Humidity sensor made of metal oxide
Assignee: JAPAN ELECTRONIC INDUSTRY DEVELOPMENT ASSOCIATION 5-8 3-OCHOME SHIBAKOEN MINATO-KU TOKYO JAPAN A CORP OF JAPAN
•
Filing: 1982-01-25
•
Granted: 1984-08-07
•
Expires: 2002-01-25
Abstract
Abstract A sintered body for a humidity sensor is formed by baking a blend at 1,000° to 1,400° C., the blend comprising ZnO, Cr 2 O 3 , V 2 O 5 and M 2 O where M 2 O is at least one metal oxide selected from Li 2 O, Na 2 O and K 2 O. A pair of electrodes are each attached to the corresponding surface of the sintered body to obtain a humidity sensor of metal oxide which is relatively low in its resistive value and stable in its aging characteristic.
Inventors
- 👤 Yuji Yokomizo
- 👤 Keiji Yuuki
- 👤 Naoe Watanabe
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-09 02:37
CPC Classifications
G; G01; G01N; G01N27/00; G01N27/02; G01N27/04; G01N27/12; G01N27/121
Claims Analysis
Total Claims: 8
Claim 1
Independent Claim
100 words
A metal oxide humidity sensor comprising: a sintered body having an average particle size less than 2 μm and comprising 69.95 to 30 mol % of ZnO, 29.95 to 50 mol % or Cr 2 O 3 , 0.05 to 10 mol % of V 2 O 5 and 0.05 to 10 mol % of M 2 O where M 2 O is at least one metal oxide selected from the group consisting of Li 2 O, Na 2 O and K 2 O; and a pair of electrodes each electrode being attached to a surface of said sintered body.
Claim 2
Dependent Claim
100 words
A metal oxide humidity sensor comprising: a sintered body having an average particle size less than 2 μm and comprising 69.95 to 30 mol % of ZnO, 29.95 to 50 mol % or Cr 2 O 3 , 0.05 to 10 mol % of V 2 O 5 and 0.05 to 10 mol % of M 2 O where M 2 O is at least one metal oxide selected from the group consisting of Li 2 O, Na 2 O and K 2 O; and a pair of electrodes each electrode being attached to a surface of said sintered body.
Claim 3
Dependent Claim
50 words
A humidity sensor according to claim 1, in which said sintered body is formed by a sintering step following two steps of (1) prebaking a blend of said composition and crushing it to powder and (2) blending the powder with a binder and shaping the blend into a shaped mass.
Claim 4
Dependent Claim
29 words
A humidity sensor according to claim 2, in which said prebaking step is carried out by heating a blend of said composition at 850° C. over about 2 hours.
Claim 5
Dependent Claim
34 words
A humidity sensor according to claim 2, in which said shaping step is carried out by subjecting said blend including said binder to a pressure of 100 kg/cm 2 to 1.2 ton/cm 2 .
Claim 6
Dependent Claim
27 words
A humidity sensor according to claim 2, in which said shaped mass is sintered at a temperature of 1,000° to 1,400° C. for 1 to 5 hours.
Claim 7
Dependent Claim
38 words
A humidity sensor according to claim 1, in which said pair of electrodes are formed by coating, and baking, a metal paste selected from a gold paste and platinum paste onto both the surfaces of said sintered body.
Claim 8
Dependent Claim
40 words
A humidity sensor according to claim 1, in which said pair of electrodes are formed by coating, and baking, an oxide paste selected from the group consisting of ruthenium oxide and indium oxide, to both surfaces of said sintered body.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-07 | 1988-02-06 | 1988-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-07 | 1992-02-06 | 1992-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-07 | 1996-02-06 | 1996-08-07 | $7700.00 | Window Closed / Lapsed |