Method of forming refractory metal conductors of low resistivity
Assignee: Intersil Corp
•
Filing: 1983-04-28
•
Granted: 1984-09-11
•
Expires: 2003-04-28
Abstract
Abstract The resistivity of a conductor of a refractory metal such as molybdenum is reduced by converting at least a portion of the conductor into a layer of molybdenum nitride in an atmosphere including ammonia at a temperature in the range from about 400° C. to about 850° C. and thereafter heating the conductor in an atmosphere including dry hydrogen in the range from about 950° C. to about 1000° C. for a time to convert the layer of molybdenum nitride into molybdenum and to convert molybdenum oxides in the conductor into molybdenum.
Inventors
- 👤 Manjin J. Kim
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 22:50
CPC Classifications
C; C22; C22B; C22B34/00; C22B34/30; C22B34/34; C22B34/36; C22B5/00; C22B5/02; C22B5/12; H; H10; H10P; H10P95/00
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
177 words
A method of lowering the resistivity of a conductor of a refractory metal comprising: providing a substrate, providing a conductor of a refractory metal selected from the class consisting of molybdenum and tungsten on said substrate, said conductor containing oxides of said refractory metal which raises the resistivity thereof, heating said substrate including said conductor in an atmosphere including ammonia at a temperature in the range from about 400° C. to about 850° C. for a time to cause said atmosphere to react with said conductor to convert at least a portion of said conductor into a layer of molybdenum nitride, heating said substrate and said conductor with said layer of refractory nitride thereon in an atmosphere of hydrogen substantially devoid of water vapor at a temperature in the range from about 950° to about 1000° C. for a time to convert said layer of refractory nitride into a layer of refractory metal and to convert a substantial portion of said oxides of said refractory metal into refractory metal whereby the resistivity of said conductor is reduced.
Claim 2
Independent Claim
177 words
A method of lowering the resistivity of a conductor of a refractory metal comprising: providing a substrate, providing a conductor of a refractory metal selected from the class consisting of molybdenum and tungsten on said substrate, said conductor containing oxides of said refractory metal which raises the resistivity thereof, heating said substrate including said conductor in an atmosphere including ammonia at a temperature in the range from about 400° C. to about 850° C. for a time to cause said atmosphere to react with said conductor to convert at least a portion of said conductor into a layer of molybdenum nitride, heating said substrate and said conductor with said layer of refractory nitride thereon in an atmosphere of hydrogen substantially devoid of water vapor at a temperature in the range from about 950° to about 1000° C. for a time to convert said layer of refractory nitride into a layer of refractory metal and to convert a substantial portion of said oxides of said refractory metal into refractory metal whereby the resistivity of said conductor is reduced.
Claim 3
Dependent Claim
12 words
The method of claim 1 in which said refractory metal is molybdenum.
Claim 4
Dependent Claim
12 words
The method of claim 1 in which said refractory metal is tungsten.
Claim 5
Dependent Claim
59 words
The method of claim 2 in which said conductor is heated in said atmosphere of ammonia at a temperature in the range from about 400° C. to about 750° C. for a time to react with said conductor to convert at least a portion of said conductor into a layer of molybdenum nitride having the composition Mo 2 N.
Claim 6
Dependent Claim
66 words
The method of claim 2 in which said substrate including said conductor is heated in an atmosphere of ammonia at a temperature in the range from about 750° to 850° C. for a time to cause said atmosphere to react with said conductor to convert at least a portion of said conductor into a layer of molybdenum nitride including the constituents Mo 2 N and MoN.
Claim 7
Dependent Claim
18 words
The method of claim 1 in which said atmosphere of ammonia consists of ammonia and an insert gas.
Claim 8
Dependent Claim
13 words
The method of claim 6 in which said relatively inert gas is nitrogen.
Claim 9
Dependent Claim
23 words
The method of claim 7 in which said atmosphere of ammonia consists of about 10% of ammonia by volume and the remainder nitrogen.
Claim 10
Dependent Claim
18 words
The method of claim 1 in which said atmosphere of hydrogen consists of hydrogen and an inert gas.
Claim 11
Dependent Claim
13 words
The method of claim 9 in which said relatively inert gas is nitrogen.
Claim 12
Dependent Claim
22 words
The method of claim 10 in which said atmosphere of ammonia consists of about 10% hydrogen by volume and the remainder nitrogen.
Claim 13
Dependent Claim
21 words
The method of claim 1 in which said atmosphere of hydrogen is caused to flow over said conductor of refractory metal.
Claim 14
Dependent Claim
15 words
The method of claim 1 in which said substrate is constituted of an insulating material.
Claim 15
Dependent Claim
15 words
The method of claim 1 in which said substrate is constituted of a semiconductor material.
Claim 16
Dependent Claim
15 words
The method of claim 1 in which said substrate is constituted of a conductive material.
References Cited (Backward Citations)
US3577275A
Cited
US3785862A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |