Pipes made of polypropylene reinforced with carbon fibers
Assignee: Kureha Corp
•
Filing: 1983-12-20
•
Granted: 1984-09-04
•
Expires: 2003-12-20
Abstract
Abstract Pipes of polypropylene reinforced with carbon fibers comprising 100 parts by weight of polypropylene, 10 to 40 parts by weight of a modified polypropylene by an organic unsaturated carboxylic acid or a copolymer of propylene and the organic unsaturated carboxylic acid and 5 to 70 parts by weight of carbon fibers of 5 to 30 micrometers in diameter and a ratio of diameter to length of 10 or more. The rate of retention of the original tensile strength of pipe in boiling water for 6 months at 100° C. was higher than 95%.
Inventors
- 👤 Hiroaki Satoh
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 16:26
CPC Classifications
C; C08; C08L; C08L23/00; C08L23/02; C08L23/10; C08L23/12; C08K; C08K7/00; C08K7/02; C08K7/04; C08K7/06; C08L23/14; C08L23/26; F; F16; F16L; F16L9/00; F16L9/12; F16L9/127; F16L9/128; F24; F24D; F24D3/00; F24D3/12; F24D3/14; F24D3/146; B; B29; B29C; B29C48/00; B29C48/03; B29C48/09; B29C48/15; B29K; B29K2023/00; B29K2023/10; B29K2023/12; B29K2105/00; B29K2105/06; B29K2105/12; B29K2307/00; B29L; B29L2023/00; B29L2023/22; Y; Y02; Y02B; Y02B30/00; Y02P; Y02P20/00; Y02P20/10; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1372
Claims Analysis
Total Claims: 4
Claim 1
Independent Claim
150 words
A pipe for hot water of polypropylene reinforced with carbon fibers made from a composite material consisting essentially of: (a) 100 parts by weight of polypropylene; (b) 10 to 40 parts by weight of a modified polypropylene selected from the group of: (1) polypropylene modified by the chemical addition of from 1 to 8 parts by weight of an organic unsaturated carboxylic acid per 100 parts by weight of polypropylene, said acid being selected from the group consisting of maleic acid, acrylic acid, methacrylic acid, fumaric acid, endobicyclo (2.2.1)2, 3-dicarboxylic acid and their anydrides; and (2) propylene copolymerized with from 1 to 8 parts by weight of said carboxylic acid per 100 parts by weight of said propylene; and (c) from 5 to 70 parts by weight of carbon fibers having a diameter of from 5 to 30 micrometers and a ratio of diameter to length of at least 10.
Claim 2
Dependent Claim
150 words
A pipe for hot water of polypropylene reinforced with carbon fibers made from a composite material consisting essentially of: (a) 100 parts by weight of polypropylene; (b) 10 to 40 parts by weight of a modified polypropylene selected from the group of: (1) polypropylene modified by the chemical addition of from 1 to 8 parts by weight of an organic unsaturated carboxylic acid per 100 parts by weight of polypropylene, said acid being selected from the group consisting of maleic acid, acrylic acid, methacrylic acid, fumaric acid, endobicyclo (2.2.1)2, 3-dicarboxylic acid and their anydrides; and (2) propylene copolymerized with from 1 to 8 parts by weight of said carboxylic acid per 100 parts by weight of said propylene; and (c) from 5 to 70 parts by weight of carbon fibers having a diameter of from 5 to 30 micrometers and a ratio of diameter to length of at least 10.
Claim 3
Dependent Claim
19 words
The pipe of claim 1, wherein the modified polypropylene is polypropylene modified by the chemical addition of maleic acid.
Claim 4
Dependent Claim
17 words
The pipe of claim 1, wherein the modified polypropylene is a copolymer of propylene and acrylic acid.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-09-04 | 1988-03-05 | 1988-09-04 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-09-04 | 1992-03-05 | 1992-09-04 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-09-04 | 1996-03-05 | 1996-09-04 | $7700.00 | Window Closed / Lapsed |