Method of preparing crystalline aluminosilicate zeolites

Claim 2

A process for the preparation of a crystalline aluminosilicate zeolite, which comprises: preparing a mixture of an alkali metal compound, an amide compound, a silicon compound, an aluminum compound and water, said mixture having a composition, in terms of mole ratios, falling within the following ranges: SiO 2 /Al 2 O 3 :5 to 1000 H 2 O/SiO 2 :5 to 300 M/SiO 2 :0.001 to 10 A/SiO 2 :0.01 to 10 wherein M is an alkali metal oxide and A is said amide compound; holding said mixture at a temperature in the range of 80° C. to 300° C. and at elevated pressure for a period in the range of 3 hours to 60 days until aluminosilicate zeolite crystals are formed; and then recovering said crystals.

Claim 3

A process as claimed in claim 1, wherein said temperature is in the range of 120° C. to 175° C., said holding period is in the range of 1-5 days, and said elevated pressure is autogenous pressure.

Claim 4

A process as claimed in claim 1, wherein said amide compound is selected from the group consisting of formamide, acetamide, acetamide benzoate, acetochloroamide, propionamide, butylamide, benzamide, nicotinamide, lactamide, N-β-hydroxyethyl lactamide, caproic amide and glycolic amide.

Claim 5

A process as claimed in claim 1, wherein said crystals are recovered by successively filtering said crystals from said mixture, washing said crystals with water, and drying said crystals.

Claim 6

A process as claimed in claim 4, further comprising calcining said dried crystals at a temperature in the range of 200° C. to 1000° C.

Claim 7

A process as claimed in claim 1, wherein said mixture further contains a mineralizer selected from the group consisting of the chloride, bromide and sulfate of at least one metal selected from sodium, potassium and barium.

Claim 8

A process as claimed in claim 1, wherein said alkali metal oxide is Na 2 O, and said silicon compound is SiO 2 .

Claim 9

A process for the preparation of a crystalline aluminosilicate zeolite which comprises: preparing a reaction mixture consisting essentially of SiO 2 , Na 2 O, Al 2 O 3 , an amide compound selected from the group consisting of formamide, acetamide, acetamide benzoate, acetochloroamide, propionamide, butylamide, benzamide, nicotinamide, lactamide, N-β-hydroxyethyl lactamide, caproic amide and glycolic amide, and the balance is essentially water, said mixture having a composition such that the mole ratios of the foregoing ingredients of said mixture fall within the ranges: SiO 2 /Al 2 O 3 :5 to 1000 H 2 O/SiO 2 :5 to 300 Na 2 O/SiO 2 :0.001 to 10 A/SiO 2 :0.01 to 10 wherein A is said amide compound; stirring said reaction mixture, while maintaining said mixture at a temperature in the range of 80° C. to 300° C., at autogenous pressure, for a period in the range of 3 hours to 60 days, thereby forming aluminosilicate zeolite crystals; and then recovering said crystals, which crystals consist essentially of Na 2 O, Al 2 O 3 and SiO 2 .

Claim 10

A process for the preparation of a crystalline aluminosilicate zeolite which comprises: preparing a reaction mixture consisting essentially of SiO 2 , Na 2 O, Al 2 O 3 , an amide compound selected from the group consisting of formamide, acetamide, acetamide benzoate, acetochloroamide, propionamide, butylamide, benzamide, nicotinamide, lactamide, N-β-hydroxyethyl lactamide, caproic amide and glycolic amide, and the balance is essentially water, said mixture having a composition such that the mole ratios of the foregoing ingredients of said mixture fall within the ranges: SiO 2 /Al 2 O 3 :5 to 1000 H 2 O/SiO 2 :5 to 300 Na 2 O/SiO 2 :0.001 to 10 A/SiO 2 :0.01 to 10 wherein A is said amide compound; stirring said reaction mixture, while maintaining said mixture at a temperature in the range of 80° C. to 300° C., at autogenous pressure, for a period in the range of 3 hours to 60 days, thereby forming aluminosilicate zeolite crystals; and then recovering said crystals, which crystals consist essentially of Na 2 O, Al 2 O 3 and SiO 2 .