent Claim
22 words
The adhesive composition of claim 7, wherein the low temperature fusion aid is tetrahydrofurfuryl alcohol present in an amount of about 5-7%.
References Cited (Backward Citations)
US2595956A
Cited
US3041301A
Cited
US3301809A
Cited
US3563851A
Cited
US3580876A
Cited
US3746679A
Cited
US3730933A
Cited
US4085074A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-02 | 1988-04-02 | 1988-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-02 | 1992-04-02 | 1992-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-02 | 1996-04-02 | 1996-10-02 | $7700.00 | Window Closed / Lapsed |