Fixation by ion exchange of toxic materials in a glass matrix
Assignee: Individual
•
Filing: 1982-04-21
•
Granted: 1984-09-04
•
Expires: 2002-04-21
Abstract
Abstract This invention relates to the immobilization of toxic, e.g., radioactive, materials in a silicate glass or silica gel matrix for extremely long periods of time. Toxic materials, such as radioactive wastes containing radioactive cations, which may be in the form of liquids, or solids dissolved or dispersed in liquids or gases, are incorporated into a glass or silica gel matrix, having alkali metal, Group Ib metal and/or ammonium cations bonded to silicon atoms of said glass or silica gel through divalent oxygen linkages, by a process which involves the ion exchange of said toxic or radioactive cations with said alkali metal, Group Ib metal and/or ammonium cations to bind said toxic or radioactive cations to silicon atoms of said glass or silica gel through said silicon-bonded divalent oxygen linkages. Thereafter, the resulting glass or silica gel now characterized by toxic or radioactive cations bonded to silicon atoms through divalent oxygen linkages can be stored, or packaged in suitable containers, or disposed of as by burial, and/or sintered to collapse the pores thereof.
Inventors
- 👤 Catherine J. Simmons
- 👤 Joseph H. Simmons
- 👤 Pedro B. Macedo
- 👤 Theodore A. Litovitz
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-30 11:05
CPC Classifications
C; C03; C03C; C03C1/00; C03C1/002; B; B01; B01J; B01J39/00; B01J39/08; B01J39/14; C03C1/02; C03C1/026; C03C11/00; C03C11/005; C03C21/00; C03C21/001; C03C23/00; C03C23/0095; C03C3/00; C03C3/04; C03C3/06; C03C3/061; C03C3/076; C03C3/089; G; G21; G21F; G21F9/00; G21F9/04; G21F9/06; G21F9/12; G21F9/28; G21F9/30; G21F9/301; G21F9/302; G21F9/305; C03C2201/00; C03C2201/06; C03C2201/08; C03C2201/10; C03C2201/20; C03C2201/23; C03C2201/30; C03C2201/34; C03C2201/3435; C03C2201/40; C03C2201/50
Claims Analysis
Total Claims: 34
Claim 1
Independent Claim
135 words
Process which causes the proton (H + ) of silicon-bonded hydroxyl groups on the internal surfaces of porous silicate glass to undergo ion-exchange reaction without occurrence of substantial dissolution of the glass during the reaction which comprises: (a) impregnating a porous silicate glass characterized by at least 75 mol percent SiO 2 , an interconnecting pore structure, and silicon-bonded hydroxyl groups on its surfaces, (b) with a liquid containing non-radioactive alkali metal cations, non-radioactive Group I(b) metal cations, ammonium cations, or mixtures thereof, (c) said liquid buffered with non-radioactive ammonium cations to maintain a pH in the range of about 11 to about 13, (d) for a period of time to provide a distribution of said non-radioactive cations within the interconnected pores of said glass, said cations being bonded to silicon through divalent oxy groups.
Claim 2
Dependent Claim
135 words
Process which causes the proton (H + ) of silicon-bonded hydroxyl groups on the internal surfaces of porous silicate glass to undergo ion-exchange reaction without occurrence of substantial dissolution of the glass during the reaction which comprises: (a) impregnating a porous silicate glass characterized by at least 75 mol percent SiO 2 , an interconnecting pore structure, and silicon-bonded hydroxyl groups on its surfaces, (b) with a liquid containing non-radioactive alkali metal cations, non-radioactive Group I(b) metal cations, ammonium cations, or mixtures thereof, (c) said liquid buffered with non-radioactive ammonium cations to maintain a pH in the range of about 11 to about 13, (d) for a period of time to provide a distribution of said non-radioactive cations within the interconnected pores of said glass, said cations being bonded to silicon through divalent oxy groups.
Claim 3
Dependent Claim
32 words
The process of claim 1 wherein said ion-exchanged porous glass contains at least about 0.3 mol percent to about 10 mol percent alkali metal cations bonded to silicon through divalent oxy groups.
Claim 4
Dependent Claim
19 words
The process of claim 1 or 2 wherein potassium cation is bonded to surface silicon through divalent oxy groups.
Claim 5
Dependent Claim
19 words
The process of claim 1 or 2 wherein sodium cation is bonded to surface silicon through divalent oxy groups.
Claim 6
Dependent Claim
71 words
The process which comprises reacting the ion-exchange porous silicate glass containing bonded non-radioactive cations defined in claim 1 or 2 with a liquid containing toxic cations, said toxic cations being capable of displacing said non-radioactive cations to provide a distribution of internal surface silicon-bonded toxic cation oxide groups within the pores of said glass; and thereafter confining the resultant porous silicate glass characterized by such internal silicon-bonded toxic cation oxide groups.
