Annealing steel strip using molten B2 O3, SiO2 Na2 O, NaF glass bath
Assignee: Nippon Steel Nisshin Co Ltd
•
Filing: 1983-02-04
•
Granted: 1984-09-25
•
Expires: 2003-02-04
Abstract
Abstract A process for annealing steel strip comprising dipping the strip in a molten glass bath maintained 950° C. or higher to anneal it, taking the strip out of the bath to form coagulated glass coatings on the surfaces of the strip and cooling the strip to destroy and peel off the coatings. The bath comprises 38.0 to 62.0% of B 2 O 3 , 18.0 to 32.0% of SiO 2 , 18.0 to 32.0% of Na 2 O partly replaceable with K 2 O, up to 10.0% of CaO partly replaceable with MgO, BaO, ZnO and/or SrO, up to 6.0% of Li 2 O, up to 10.0% of Al 2 O 3 and 0.5 to 4.0% of NaF, and has a viscosity not exceeding 200 poises as measured at 950° C. The strip is preferably not exposed to air while above 400° C.
Inventors
- 👤 Shigeaki Maruhashi
- 👤 Takayoshi Kanamaru
- 👤 Hiroto Matsumoto
- 👤 Kousuke Sawashige
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:21
CPC Classifications
C; C21; C21D; C21D1/00; C21D1/34; C21D1/44; C21D1/46; C21D1/68; C21D1/70
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
179 words
A process for annealing steel strip comprising the steps of dipping the steel strip in a molten glass bath maintained at a temperature of at least 950° C. to anneal it, said bath consisting essentially in % by weight 38.0 to 62.0% of B 2 O 3 , 18.0 to 32.0% of SiO 2 , 8.0 to 32.0% of Na 2 O, 0 to 20.0% of K 2 O with the sum of the Na 2 O and K 2 O being 8.0 to 32.0%, 0 to 10.0% of CaO which may be partly replaced with at least one of MgO, BaO, ZnO and SrO, 0 to 6.0% of Li 2 O, 0 to 10.0% of Al 2 O 3 and 0.5 to 4.0% of NaF, and having a viscosity not exceeding 200 poises as measured at a temperature of 950° C., taking the strip out of the bath to form coagulated glass coatings on the surfaces of the strip, and cooling the strip to destroy and peel off the coagulated glass coatings from the surfaces of the strip.
Claim 2
Dependent Claim
179 words
A process for annealing steel strip comprising the steps of dipping the steel strip in a molten glass bath maintained at a temperature of at least 950° C. to anneal it, said bath consisting essentially in % by weight 38.0 to 62.0% of B 2 O 3 , 18.0 to 32.0% of SiO 2 , 8.0 to 32.0% of Na 2 O, 0 to 20.0% of K 2 O with the sum of the Na 2 O and K 2 O being 8.0 to 32.0%, 0 to 10.0% of CaO which may be partly replaced with at least one of MgO, BaO, ZnO and SrO, 0 to 6.0% of Li 2 O, 0 to 10.0% of Al 2 O 3 and 0.5 to 4.0% of NaF, and having a viscosity not exceeding 200 poises as measured at a temperature of 950° C., taking the strip out of the bath to form coagulated glass coatings on the surfaces of the strip, and cooling the strip to destroy and peel off the coagulated glass coatings from the surfaces of the strip.
Claim 3
Dependent Claim
121 words
A process in accordance with claim 1 wherein said molten glass bath consisting essentially in % by weight 40.0 to 60.0% of B 2 O 3 , 20.0 to 30.0% of SiO 2 , 10.0 to 30.0% of Na 2 O, 0 to 20.0% of K 2 O with the sum of the Na 2 O and K 2 O being 10.0 to 30.0%, 1.0 to 7.0% of CaO which may be partly replaced with at least one of MgO, BaO, ZnO and SrO, 1.0 to 5.0% of Li 2 O, 3.0 to 8.0% of Al 2 O 3 and 1.0 to 3.0% of NaF, and has a viscosity not exceeding 100 poises as measured at a temperature of 950° C.
Claim 4
Dependent Claim
17 words
A process in accordance with claim 1 or claim 2 wherein the process is carried out continuously.
Claim 5
Dependent Claim
23 words
A process in accordance with any one of the preceding claims wherein the steel strip is a cold rolled strip of stainless steel.
