US4469825A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Sequential heteropolymer dispersion and a particulate material obtainable therefrom, useful in coating compositions as an opacifying agent
Assignee: Rohm and Haas Co
•
Filing: 1983-03-09
•
Granted: 1984-09-04
•
Expires: 2003-03-09
Abstract
Abstract The present invention is concerned with the production and use of water-insoluble particulate heteropolymers made by sequential emulsion polymerization in dispersed particles of which a "core" of a polymeric base is at least partially encased in a "sheath" polymer that is permeable to an acid, such as acetic acid, adapted to cause swelling of the core by neutralization. The aqueous dispersion of the acid-swollen, base-containing core/sheath particles is useful in making water-base coating compositions, microvoids being formed in cores of the swollen particles in the film during the drying thereof. Thus, the heteropolymer dispersion can serve as an opacifying agent in coating compositions, such as water-base paints, as a supplement or replacement of part or all of the pigmentary material or extenders that would otherwise be used in such coating compositions. For convenience of description herein, the terms "core", "sheath", and "core/sheath polymer" are frequently used to refer to the distinct functional components of the individual polymer particles of the essential "mode" of the heteropolymers of the present invention even though in actuality, the components of the polymer particles thereof may not have the precise arrangement implied by this terminology.
Inventors
- 👤 Alexander Kowalski
- 👤 Martin Vogel
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-27 21:16
CPC Classifications
C; C09; C09D; C09D151/00; C09D151/003; C08; C08F; C08F265/00; Y; Y10; Y10S; Y10S525/00; Y10S525/902
Claims Analysis
Total Claims: 14
Claim 1
Independent Claim
274 words
A process for making an aqueous dispersion of water-insoluble core/sheath polymer particles comprising sequentially emulsion polymerizing at a temperature of from about 10° C. to about 100° C. in an aqueous medium containing a free radical initiator: (a) a core monomer system comprising one or more monoethylenically unsaturated monomers at least one of which monomers having an amine group and comprising at least 5% by weight of the core monomer system, thereby forming dispersed core particles having an average diameter of from about 0.05 to 1 micron, and (b) polymerizing in the presence of the dispersed core particles a sheath monomer system comprising at least one monoethylenically unsaturated monomer having no ionizable group to form a sheath on the core particles, any monoethylenically unsaturated amine in the sheath monomer mixture being present in an amount of no more than 10% by weight of the sheath monomers, the proportion of amine in the sheath monomer mixture being less than 1/3 the proportion thereof in the core monomer mixture, the resultant core-sheath particles having an average diameter before acidification and swelling of from about 0.07 to 4.5 microns, the relative amounts of core-forming monomer(s) and sheath forming monomer(s) being such that the ratio of the weight of the core to the weight of the total polymer in the resulting dispersed particles is from about 1:4 to 1:100, said sheath being permeable to an aqueous acid and having a T i of greater than 50° C., and (c) neutralizing with acid so as to swell said core and form particles which, when dried, contain a single void and cause opacity in compositions in which they are contained.
Claim 2
Dependent Claim
274 words
A process for making an aqueous dispersion of water-insoluble core/sheath polymer particles comprising sequentially emulsion polymerizing at a temperature of from about 10° C. to about 100° C. in an aqueous medium containing a free radical initiator: (a) a core monomer system comprising one or more monoethylenically unsaturated monomers at least one of which monomers having an amine group and comprising at least 5% by weight of the core monomer system, thereby forming dispersed core particles having an average diameter of from about 0.05 to 1 micron, and (b) polymerizing in the presence of the dispersed core particles a sheath monomer system comprising at least one monoethylenically unsaturated monomer having no ionizable group to form a sheath on the core particles, any monoethylenically unsaturated amine in the sheath monomer mixture being present in an amount of no more than 10% by weight of the sheath monomers, the proportion of amine in the sheath monomer mixture being less than 1/3 the proportion thereof in the core monomer mixture, the resultant core-sheath particles having an average diameter before acidification and swelling of from about 0.07 to 4.5 microns, the relative amounts of core-forming monomer(s) and sheath forming monomer(s) being such that the ratio of the weight of the core to the weight of the total polymer in the resulting dispersed particles is from about 1:4 to 1:100, said sheath being permeable to an aqueous acid and having a T i of greater than 50° C., and (c) neutralizing with acid so as to swell said core and form particles which, when dried, contain a single void and cause opacity in compositions in which they are contained.
