Molded articles comprising fiber reinforced styrene polymers
Assignee: Monsanto Co
•
Filing: 1983-12-21
•
Granted: 1984-09-25
•
Expires: 2003-12-21
Abstract
Abstract Molded articles comprising glass fiber reinforced styrene polymer wherein the weight ratio of glass fiber to styrene polymer is in the range of about 55:45 to about 75:25. The molded articles are prepared by a transfer molding process in which glass fiber mat containing 1 to 5 weight percent of an unsaturated polyester binder is impregnated with styrene monomer and the mold is subjected to conditions which induce fast polymerization of the styrene monomer. The molded articles possess resistance to heat distortion.
Inventors
- 👤 Leo E. Rademacher
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 05:31
CPC Classifications
C; C08; C08J; C08J5/00; C08J5/04; C08J5/0405; C08J5/043; B; B29; B29C; B29C70/00; B29C70/04; B29C70/28; B29C70/40; B29C70/42; B29C70/46; B29C70/48; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/14; C08J2325/00; C08J2325/02; C08J2325/04; Y; Y10; Y10T; Y10T442/00; Y10T442/20; Y10T442/2631; Y10T442/2721
Claims Analysis
Total Claims: 5
Claim 1
Independent Claim
106 words
A molded article comprising a glass fiber-reinforced styrene homopolymer or styrene acrylonitrile copolymers consisting of up to 50 weight percent of acrylonitrile, wherein the weight ratio of the glass fiber reinforcement to the styrene polymer is in the range of about 55:45 to about 75:25, and wherein the fiber reinforcement is a mat or weave of long glass fibers of at least about 25 mm in length and of diameter in the range of about 5 to about 25 microns containing from about 1 to about 5 weight percent of an unsaturated polyester binder of molecular weight in the range of about 1000 to about 10000.
Claim 2
Dependent Claim
106 words
A molded article comprising a glass fiber-reinforced styrene homopolymer or styrene acrylonitrile copolymers consisting of up to 50 weight percent of acrylonitrile, wherein the weight ratio of the glass fiber reinforcement to the styrene polymer is in the range of about 55:45 to about 75:25, and wherein the fiber reinforcement is a mat or weave of long glass fibers of at least about 25 mm in length and of diameter in the range of about 5 to about 25 microns containing from about 1 to about 5 weight percent of an unsaturated polyester binder of molecular weight in the range of about 1000 to about 10000.
Claim 3
Dependent Claim
24 words
The molded article of claim 1 wherein the heat distortion temperature determined under a load of 264 psi (1819 kPa) is above 200° C.
Claim 4
Dependent Claim
194 words
A process of preparing a molded article of a glass fiber reinforced styrene polymer of heat distortion temperature above 200° C. determined under a load of 264 psi (1819 kPa), wherein the weight ratio of the glass fiber reinforcement to the styrene polymer is in the range of about 55:45 to about 75:25, said process comprising: A. fitting a weave or mat of glass fibers of length at least about 25 mm and a diameter in the range of about 5 to about 25 microns containing from about 1 to about 5 weight percent of an unsaturated polyester binder of molecular weight in the range of about 1000 to about 10000 into the cavity of a transfer mold; B. closing and clamping the mold; C. filling the free space in the mold with styrene or a styrene acrylonitrile solution containing up to 50 weight percent acrylonitrile, said styrene or styrene acrylonitrile solution containing a free radical initiator; D. heating the mold to a temperature which allows polymerization of the monomers initiated by the free radical initiator to proceed to about a 98 percent conversion; and E. opening the mold and removing the molded article.
Claim 5
Dependent Claim
194 words
A process of preparing a molded article of a glass fiber reinforced styrene polymer of heat distortion temperature above 200° C. determined under a load of 264 psi (1819 kPa), wherein the weight ratio of the glass fiber reinforcement to the styrene polymer is in the range of about 55:45 to about 75:25, said process comprising: A. fitting a weave or mat of glass fibers of length at least about 25 mm and a diameter in the range of about 5 to about 25 microns containing from about 1 to about 5 weight percent of an unsaturated polyester binder of molecular weight in the range of about 1000 to about 10000 into the cavity of a transfer mold; B. closing and clamping the mold; C. filling the free space in the mold with styrene or a styrene acrylonitrile solution containing up to 50 weight percent acrylonitrile, said styrene or styrene acrylonitrile solution containing a free radical initiator; D. heating the mold to a temperature which allows polymerization of the monomers initiated by the free radical initiator to proceed to about a 98 percent conversion; and E. opening the mold and removing the molded article.
References Cited (Backward Citations)
US3022210A
Cited
US3635879A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-25 | 1988-03-26 | 1988-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-25 | 1992-03-26 | 1992-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-25 | 1996-03-26 | 1996-09-25 | $7700.00 | Window Closed / Lapsed |