High shear resistant pipewrap anti-corrosion system
Assignee: Kendall Co
•
Filing: 1982-07-19
•
Granted: 1984-09-18
•
Expires: 2002-07-19
Abstract
Abstract An anticorrosion and high shear resistant pipewrap system is described wherein a pipe surface is first coated with a primer comprised of natural rubber, resins, and a metal oxide activator dispersed in an organic solvent. The primer-coated pipe is then overlaid with an adhesive-coated polyolefin tape, the adhesive comprising a butyl-based rubber, tackifying agent and a cross-linking agent, p-quinone dioxime. The cross linking agent functions in the presence of an organo-titanate-treated metal oxide, being a catalyst such as lead dioxide, or the like, that results in high rates of cross linking in both the primer coating, the adhesive coating and the primer/adhesive interface zone. Minimal creep of the described anti-corrosion protective coating is noted in high shear stress environments.
Inventors
- 👤 Robert F. Jenkins
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 17:32
CPC Classifications
C; C09; C09J; C09J5/00; C09J5/02; C09J7/00; C09J7/30; C09J7/38; C09J7/381; C09J7/383; C09J2400/00; C09J2400/10; C09J2400/16; C09J2400/166; Y; Y10; Y10S; Y10S138/00; Y10S138/01; Y10S138/06; Y10T; Y10T428/00; Y10T428/31504; Y10T428/31536
Claims Analysis
Total Claims: 12
Claim 1
Independent Claim
117 words
A method of anti-corrosion coating of metal pipes, comprising the steps of: first applying a primer mixture to the outer surface of said pipe; said primer mixture comprising a blend of natural rubber, resins, and a crosslinking activator coated with organotitanate prior to incorporation in said primer mixture; said cross-linking activator being a metal oxide; then over-laying said primer-coated pipe surface with an adhesive-coated tape; said adhesive coated tape comprising an olefin polymer backing material, and having a rubber-based adhesive-coated onto a surface thereof; said adhesive coating being initially partially cross linked, and comprising a blend of virgin butyl rubber and reclaimed butyl rubber, a tackifier, and a residual amount of unreacted crosslinking agent, being p-quinone dioxime.
Claim 2
Dependent Claim
32 words
The method of anti-corrosion coating of pipes, according to claim 1, wherein said crosslinking agent, p-quinone dioxime is present in a concentration range of from about 0.25 to 0.45 percent by weight.
Claim 3
Dependent Claim
18 words
The method of anti-corrosion coating of pipes according to claim 1, wherein said metal oxide is lead dioxide.
Claim 4
Dependent Claim
32 words
The method of anti-corrosion coating of pipes according to claim 3, wherein said lead dioxide is present in the concentration range of up to about 15 percent by weight of total solids.
Claim 5
Dependent Claim
28 words
The method of anti-corrosion coating of pipes according to claim 3, wherein the preferred concentration of said lead dioxide is about 5 percent by weight of total solids.
Claim 6
Dependent Claim
41 words
The method of anti-corrosion coating of pipes according to claim 1, wherein additional crosslinking occurs at the primer-adhesive layer interface, as well as throughout the rest of primer and adhesive layers following overlaying of the primer surface by the adhesive-coated tape.
Claim 7
Dependent Claim
115 words
An anti-corrosion coating for pipe surfaces comprising: a primer mixture coating applied to outer surface of said pipes; said primer mixture coating comprising a blend of natural rubber, resins, and a crosslinking activator coated with organotitanate prior to incorporation in said primer mixture; said crosslinking activator being a metal oxide; an adhesive-coated tape overlaying said primer-coated pipe surface; said adhesive-coated tape comprising an olefin polymer backing material; said polymer backing material having a rubber-based adhesive coated onto a surface thereof; said adhesive coating being initially partially crosslinked, and comprising a blend of virgin butyl rubber and reclaimed butyl rubber, a tackifier, and a residual amount of unreacted crosslinking agent; said crosslinking agent being p-quinone dioxime.
Claim 8
Dependent Claim
31 words
An anti-corrosion coating for pipe surfaces according to claim 7, wherein said crosslinking agent, p-quinone dioxime, is present in a concentration range of from about 0.25 to 0.45 percent by weight.
Claim 9
Dependent Claim
17 words
An anti-corrosion coating for pipe surfaces according to claim 7, wherein said metal oxide is lead dioxide.
Claim 10
Dependent Claim
31 words
An anti-corrosion coating for pipe surfaces according to claim 9, wherein said lead dioxide is present in the concentration range of up to about 15 percent by weight of total solids.
Claim 11
Dependent Claim
27 words
An anti-corrosion coating for pipe surfaces according to claim 9, wherein the preferred concentration of said lead dioxide is about 5 percent by weight of total solids.
Claim 12
Dependent Claim
39 words
An anti-corrosion coating for pipe surfaces according to claim 7, wherein additional crosslinking occurs at the primer-adhesive layer interface, as well as throughout the rest of primer and adhesive-layers following overlaying of the primer surface by the adhesive-coated tape.
References Cited (Backward Citations)
US2161036A
Cited
GB704096A
Cited
US3002854A
Cited
US3063891A
Cited
US3160595A
Cited
US4268334A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-18 | 1988-03-19 | 1988-09-18 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-18 | 1992-03-19 | 1992-09-18 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-18 | 1996-03-19 | 1996-09-18 | $7700.00 | Window Closed / Lapsed |