Claim 3
Dependent Claim
27 words
A process according to claim 1 wherein the amine monomer in (a) is selected from the group consisting of vinylpyridine, 2-(dimethylamino)ethyl methacrylate, 2-(tert-butylamino)ethyl methacrylate, and 3-(dimethylamino)propyl methacrylamide.
Claim 4
Dependent Claim
25 words
A process according to claim 1 in which the core/sheath particles have an average diameter of from 0.2 to about 2.0 microns in unswollen condition.
Claim 5
Dependent Claim
19 words
A process according to claim 1 in which the formation of the sheath in (b) is a multistage process.
Claim 6
Dependent Claim
92 words
A process according to claim 4 wherein in at least one stage of the multistage formation of the sheath a crosslinked polymer is formed from a monomer mixture of at least one monoethylenically unsaturated monomer and about 1% to about 50% by weight of the monomer mixture of at least one polyethylenically unsaturated monomer, the core/sheath polymer being swollen by at least partial neutralization by application of acid prior to the completion of the crosslinking stage when the amount of polyethylenically unsaturated monomer exceeds about 5% by weight of the monomer mixture.
Claim 7
Dependent Claim
65 words
A process according to claim 1 in which the formation of the sheath in (b) is a multistage process comprising first forming a hard and/or crosslinked polymer sheath, then forming a soft polymer sheath of monomers selected to provide a relatively softer polymer having a T i of less than 50° C. and at least 10° C. lower than that of the hard sheath polymer.
Claim 8
Dependent Claim
25 words
A process according to claim 6 in which the T i of the polymer at the exterior surface of the particles is about 20° C.
Claim 9
Dependent Claim
138 words
A composition comprising an aqueous dispersion of water-insoluble core/sheath polymer particles have an average diameter of 0.07 to 4.5 microns, having a core polymerized from a monomer system comprising one or more monoethylenically unsaturated monomers, at least one of said unsaturated monomers having an amine group, and having at least one sheath polymerized from at least one different sheath monomer system, at least one of said different sheath monomer systems being hard and producing a sheath polymer having a T i greater than 50° C., being non film-forming at 20° C., and being permeable to acid, said core being swollen by neutralization with acid in the presence of water, said particles having a property such that when subsequently dried a single cavity forms in said core and said particles cause opacity in compositions in which they are contained.
Claim 10
Dependent Claim
138 words
A composition comprising an aqueous dispersion of water-insoluble core/sheath polymer particles have an average diameter of 0.07 to 4.5 microns, having a core polymerized from a monomer system comprising one or more monoethylenically unsaturated monomers, at least one of said unsaturated monomers having an amine group, and having at least one sheath polymerized from at least one different sheath monomer system, at least one of said different sheath monomer systems being hard and producing a sheath polymer having a T i greater than 50° C., being non film-forming at 20° C., and being permeable to acid, said core being swollen by neutralization with acid in the presence of water, said particles having a property such that when subsequently dried a single cavity forms in said core and said particles cause opacity in compositions in which they are contained.
Claim 11
Dependent Claim
35 words
A composition for coating and/or impregnating a substrate comprising a film-forming vinyl addition polymer either dissolved or dispersed in an aqueous medium and an aqueous dispersion of water insoluble core/sheath polymer particles of claim 8.
Claim 12
Dependent Claim
49 words
A composition in accordance with claim 9 wherein the film-forming vinyl addition polymer has an apparent second order transition temperature (T i ) of about 17° to 20° C., and the core/sheath polymer is present in a pigment volume concentration of at least 5%, and further including inorganic pigment.
Claim 13
Dependent Claim
49 words
A process comprising depositing a film of the composition according to claim 9 on a solid substrate to be coated and/or impregnated, and subsequently drying the composition forming single cavities in the core of substantially each of said particles so as to contribute to the opacity of said film.
Claim 14
Dependent Claim
12 words
Articles coated and/or impregnated with the opaque film-forming composition of claim 1.
References Cited (Backward Citations)
EP0022633B1
Cited
US4304703A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-04 | 1988-03-05 | 1988-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-04 | 1992-03-05 | 1992-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-04 | 1996-03-05 | 1996-09-04 | $7700.00 | Window Closed / Lapsed |