Elastic fluorohydrocarbon resin and method of producing same
Assignee: Central Glass Co Ltd
•
Filing: 1983-05-19
•
Granted: 1984-09-18
•
Expires: 2003-05-19
Abstract
Abstract A fluorohydrocarbon resin that has elasticity and retains favorable properties of known fluorohydrocarbon polymers is obtained by graft copolymerization of a fluorine-containing elastomeric polymer with a fluorine-containing crystalline polymer. One of the elastomeric and crystalline polymers is prepared by copolymerizing at least one fluorine-containing monomer with at least one unsaturated monomer that has peroxy bond. When the elastomeric polymer is employed as the basic polymer and the crystalline polymer is polyvinylidene fluoride, the graft copolymerized fluorohydrocarbon resin is high in mutual solubility with polyvinylidene fluoride, so that the addition of this resin to polyvinylidene fluoride gives a resin composition which has elasticity and good low temperature characteristics.
Inventors
- 👤 Chikashi Kawashima
- 👤 Takashi Yasumura
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 08:24
CPC Classifications
C; C08; C08F; C08F293/00; C08F259/00; C08F259/08
Claims Analysis
Total Claims: 26
Claim 1
Independent Claim
103 words
An elastic fluorohydrocarbon resin which consists essentially of a copolymer comprising a first segment which is a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and a second segment which is a fluorine-containing crystalline polymer not lower than 130° C. in melting temperature, one of said first and second segments having at least one peroxy bond capable of decomposition during graft copolymerization and the other of said segments being capable of undergoing graft copolymerization with said segment having at least one peroxy bond, said other segment being at least partly grafted to said segment having at least one peroxy bond.
Claim 2
Dependent Claim
103 words
An elastic fluorohydrocarbon resin which consists essentially of a copolymer comprising a first segment which is a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and a second segment which is a fluorine-containing crystalline polymer not lower than 130° C. in melting temperature, one of said first and second segments having at least one peroxy bond capable of decomposition during graft copolymerization and the other of said segments being capable of undergoing graft copolymerization with said segment having at least one peroxy bond, said other segment being at least partly grafted to said segment having at least one peroxy bond.
Claim 3
Dependent Claim
69 words
A resin composition comprising 100 parts by weight of polyvinylidene fluoride and 1 to 100 parts by weight of an elastic fluorohydrocarbon resin, said elastic fluorohydrocarbon resin consisting essentially of a copolymer comprising a first segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and a second segment which comprises polyvinylidene fluoride and which is at least partly grafted to said first segment.
Claim 4
Dependent Claim
69 words
A resin composition comprising 100 parts by weight of polyvinylidene fluoride and 1 to 100 parts by weight of an elastic fluorohydrocarbon resin, said elastic fluorohydrocarbon resin consisting essentially of a copolymer comprising a first segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and a second segment which comprises polyvinylidene fluoride and which is at least partly grafted to said first segment.
Claim 5
Dependent Claim
72 words
A resin composition according to claim 2, wherein said elastomeric polymer is produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and a combination of other monomers selected from the group consisting of a combination of vinylidene fluoride and hexafluoropropene, a combination of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, a combination of vinylidene fluoride and chlorotrifluoroethylene, a combination of tetrafluoroethylene and propylene, and a combination of tetrafluoroethylene and a fluorine-substituted vinyl ether.
Claim 6
Dependent Claim
32 words
A resin composition according to claim 3, wherein the weight ratio of said second segment to said first segment in said elastic fluorocarbon resin is in the range from 1:100 to 100:100.
Claim 7
Dependent Claim
86 words
An elastic fluorohydrocarbon according to claim 1, wherein said copolymer comprises: (a) a first segment which comprises a fluorine-containing lastomeric polymer having a glass transition temperature below room temperature and at least one peroxy bond capable of decomposition during graft copolymerization, and (b) a second segment which comprises a fluorine-containing crystalline polymer which has a melting temperature not lower than 130° C. and which is capable of undergoing graft copolymerization with said elastomeric polymer, said second segment being at least partly grafted to said first segment.