Claim 7
Dependent Claim
30 words
The process of claim 5 wherein the confinement of said resultant porous silicate glass is effected by heating to collapse said pores containing such internal silicon-bonded toxic cation oxide groups.
Claim 8
Dependent Claim
111 words
The process of claim 5 which comprises impregnating the ion-exchanged porous silicate glass which contains bonded non-radioactive cations as defined in claim 1 or 2 with a liquid having a pH in the range of from about 2 to about 13 and containing radioactive cations, for a period of time to dispose said liquid within the pores of said glass and to displace at least a portion of said non-radioactive cations by said radioactive cations to provide a distribution of internal surface silicon-bonded radioactive cation oxy groups disposed within the pores of said glass; and thereafter confining the resultant porous silicate glass characterized by such internal silicon-bonded radioactive cation oxy groups.
Claim 9
Dependent Claim
33 words
The process of claim 7 wherein said ion-exchanged porous silicate glass contains non-radioactive alkali metal cations bonded to silicon through divalent oxygen linkages on the internal surfaces of said pores of the glass.
Claim 10
Dependent Claim
24 words
The process of claim 7 wherein from about 0.3 mol percent to about 10 mol percent non-radioactive sodium cation is bonded to said silicon.
Claim 11
Dependent Claim
29 words
Process of claim 9 wherein the resultant porous silicate glass contains at least one part per billion by weight of radioactive cation bonded to silicon through divalent oxygen linkages.
Claim 12
Dependent Claim
86 words
Process of claim 7 wherein said liquid is an aqueous medium comprising a mixture of radioactive cations selected from the group consisting of radioactive cations of rubidium, strontium, the lanthanides, cobalt, cadmium, zironium, molybdenum, technetium, niobium, ruthenium, palladium, tellurium, cesium, barium, francium, yttrium, radium, the actinides, and mixtures thereof; wherein the amount of said non-radioactive cations in said porous silicate glass is about 0.3 mol percent to about 10 mol percent; and wherein said pH is in the range of from about 6 to about 9.5.
Claim 13
Dependent Claim
101 words
A process for removing radioactive cations from a liquid stream of radioactive nuclear wastes containing the same and concentrating said radioactive cations comprising impregnating an ion-exchanged porous silicate glass which contains bonded non-radioactive cations defined in claim 1 or 2, with a liquid stream of radioactive nuclear wastes containing radioactive cations for a period of time sufficient to dispose said liquid within the pores of said glass and to displace said non-radioactive cations to provide a distribution of internal silicon-bonded radioactive cation oxide groups; and thereafter confining the resultant porous silicate glass characterized by such internal silicon-bonded radioactive cation oxide groups.
Claim 14
Dependent Claim
23 words
Process of claim 12 wherein said liquid containing radioactive cations has a radioactivity of about 0.01 microcurie to about 1 microcurie per milliliter.
Claim 15
Dependent Claim
153 words
A process which comprises impregnating a porous silicate glass or silica gel having interconnected pores and non-radioactive protons (H + ) bonded to silicon through divalent oxygen linkages on the internal surfaces of said pores, with primary coolant water of a boiling water reactor system which contains radioactive cations to dispose said primary coolant water within the pores of said glass or silica gel after adding ammonium hydroxide to said primary collant water to both maintain the pH thereof in the range of about 6 to about 9.5 and to effect the ion-exchange of said non-radioactive protons with ammonium cations, said non-radioactive ammonium cations being capable of being displaced by said radioactive cations to provide a distribution of internal silicon-bonded radioactive cation oxy groups within the pores of said glass or silica gel; and thereafter confining the resultant porous silicate glass or silica gel characterized by such internal silicon-bonded radioactive cation oxy groups.
Claim 16
Dependent Claim
153 words
A process which comprises impregnating a porous silicate glass or silica gel having interconnected pores and non-radioactive protons (H + ) bonded to silicon through divalent oxygen linkages on the internal surfaces of said pores, with primary coolant water of a boiling water reactor system which contains radioactive cations to dispose said primary coolant water within the pores of said glass or silica gel after adding ammonium hydroxide to said primary collant water to both maintain the pH thereof in the range of about 6 to about 9.5 and to effect the ion-exchange of said non-radioactive protons with ammonium cations, said non-radioactive ammonium cations being capable of being displaced by said radioactive cations to provide a distribution of internal silicon-bonded radioactive cation oxy groups within the pores of said glass or silica gel; and thereafter confining the resultant porous silicate glass or silica gel characterized by such internal silicon-bonded radioactive cation oxy groups.
