Oil well casing and tubing joint and production of same
Assignee: Nippon Steel Corp
•
Filing: 1982-08-13
•
Granted: 1984-10-02
•
Expires: 2002-08-13
Abstract
Abstract A joint for used in connecting oil well casing and/or tubing and method of producing same are disclosed. The joint with improved metal-to-metal sealing properties as well as improved resistance to galling is made of an alloy steel containing 10% or more by weight of Cr and comprises a metal sealing portion and a threaded portion provided with an activating layer of a metal or an alloy selected iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, and an electrodeposited layer of a metal or an alloy selected from iron, copper, zinc, chromium, nickel, and alloys thereof.
Inventors
- 👤 Akihiro Yauchi
- 👤 Minoru Nishihara
- 👤 Kunihiro Fukui
- 👤 Hisakazu Kawashima
- 👤 Yoshiyasu Morita
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:04
CPC Classifications
F; F16; F16L; F16L15/00; F16L15/001; F16L15/004; C; C25; C25D; C25D5/00; C25D5/10; C25D5/34; C25D5/36; C25D7/00; C25D7/04; E; E21; E21B; E21B17/00; E21B17/02; E21B17/04; E21B17/042; F16L58/00; F16L58/18; F16L58/182
Claims Analysis
Total Claims: 25
Claim 1
Independent Claim
158 words
A joint with improved metal-to-metal sealing properties for use in connecting oil well casing and/or tubing, which comprises a metal sealing portion and a threaded portion and which is made of an alloy steel containing 10% or more by weight of chromium, characterized in that at least part of the surface of said metal sealing portion has been provided with an activating layer of a metal or an alloy selected from the group consisting of iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, and an electrodeposited layer of a metal or an alloy selected from the group consisting of iron, copper, zinc, chromium, nickel and alloys thereof, said activating layer being firmly adhered to the steel surface by subjecting said surface to anodic electrolysis in an acidic aqueous solution containing halide ions and then immediately thereafter to cathodic electrolysis, the amount of said electrodeposited layer provided on said activating layer being 2 g/m 2 or more.
Claim 2
Dependent Claim
158 words
A joint with improved metal-to-metal sealing properties for use in connecting oil well casing and/or tubing, which comprises a metal sealing portion and a threaded portion and which is made of an alloy steel containing 10% or more by weight of chromium, characterized in that at least part of the surface of said metal sealing portion has been provided with an activating layer of a metal or an alloy selected from the group consisting of iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, and an electrodeposited layer of a metal or an alloy selected from the group consisting of iron, copper, zinc, chromium, nickel and alloys thereof, said activating layer being firmly adhered to the steel surface by subjecting said surface to anodic electrolysis in an acidic aqueous solution containing halide ions and then immediately thereafter to cathodic electrolysis, the amount of said electrodeposited layer provided on said activating layer being 2 g/m 2 or more.
Claim 3
Dependent Claim
56 words
A joint for use in connecting oil well casing and/or tubing, as defined in claim 1, in which said activating layer and said electrodeposited layer are provided on at least part of said surface of said metal sealing portion as well as on at least part of the surface of said threaded portion of said joint.
Claim 4
Dependent Claim
32 words
A joint for use in connecting oil well casing and/or tubing, as defined in claim 1 or 2, in which said alloy steel contains not less than 20% by weight of Cr.
Claim 5
Dependent Claim
26 words
A joint for use in connecting oil well casing and/or tubing, as defined in claim 1 or 2, in which said halide ions are chloride ions.
Claim 6
Dependent Claim
32 words
A joint for used in connecting oil well casing and/or tubing, as defined in claim 1 or 2, in which the amount of said electrodeposited layer is 20 g/m 2 or more.
Claim 7
Independent Claim
135 words
A method of producing a joint with improved metal-to-metal sealing properties for use in connecting oil well casing and/or tubing, which comprises preparing a joint made of an alloy steel containing 10% or more by weight of chromium, said joint comprising a threaded portion and a metal sealing portion, subjecting at least part of said metal sealing portion to anodic electrolysis in an acidic aqueous solution containing halide ions, then immediately thereafter switching the anodic electrolysis to cathodic electrolysis in the same aqueous solution to provide an activating layer of a metal or an alloy selected from the group consisting of iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, and carrying out electrodeposition of a metal or an alloy selected from the group consisting of iron, copper, zinc, chromium, nickel and alloys thereof.
Claim 8
Independent Claim
135 words
A method of producing a joint with improved metal-to-metal sealing properties for use in connecting oil well casing and/or tubing, which comprises preparing a joint made of an alloy steel containing 10% or more by weight of chromium, said joint comprising a threaded portion and a metal sealing portion, subjecting at least part of said metal sealing portion to anodic electrolysis in an acidic aqueous solution containing halide ions, then immediately thereafter switching the anodic electrolysis to cathodic electrolysis in the same aqueous solution to provide an activating layer of a metal or an alloy selected from the group consisting of iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, and carrying out electrodeposition of a metal or an alloy selected from the group consisting of iron, copper, zinc, chromium, nickel and alloys thereof.