Claim 8
Dependent Claim
71 words
A fluorohydrocarbon resin according to claim 5, wherein said elastomeric polymer is produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and a combination of other monomers selected from the group consisting a combination of vinylidene fluoride and hexafluoropropene, a combination of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, a combination of vinylidene fluoride and chlorotrifluoroethylene, a combination of tetrafluoroethylene and propylene, and a combination of tetrafluoroethylene and a fluorine-substituted vinyl ether.
Claim 9
Dependent Claim
42 words
A fluorohydrocarbon resin according to claim 6, wherein said crystalline polymer is selected from the group consisting of polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride, polyvinyl fluoride, copolymers of tetrafluoroethylene and ethylene, copolymers of chlorotrifluoroethylene and ethylene, and copolymers of tetrafluoroethylene and fluorine-substituted vinyl ether.
Claim 10
Dependent Claim
88 words
An elastic fluorohydrocarbon resin according to claim 1, wherein said copolymer comprises: (a) a first segment which comprises a fluorine-containing crystalline polymer which has a melting temperature not lower than 130° C. and has at least one peroxy bond capable of decomposition during grafted copolymerization; and (b) a second segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and which is capable of undergoing grafted copolymerization with said crystalline polymer, said second segment being at least partly grafted to said first segment.
Claim 11
Dependent Claim
40 words
A fluorohydrocarbon resin according to claim 8, wherein said crystalline polymer is a copolymer produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and another monomer selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, vinylidene fluoride, vinylfluoride, and ethylene.
Claim 12
Dependent Claim
51 words
A fluorhydrocarbon resin according to claim 9, wherein said elastomeric polymer is selected from the group consisting of copolymers of vinylidene fluoride and hexafluoropropene, copolymers of vinylidene fluoride, hexafluoropropene, and tetrafluoroethylene, copolymers of vinylidene fluoride and chlorotrifluoroethylene, copolymers of tetrafluoroethylene and propylene, and copolymers of tetrafluoroethylene and a fluorine-substituted vinyl ether.
Claim 13
Dependent Claim
159 words
An elastic fluorohydrocarbon resin which consists essentially of a copolymer comprising: (a) a first segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and being selected from the group consisting of copolymers produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and a combination of other monomers selected from the group consisting of a combination of vinylidene fluoride and hexafluoropropene, a combination of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, a combination of vinylidene fluoride and chlorotrifluoroethylene, a combination of tetrafluoroethylene and propylene, and a combination of tetrafluorethylene and fluorine-substituted vinyl ether; and (b) a second segment comprising a fluorine-containing crystalline polymer having a melting temperature lower than 130° C. and being selected from the group consisting of polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride, polyvinyl fluoride, copolymers of tetrafluoroethylene and ethylene, copolymers of chlorotrifluoroethylene and ethylene, and copolymers of tetrafluoroethylene and fluorine-substituted vinyl ether, said second segment being at least partly grafted to said first segment.
Claim 14
Dependent Claim
159 words
An elastic fluorohydrocarbon resin which consists essentially of a copolymer comprising: (a) a first segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and being selected from the group consisting of copolymers produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and a combination of other monomers selected from the group consisting of a combination of vinylidene fluoride and hexafluoropropene, a combination of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, a combination of vinylidene fluoride and chlorotrifluoroethylene, a combination of tetrafluoroethylene and propylene, and a combination of tetrafluorethylene and fluorine-substituted vinyl ether; and (b) a second segment comprising a fluorine-containing crystalline polymer having a melting temperature lower than 130° C. and being selected from the group consisting of polytetrafluoroethylene, polychlorotrifluoroethylene, polyvinylidene fluoride, polyvinyl fluoride, copolymers of tetrafluoroethylene and ethylene, copolymers of chlorotrifluoroethylene and ethylene, and copolymers of tetrafluoroethylene and fluorine-substituted vinyl ether, said second segment being at least partly grafted to said first segment.