Claim 17
Dependent Claim
19 words
Process of claim 14 wherein said pH is maintained in the range of from above 7 to about 9.
Claim 18
Dependent Claim
9 words
The ion-exchanged porous silicate glass product of claim 1.
Claim 19
Dependent Claim
9 words
The ion-exchanged porous silicate glass product of claim 2.
Claim 20
Dependent Claim
26 words
The ion-exchanged porous silicate glass product of claim 1 or 2 wherein said alkali metal cation is potassium bonded to surface silicon through divalent oxy groups.
Claim 21
Dependent Claim
25 words
The ion-exchanged porous silicate glass product of claim 1 or 2 wherein said alkali metal is sodium bonded to surface silicon through divalent oxy groups.
Claim 22
Dependent Claim
19 words
An ion-exchange column comprising the ion-exchanged porous silicate glass product of claim 16 or 17 as ion-exchange medium therefor.
Claim 23
Dependent Claim
17 words
An ion-exchange column comprising the ion-exchanged porous silicate glass product of claim 19 as ion-exchanged medium therefor.
Claim 24
Dependent Claim
64 words
Porous silicate glass prepared as defined in claim 1 and containing at least one part per billion by weight of radioactive cation of the group consisting of radioactive cations of rubidium, strontium, the lanthanides, cobalt, cadmium, zirconium, molybdenum, technetium, niobium, ruthenium, palladium, tellurium, cesium, barium, francium, yttrium, radium, the actinides, and mixtures thereof; said radioactive cation bonded to surface silicon through divalent oxygen linkages.
Claim 25
Dependent Claim
51 words
Porous silicate glass of at least 75 mol percent SiO 2 , an interconnected pore structure, a surface to weight ratio of from about 5 to about 1500 m 2 /g, and containing non-radioactive ammonium cations disposed within the interconnecting pores and bonded to surface silicon thereof through divalent oxy linkages.
Claim 26
Dependent Claim
51 words
Porous silicate glass of at least 75 mol percent SiO 2 , an interconnected pore structure, a surface to weight ratio of from about 5 to about 1500 m 2 /g, and containing non-radioactive ammonium cations disposed within the interconnecting pores and bonded to surface silicon thereof through divalent oxy linkages.
Claim 27
Dependent Claim
34 words
The porous silicate glass of claim 23 which, in addition to ammonium cations, contains non-radioactive cations of the group consisting of alkali-metal cations, Group I(b) cations and mixtures thereof, bonded to said surface silicon.
Claim 28
Dependent Claim
32 words
The porous silicate glass of claim 24 characterized by a surface to weight ratio at least upward of 100 m 2 /g and ammonium and sodium cations bonded to said surface silicon.
Claim 29
Dependent Claim
21 words
The porous silicate glass of claim 23 or 24 or 25 characterized by about 0.3 to about 10 mol percent cations.
Claim 30
Dependent Claim
19 words
The porous silicate glass of claims 24 or 25 characterized by about 1 to about 10 mol percent cations.
Claim 31
Dependent Claim
14 words
The porous silicate glass of claims 23 or 24 or 25 in particulate form.
Claim 32
Dependent Claim
17 words
An ion-exchange column comprising particulate porous silicate glass as defined in claims 23 or 24 or 25.
Claim 33
Dependent Claim
93 words
Porous silicate glass characterized by at least 75 mol percent SiO 2 , an interconnecting pore structure, a surface to weight ratio of from about 5 to about 1500 m 2 /g, and radioactive cations, disposed within the interconnecting pores and bonded to surface silicon through divalent oxy linkages, said radioactive cations of the group consiting of radioactive cations of rubidium, strontium, the lanthanides, cobalt, cadmium, zirconium, molybdenum, technetium, niobium, ruthenium, palladium, tellurium, cesium, barium, francium, yttrium, radium, the actinides, and mixtures thereof; said radioactive cation bonded to silicon through divalent oxygen linkages.
Claim 34
Dependent Claim
93 words
Porous silicate glass characterized by at least 75 mol percent SiO 2 , an interconnecting pore structure, a surface to weight ratio of from about 5 to about 1500 m 2 /g, and radioactive cations, disposed within the interconnecting pores and bonded to surface silicon through divalent oxy linkages, said radioactive cations of the group consiting of radioactive cations of rubidium, strontium, the lanthanides, cobalt, cadmium, zirconium, molybdenum, technetium, niobium, ruthenium, palladium, tellurium, cesium, barium, francium, yttrium, radium, the actinides, and mixtures thereof; said radioactive cation bonded to silicon through divalent oxygen linkages.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-04 | 1988-03-05 | 1988-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-04 | 1992-03-05 | 1992-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-04 | 1996-03-05 | 1996-09-04 | $7700.00 | Window Closed / Lapsed |