Method for making a silicon dioxide coating
Assignee: Nippon Sheet Glass Co Ltd
•
Filing: 1983-10-03
•
Granted: 1984-08-28
•
Expires: 2003-10-03
Abstract
Abstract A method for making a silicon dioxide coating on a surface of a substrate such as, for example, an alkali metal-containing glass sheet by dipping the substrate in a treatment liquid obtained by adding boric acid to an aqueous silicon dioxide-saturated solution of hydrosilicofluoric acid.
Inventors
- 👤 Hideo Kawahara
- 👤 Hirotsugu Nagayama
- 👤 Hisao Honda
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-01 16:38
CPC Classifications
C; C03; C03C; C03C17/00; C03C17/22; C03C17/23; C03C17/25; C03C2217/00; C03C2217/20; C03C2217/21; C03C2217/213; C03C2218/00; C03C2218/10; C03C2218/11; C03C2218/111
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
38 words
A method for making a silicon dioxide coating on a surface of a substrate, which method comprises dipping the substrate in a treatment liquid obtained by adding boric acid to an aqueous silicon dioxide-saturated solution of hydrosilicofluoric acid.
Claim 2
Independent Claim
38 words
A method for making a silicon dioxide coating on a surface of a substrate, which method comprises dipping the substrate in a treatment liquid obtained by adding boric acid to an aqueous silicon dioxide-saturated solution of hydrosilicofluoric acid.
Claim 3
Dependent Claim
20 words
A method as claimed in claim 1, wherein the concentration of hydrosilicofluoric acid ranges from 0.5 mol/l to 3.0 mol/l.
Claim 4
Dependent Claim
63 words
A method as claimed in claim 2, wherein, upon preparation of the aqueous solution of hydrosilicofluoric acid, silicon dioxide is first of all saturated in an aqueous solution containing hydrosilicofluoric acid at a concentration higher than the desired value and the silicon dioxide-saturated squeous solution is then diluted with water so as to lower the concentration of hydrosilicofluoric acid to its desired value.
Claim 5
Independent Claim
36 words
A method as claimed in any one of claims 1 to 3, wherein boric acid is added in an amount of 1.0×10 -2 to 3.0×10 -2 mole per unit mole of H 2 SiF 6 .
Claim 6
Independent Claim
35 words
A method as claimed in any one of claims 1 to 4, wherein, after making the silicon dioxide coating by dipping the substrate in the treatment liquid, the substrate is subjected to a heat treatment.
Claim 7
Dependent Claim
18 words
A method as claimed in claim 5, wherein the heat treatment is effected at 300° to 550° C.
Claim 8
Independent Claim
58 words
A method as claimed in any one of claims 1 to 6, wherein, after making the silicon dioxide coating by dipping the substrate in the treatment liquid, boric acid is added to the treatment liquid so as to repeatedly use the treatment liquid while maintaining the silicon dioxide making capacity of the treatment liquid at a constant level.
Claim 9
Independent Claim
80 words
A method as claimed in any one of claims 1 to 7, wherein a relatively thin silicon dioxide coating of at least 400 Å is made in advance on the surface of the substrate and the resulting silicon dioxide-coated substrate is dipped in the treatment liquid obtained by adding boric acid to the aqueous silicon dioxide-saturated solution of hydrosilicofluoric acid, thereby making a thick silicon dioxide coating of at least 5000 Å on the surface of the silicon dioxide-coated substrate.
Claim 10
Dependent Claim
34 words
A method as claimed in claim 8, wherein the relatively thin silicon dioxide coating made in advance on the surface of the substrate is made of a mixture of silicon dioxide and another material.
Claim 11
Dependent Claim
36 words
A method as claimed in claim 8 or 9, wherein the surface of the substrate is coated in advance with the relatively thin silicon dioxide coating by the vacuum deposition, sputtering, CVD or conventionally-known dipping technique.
Claim 12
Independent Claim
115 words
A method as claimed in any one of claims 1 to 10, wherein the dipping treatment step is a continuous treatment step comprising, after pumping out the treatment liquid continuously at a constant rate from a substrate-dipping tank, continuously filtering the thus-pumped out treatment liquid through a filter having apertures of 1.5 microns or smaller in diameter and returning the thus-filtered treatment liquid to the substrate-dipping tank; and, in the continuous treatment step, the percentage of the amount of the treatment liquid circulated per minute relative to the whole treatment liquid is a least 3% and a necessary amount of boric acid is continuously charged and mixed as an aqueous solution in the treatment liquid.
Claim 13
Dependent Claim
27 words
A method as claimed in claim 11, wherein the treatment liquid flows as a laminar flow parallel to the surface of the substrate through the substrate-dipping tank.
References Cited (Backward Citations)
US2695247A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-28 | 1988-02-27 | 1988-08-28 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-28 | 1992-02-27 | 1992-08-28 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-28 | 1996-02-27 | 1996-08-28 | $7700.00 | Window Closed / Lapsed |