Claim 15
Dependent Claim
132 words
An elastic fluorohydrocarbon resin which consists essentially of a copolymer comprising: (a) a first segment which comprises a fluorine-containing crystalline polymer having a melting temperature not lower than 130° C. and being a copolymer produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and monomers selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride, and ethylene; and (b) a second segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and being selected from the group consisting of copolymers of vinylidene fluoride and hexafluoropropene, copolymers of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, copolymers of vinylidene fluoride and chlorotrifluoroethylene, copolymers of tetrafluoroethylene and propylene, and copolymers of tetrafluoroethylene and a fluorine-substituted vinyl ether, said second segment being at least partly grafted to said first segment.
Claim 16
Dependent Claim
132 words
An elastic fluorohydrocarbon resin which consists essentially of a copolymer comprising: (a) a first segment which comprises a fluorine-containing crystalline polymer having a melting temperature not lower than 130° C. and being a copolymer produced by copolymerizing a mixture comprising an unsaturated peroxy monomer and monomers selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride, and ethylene; and (b) a second segment which comprises a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and being selected from the group consisting of copolymers of vinylidene fluoride and hexafluoropropene, copolymers of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, copolymers of vinylidene fluoride and chlorotrifluoroethylene, copolymers of tetrafluoroethylene and propylene, and copolymers of tetrafluoroethylene and a fluorine-substituted vinyl ether, said second segment being at least partly grafted to said first segment.
Claim 17
Independent Claim
195 words
A method of producing an elastic fluorohydrocarbon resin, comprising the steps of: (a) copolymerizing at least one first fluorine-containing monomer with at least one second monomer having (i) at least one double bond and (ii) at least one peroxy bond having a decomposition temperature higher than the reaction temperature of said copolymerizing to produce a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and a peroxy bond capable of decomposition during graft copolymerization, the weight ratio of said second monomer to said first fluorine-containing monomer being in the range from about 0.05:100 to 20:100; (b) providing a dispersion of said fluorine-containing elastomeric polymer in a liquid medium, said dispersion being substantially free of unreacted said first monomer and said second monomer; (c) introducing into said dispersion at least one third monomer which comprises at least one fluorine-containing monomer and which is capable of providing a crystalline polymer having a melting temperature not lower than 130° C.; and (d) polymerizing said third monomer in said dispersion so as to cause decomposition of said peroxy bond, thereby causing at least a portion of said third monomer to undergo graft copolymerization with said elastomeric polymer.
Claim 18
Independent Claim
195 words
A method of producing an elastic fluorohydrocarbon resin, comprising the steps of: (a) copolymerizing at least one first fluorine-containing monomer with at least one second monomer having (i) at least one double bond and (ii) at least one peroxy bond having a decomposition temperature higher than the reaction temperature of said copolymerizing to produce a fluorine-containing elastomeric polymer having a glass transition temperature below room temperature and a peroxy bond capable of decomposition during graft copolymerization, the weight ratio of said second monomer to said first fluorine-containing monomer being in the range from about 0.05:100 to 20:100; (b) providing a dispersion of said fluorine-containing elastomeric polymer in a liquid medium, said dispersion being substantially free of unreacted said first monomer and said second monomer; (c) introducing into said dispersion at least one third monomer which comprises at least one fluorine-containing monomer and which is capable of providing a crystalline polymer having a melting temperature not lower than 130° C.; and (d) polymerizing said third monomer in said dispersion so as to cause decomposition of said peroxy bond, thereby causing at least a portion of said third monomer to undergo graft copolymerization with said elastomeric polymer.
Claim 19
Independent Claim
194 words
A method of producing an elastic fluorohydrocarbon resin, comprising the steps of: (a) copolymerizing at least one first fluorine-containing monomer with at least one second monomer having (i) at least one double bond and (ii) at least one peroxy bond having a decomposition temperature higher than the reaction temperature of said copolymerizing to produce a fluorine-containing crystalline polymer having a melting temperature not lower than 130° C. and a peroxy bond capable of decomposition during grafted copolymerization, the weight ratio of said second monomer to said first fluorine-containing monomer being in the range of 0.05:100 to 20:100; (b) providing a dispersion of said fluorine-containing crystalline polymer in a liquid medium, said dispersion being substantially free of unreacted said first monomer and said second monomer; (c) introducing into said dispersion at least one third monomer which comprises at least one fluorine-containing monomer and which is capable of providing an elastomeric polymer having a glass transition temperature below room temperature; and (d) polymerizing said third monomer in said dispersion so as to cause decomposition of said peroxy bond, thereby causing at least a portion of said third monomer to undergo graft copolymerization with said crystalline polymer.