Claim 6
Dependent Claim
207 words
A process for annealing steel strip, comprising the step of dipping the steel strip in a molten glass bath maintained at a temperature of at least 950° C. to anneal it, said bath consisting essentially in % by weight 38.0 to 62.0% of B 2 O 3 , 18.0 to 32.0% of SiO 2 , 8.0 to 32.0% of Na 2 O, 0 to 20.0% of K 2 O with the sum of the Na 2 O and K 2 O being 8.0 to 32.0%, 0 to 10.0% of CaO which may be partly replaced with at least one of MgO, BaO, ZnO and SrO, 0 to 6.0% of Li 2 O, 0 to 10.0% of Al 2 O 3 and 0.5 to 4.0% of NaF, and having a viscosity not exceeding 200 poises as measured at a temperature of 950° C., taking the strip out of the bath to form coagulated glass coatings on the surfaces of the strip, and cooling the strip to destroy and peel off the coagulated glass coatings from the surfaces of the strip, the cooling conditions being controlled so that the surfaces of the strip are not exposed to air when the temperature of the strip is still above 400° C.
Claim 7
Dependent Claim
207 words
A process for annealing steel strip, comprising the step of dipping the steel strip in a molten glass bath maintained at a temperature of at least 950° C. to anneal it, said bath consisting essentially in % by weight 38.0 to 62.0% of B 2 O 3 , 18.0 to 32.0% of SiO 2 , 8.0 to 32.0% of Na 2 O, 0 to 20.0% of K 2 O with the sum of the Na 2 O and K 2 O being 8.0 to 32.0%, 0 to 10.0% of CaO which may be partly replaced with at least one of MgO, BaO, ZnO and SrO, 0 to 6.0% of Li 2 O, 0 to 10.0% of Al 2 O 3 and 0.5 to 4.0% of NaF, and having a viscosity not exceeding 200 poises as measured at a temperature of 950° C., taking the strip out of the bath to form coagulated glass coatings on the surfaces of the strip, and cooling the strip to destroy and peel off the coagulated glass coatings from the surfaces of the strip, the cooling conditions being controlled so that the surfaces of the strip are not exposed to air when the temperature of the strip is still above 400° C.
Claim 8
Dependent Claim
121 words
A process in accordance with claim 1 wherein said molten glass bath consisting essentially in % by weight 40.0% to 60.0% of B 2 O 3 , 20.0 to 30.0% of SiO 2 , 10.0 to 30.0% of Na 2 O, 0 to 20.0% of K 2 O with the sum of the Na 2 O and K 2 O being 10.0 to 30.0% 1.0 to 7.0% of CaO which may be partly replaced with at least one of MgO, BaO, ZnO and SrO, 1.0 to 5.0% of Li 2 O, 3.0 to 8.0% of Al 2 O 3 and 1.0 to 3.0% of Naf, and has a viscosity not exceeding 100 poises as measured at a temperature of 950° C.
Claim 9
Dependent Claim
40 words
A process in accordance with claim 5 or claim 6 wherein the strip taken out of the bath is cooled with an inert gas to destroy and peel off the coagulated glass coatings are from the surfaces of the strip.
Claim 10
Dependent Claim
13 words
A process in accordance with claim 7 wherein said inert gas is argon.
Claim 11
Dependent Claim
68 words
A process in accordance with claim 5 or claim 6 wherein the strip taken out of the bath is initially allowed to cool without the destruction of the coagulated glass coatings, and after the temperature of the strip has fallen to 400° C. a temperature not higher than the strip is forcibly cooled to destroy and peel off the coagulated glass coatings from the surfaces of the strip.
Claim 12
Dependent Claim
29 words
A process in accordance with claim 9 wherein after the temperature of the strip has fallen to a temperature not more than 300° C. the strip is forcibly cooled.
Claim 13
Dependent Claim
19 words
A process in accordance with any one of claims 5 through 10 wherein the process is continuously carried out.
Claim 14
Dependent Claim
24 words
A process in accordance with any one of claims 5 through 11 wherein the steel strip is a cold rolled strip of stainless steel.
References Cited (Backward Citations)
US1919136A
Cited
US2328933A
Cited
US2328932A
Cited
US2337186A
Cited
US3158515A
Cited
US4358544A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-25 | 1988-03-26 | 1988-09-25 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-25 | 1992-03-26 | 1992-09-25 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-25 | 1996-03-26 | 1996-09-25 | $7700.00 | Window Closed / Lapsed |