Claim 9
Dependent Claim
26 words
A method as defined in claim 6, in which said halide ions are chloride ions in an amount of 1 g/1 or more calculated as chloride.
Claim 10
Dependent Claim
34 words
A method as defined in claim 7, in which the alloy steel contains 20% or more of Cr and the chloride ions are in an amount of 30 g/1 or more calculated as chloride.
Claim 11
Dependent Claim
58 words
A method as defined in claim 6, in which said anodic electrolysis is carried out at a current density of 1 A/dm 2 or higher for a period of 10 seconds or longer, and said cathodic electrolysis is carried out at a current density of 1 A/dm 2 or higher for a period of 10 seconds or longer.
Claim 12
Dependent Claim
34 words
A method as defined in claim 9, in which said anodic electrolysis is carried out for a period of 2-5 minutes and said cathodic electrolysis is carried out for a period of 2-6 minutes.
Claim 13
Dependent Claim
26 words
A method as defined in claim 6, in which the amount of the electrodeposited layer placed over the activating layer is 2 g/m 2 or more.
Claim 14
Dependent Claim
21 words
A method as defined in claim 11, in which the amount of the electrodeposited layer is 20 g/m 2 or more.
Claim 15
Independent Claim
27 words
A method as defined in any one of claims 6-12, in which the electrodeposition onto said activating layer is carried out using a separate electroplating acidic bath.
Claim 16
Dependent Claim
132 words
A process for improving metal-to-metal sealing properties of a joint for use in connecting casing and/or tubing, said joint being prepared from an alloy steel containing 10% or more by weight of chromium and said joint comprising a metal sealing portion and a threaded portion, which comprises subjecting at least part of said metal sealing portion to anodic electrolysis in an acidic aqueous solution containing halide ions, then immediately thereafter switching the anodic electrolysis to cathodic electrolysis in the same aqueous solution to provide an activating layer of a metal or an alloy selected from the group consisting of iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, followed by electrodeposition of a metal or an alloy selected from the group consisting of iron, copper, zinc, chromium, nickel and alloys thereof.
Claim 17
Dependent Claim
132 words
A process for improving metal-to-metal sealing properties of a joint for use in connecting casing and/or tubing, said joint being prepared from an alloy steel containing 10% or more by weight of chromium and said joint comprising a metal sealing portion and a threaded portion, which comprises subjecting at least part of said metal sealing portion to anodic electrolysis in an acidic aqueous solution containing halide ions, then immediately thereafter switching the anodic electrolysis to cathodic electrolysis in the same aqueous solution to provide an activating layer of a metal or an alloy selected from the group consisting of iron, nickel, zinc, cobalt, copper, manganese, chromium and alloys thereof, followed by electrodeposition of a metal or an alloy selected from the group consisting of iron, copper, zinc, chromium, nickel and alloys thereof.
Claim 18
Dependent Claim
38 words
A process as defined in claim 14, in which at least part of the surface of said threaded portion of said joint is subjected to the same treatment as said at least part of said metal sealing portion.
Claim 19
Dependent Claim
21 words
A process as defined in claim 14 in which said alloy steel contains not less than 20% by weight of Cr.
Claim 20
Dependent Claim
26 words
A process as defined in claim 14 in which said halide ions are chloride ions in an amount of 1 g/1 or more calculated as chloride.
Claim 21
Dependent Claim
58 words
A process as defined in claim 14, in which said anodic electrolysis is carried out at a current density of 1 A/dm 2 or higher for a period of 10 seconds or longer, and said cathodic electrolysis is carried out at a current density of 1 A/dm 2 or higher for a period of 10 seconds or longer.
Claim 22
Dependent Claim
34 words
A process as defined in claim 18, in which said anodic electrolysis is carried out for a period of 2.5 minutes and said cathodic electrolysis is carried out for a period of 2-6 minutes.
Claim 23
Dependent Claim
26 words
A process as defined in claim 14, in which the amount of the electrodeposited layer placed over the activating layer is 2 g/m 2 or more.
Claim 24
Dependent Claim
21 words
A process as defined in claim 20, in which the amount of the electrodeposited layer is 20 g/m 2 or more.
Claim 25
Dependent Claim
24 words
A process as defined in claim 14, in which the electrodeposition onto said activating layer is carried out using a separate electroplating acidic bath.
References Cited (Backward Citations)
US1954473A
Cited
US2528717A
Cited
US2780019A
Cited
US2965551A
Cited
US2898490A
Cited
US3338803A
Cited
US3669851A
Cited
US4039399A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-10-02 | 1988-04-02 | 1988-10-02 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-10-02 | 1992-04-02 | 1992-10-02 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-10-02 | 1996-04-02 | 1996-10-02 | $7700.00 | Window Closed / Lapsed |