Claim 20
Independent Claim
194 words
A method of producing an elastic fluorohydrocarbon resin, comprising the steps of: (a) copolymerizing at least one first fluorine-containing monomer with at least one second monomer having (i) at least one double bond and (ii) at least one peroxy bond having a decomposition temperature higher than the reaction temperature of said copolymerizing to produce a fluorine-containing crystalline polymer having a melting temperature not lower than 130° C. and a peroxy bond capable of decomposition during grafted copolymerization, the weight ratio of said second monomer to said first fluorine-containing monomer being in the range of 0.05:100 to 20:100; (b) providing a dispersion of said fluorine-containing crystalline polymer in a liquid medium, said dispersion being substantially free of unreacted said first monomer and said second monomer; (c) introducing into said dispersion at least one third monomer which comprises at least one fluorine-containing monomer and which is capable of providing an elastomeric polymer having a glass transition temperature below room temperature; and (d) polymerizing said third monomer in said dispersion so as to cause decomposition of said peroxy bond, thereby causing at least a portion of said third monomer to undergo graft copolymerization with said crystalline polymer.
Claim 21
Dependent Claim
58 words
A method according to claim 13, wherein said first fluorine-containing monomer comprises a combination selected from the group consisting of a combination of vinylidene fluoride and hexafluoropropene, a combination of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, a combination of vinylidene fluoride and chlorotrifluoroethylene, a combination of tetrafluoroethyulene and proplylene, and a combination of tetrafluoroethylene and a fluorine-substituted vinyl ether.
Claim 22
Dependent Claim
38 words
A method according to claim 15, wherein said second monomer is selected from the group consisting of t-butyl peroxymethacrylate, di(t-butyl peroxy)fumarate, t-butyl peroxycrotonate, t-butyl peroxyallylcarbonate, t-hexyl peroxyallylcarbonate, 1,1,3,3-tetramethylbutyl peroxyallylcarbonate, t-butyl peroxymethallylcarbonate, 1,1,3,3-tetramethylbutyl peroxymethallylcarbonate, p-menthane peroxyallylcarbonate and p-menthane peroxymethallylcarbonate.
Claim 23
Dependent Claim
32 words
A method according to claim 16, wherein said fluorine-containing monomer comprising said third monomer at step (c) is selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, polyvinylidene fluoride and fluorine-substituted vinyl ether.
Claim 24
Dependent Claim
31 words
A method according to claim 14, wherein said first fluorine-containing monomer at step (a) is selected from the group consisting of tetrafluoroethylene, chlorotrifluoroethylene, vinylidene fluoride, vinyl fluoride and fluorine-substituted vinyl ether.
Claim 25
Dependent Claim
38 words
A method according to claim 18, wherein said second monomer is selected from the group consisting of t-butyl peroxymethacrylate, di(t-butyl peroxy)fumarate, t-butyl peroxycrotonate, t-butyl peroxyallylcarbonate, t-hexyl peroxyallylcarbonate, 1,1,3,3-tetramethylbutyl peroxyallylcarbonate, t-butyl peroxymethallylcarbonate, 1,1,3,3-tetramethylbutyl peroxymethallylcarbonate, p-menthane peroxyallylcarbonate and p-menthane peroxymethallylcarbonate.
Claim 26
Dependent Claim
51 words
A method according to claim 19, wherein said third monomer comprises a combination selected from the group consisting of combinations of vinylidene fluoride and hexafluoropropene, combinations of vinylidene fluoride, hexafluoropropene and tetrafluoroethylene, combinations of vinylidene fluoride and chlorotrifluoroethylene, combinations of tetrafluoroethylene and propylene, combinations of tetrafluoroethylene and a fluorine-substituted vinyl ether.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-18 | 1988-03-19 | 1988-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-18 | 1992-03-19 | 1992-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-18 | 1996-03-19 | 1996-09-18 | $7700.00 | Window Closed / Lapsed |