Method of recovering metal carbides
Assignee: Osram Sylvania Inc
•
Filing: 1982-10-18
•
Granted: 1984-09-11
•
Expires: 2002-10-18
Abstract
Abstract Metal carbide is reclaimed from scrap by sorting the scrap to separate pieces of cemented carbide having similar composition and grain size and treating the separated portion to form metal carbide grains which may be resintered with metal binder to obtain cemented carbides having grain characteristics similar to the starting material.
Inventors
- 👤 Richard F. Cheney
- 👤 Anil Bansal
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 07:07
CPC Classifications
C; C22; C22C; C22C29/00; C22C29/02; C22C29/06; C01; C01B; C01B32/00; C01B32/90; C01P; C01P2004/00; C01P2004/60; C01P2004/61; C01P2006/00; C01P2006/10; C01P2006/42; C01P2006/80
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
194 words
A method of reclaiming metal carbide in powder form from pieces of cemented metal carbide according to a desired grain size wherein said pieces have a substantially similar metal binder composition comprising determining the grain size of said pieces by measuring the coercive force of at least some of said pieces and ascertaining the grain size of said same pieces as a function of measured coercive force and metal binder content according to an approximate straight line when plotted on a Cartesian graph with the log G as the ordinate and Hc is the absicisa, where G is grain size and Hc is coercive force in oersteds according to the following equation: Log G=I 1 -mHc m=slope of said straight line I 1 =intercept of straight line with ordinate separating said pieces having an ascertained grain size into at least one lot, treating said lot by contacting at said cemented metal carbide with hydrochloric acid for a period of time and at a sufficient temperature and suitable concentration to substantially dissolve said matrix metal binder and form a matrix depeleted metal carbide, and forming a metal carbide powder from said matrix depleted metal carbide.
Claim 2
Dependent Claim
76 words
A method of reclaiming metal carbide according to claim 1 wherein said cemented metal carbide is separated into at least two additional lots, said one lot comprising a fine grain lot having a grain size less than about 2 microns, said additional two lots comprising a medium grain lot having a grain size from about 2 to less than about 5 microns, and a coarse grain lot having a grain size greater than about 5 microns.
Claim 3
Dependent Claim
76 words
A method of reclaiming metal carbide according to claim 1 wherein said cemented metal carbide comprises tungsten carbide and alloying metal carbide said one lot is separated into other lots, said other lots comprising a first lot consisting essentially of tungsten carbide and less than about one-half percent of alloying metal carbide, a second lot consisting essentially of tungsten carbide and from about 0.5 to less than about 4 percent by weight of alloying metal carbide.
Claim 4
Dependent Claim
26 words
A method of reclaiming metal carbide according to claim 1 wherein said one lot has substantially similar metal binder composition and substantially similar metal carbide composition.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-11 | 1988-03-12 | 1988-09-11 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-11 | 1992-03-12 | 1992-09-11 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-11 | 1996-03-12 | 1996-09-11 | $7700.00 | Window Closed / Lapsed |