Preparation of yttria-gadolinia ceramic scintillators by vacuum hot pressing
Assignee: General Electric Co
•
Filing: 1982-06-18
•
Granted: 1984-08-21
•
Expires: 2002-06-18
Abstract
Abstract Polycrystalline ceramic scintillators are prepared by a vacuum hot-pressing method. The process includes pressing a multi-component powder at high temperature under vacuum. Following a holding period, the pressure and temperature are increased and maintained for a predetermined length of time. The finished scintillator includes Y 2 O 3 , Gd 2 O 3 , and one or more of Eu 2 O 3 , Nd 2 O 3 , Yb 2 O 3 , DY 2 O 3 , Pr 2 O 3 , and Tb 2 O 3 rare earth activator oxides. The finished scintillator may also include at least one of SrO and CaO as afterglow reducers.
Inventors
- 👤 Charles D. Greskovich
- 👤 Dominic A. Cusano
- 👤 Frank A. DiBianca
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 20:35
CPC Classifications
G; G01; G01T; G01T1/00; G01T1/16; G01T1/20; G01T1/202; G01T1/2023; C; C04; C04B; C04B35/00; C04B35/50; C04B35/505; C04B35/622; C04B35/64; C04B35/645; C04B35/6455; C09; C09K; C09K11/00; C09K11/08; C09K11/77; C09K11/7766; C09K11/7767; C09K11/7769; C09K11/7783; C09K11/7784; C09K11/7787
Claims Analysis
Total Claims: 20
Claim 1
Independent Claim
164 words
A method for preparing a polycrystalline ceramic x-ray or gamma ray scintillator body comprising the steps of: preparing a multicomponent powder consisting essentially of between about 5 and 50 mole percent Gd 2 O 3 , and between about 0.02 and 12 mole percent of at least one rare earth activator oxide selected from the group consisting of Eu 2 O 3 , Nd 2 O 3 , Yb 2 O 3 , Dy 2 O 3 , Tb 2 O 3 , and Pr 2 O 3 , the remainder of said multicomponent powder being Y 2 O 3 ; pressing said multicomponent powder under vacuum at a first temperature and pressure for a first predetermined period of time; and PG,25 increasing said first temperature and pressure to a second temperature and pressure and maintaining said second temperature and pressure for a second period of time to form said polycrystalline ceramic scintillator body, whereby the optical clarity of said scintillator body is transparent-to-translucent.
Claim 2
Independent Claim
164 words
A method for preparing a polycrystalline ceramic x-ray or gamma ray scintillator body comprising the steps of: preparing a multicomponent powder consisting essentially of between about 5 and 50 mole percent Gd 2 O 3 , and between about 0.02 and 12 mole percent of at least one rare earth activator oxide selected from the group consisting of Eu 2 O 3 , Nd 2 O 3 , Yb 2 O 3 , Dy 2 O 3 , Tb 2 O 3 , and Pr 2 O 3 , the remainder of said multicomponent powder being Y 2 O 3 ; pressing said multicomponent powder under vacuum at a first temperature and pressure for a first predetermined period of time; and PG,25 increasing said first temperature and pressure to a second temperature and pressure and maintaining said second temperature and pressure for a second period of time to form said polycrystalline ceramic scintillator body, whereby the optical clarity of said scintillator body is transparent-to-translucent.
Claim 3
Dependent Claim
55 words
The method of claim 1 wherein said multicomponent powder comprises between about 20 and 40 mole percent Gd 2 O 3 , between about 1 and 6 mole percent Eu 2 O 3 , and between about 0.1 and 2 mole percent Yb 2 O 3 , the remainder being Y 2 O 3 .
Claim 4
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 1 and 6 mole percent Eu 2 O 3 .
Claim 5
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 0.05 and 1.5 mole percent Nd 2 O 3 .
Claim 6
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 0.05 and 3 mole percent Tb 2 O 3 .
Claim 7
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 0.1 and 2 mole percent Yb 2 O 3 .
Claim 8
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 0.03 and 1 mole percent Dy 2 O 3 .
Claim 9
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 0.02 and 0.05 mole percent Pr 2 O 3 .
Claim 10
Dependent Claim
22 words
The method of claim 1 wherein said multicomponent powder comprises between about 20 and 40 mole percent Gd 2 O 3 .
Claim 11
Dependent Claim
19 words
The method of claim 1 wherein said multicomponent powder further comprises between about 0.1 and 2 mole percent SrO.
Claim 12
Dependent Claim
18 words
The method of claim 1 wherein said multicomponent powder further comprises between about 0.1 and 2mole percent CaO.
Claim 13
Dependent Claim
40 words
The method of claim 1 wherein said step of preparing said multicomponent powder comprises mixing high purity, micron-to-submicron powders of Gd 2 O 3 , Y 2 O 3 , and at least one of said rare earth activator oxides.
Claim 14
Dependent Claim
50 words
The method of claim 1 wherein said step of preparing said multicomponent powder comprises the steps of: coprecipitating by the wet chemical oxalate process the oxalates of Y, Gd, and at least one of said rare earth activator oxides; and calcining said oxalates so as to obtain the corresponding oxides.
Claim 15
Dependent Claim
38 words
The method of claim 13 wherein said step of calcining comprises the step of heating said oxalates in air at a temperature of between about 700° C. and 900° C. for between about 1 hour and 4 hours.
Claim 16
Dependent Claim
19 words
The method of claim 13 wherein said step of calcining is preceded by the step of milling said oxalates.
Claim 17
Dependent Claim
20 words
The method of claim 13 or 15 further comprising the step of milling said oxides obtained in said calcining step.
Claim 18
Dependent Claim
54 words
The method of claim 1, 12, or 13 wherein said step of pressing comprises the step of pressing said multicomponent powder at a pressure of between about 1,000 psi and 1,200 psi at a temperature of between about 600° C. and 700° C. under a vacuum of up to 200 microns for 1 hour.
Claim 19
Dependent Claim
53 words
The method of claim 17 wherein said step of increasing said first temperature and pressure comprises increasing the temperature to between about 1300° C. and 1600° C., increasing the pressure to between about 4,000 psi and 10,000 psi, and maintaining said increased temperature and pressure for between about one-half hour and 4 hours.
Claim 20
Dependent Claim
52 words
The method of claim 18 further comprising the step of oxidizing the resulting hot pressed ceramic, said step of oxidizing including heating said ceramic in an oxygen-containing atmosphere for between about 1 and 20 hours at a temperature of between about 800° C. and 1200° C. so as to remove any discoloration.
References Cited (Backward Citations)
GB1118800A
Cited
US3545987A
Cited
US3640887A
Cited
US3878280A
Cited
US3666676A
Cited
GB1364008A
Cited
US3842012A
Cited
US4147744A
Cited
US4242221A
Cited
US4224524A
Cited
US4225653A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-21 | 1988-02-20 | 1988-08-21 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-21 | 1992-02-20 | 1992-08-21 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-21 | 1996-02-20 | 1996-08-21 | $7700.00 | Window Closed / Lapsed |