Polymer hydrogenation process
Assignee: Polysar Ltd
•
Filing: 1983-10-11
•
Granted: 1984-08-07
•
Expires: 2003-10-11
Abstract
Abstract A process is provided for the selective hydrogenation of the carbon-carbon double bonds in a copolymer of a conjugated diene and one or more copolymerizable monomers comprising hydrogenating the copolymer in the presence of (i) a monovalent rhodium hydride complex catalyst, (ii) a ligand compound, and (iii) a solvent for the copolymer, catalyst and ligand compound.
Inventors
- 👤 Gary L. Rempel
- 👤 Hormoz Azizian
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 22:57
CPC Classifications
C; C08; C08C; C08C19/00; C08C19/02
Claims Analysis
Total Claims: 21
Claim 1
Independent Claim
266 words
An improved process for the selective hydrogenation of the carbon-carbon double bonds in a copolymer of a conjugated diene and one or more copolymerizable monomers which comprises hydrogenating said copolymer at a temperature of from about 40° to about 170° C. and at a pressure of hydrogen of from about 0.05 to about 7 MPa, the improvement being that said hydrogenation is carried out in the presence of (i) from about 0.05 to about 20 percent by weight of a catalyst which is a monovalent rhodium hydride complex of the general formula RhH(L 1 ) x in which x is 3 or 4 and L 1 is a first ligand compound, (ii) from about 1 to about 25 percent by weight of a second ligand compound L 2 and (iii) a solvent for said copolymer, said (i) and said (ii), the weights of said (i) and (ii) being based on the weight of said copolymer and the weight ratio of (ii):(i) being from about 0.1:1 to about 20:1, wherein L 1 and L 2 may be the same or different ligand compounds which when x is 4, are phosphorus compounds selected from 5-phenyl-5H-dibenzophosphole and compounds of the formula PR 1 R 2 R 3 and when x is 3, are arsenic or antimony compounds of the formula MR 1 R 2 R 3 wherein M is arsenic or antimony, and wherein R 1 , R 2 and R 3 may be the same or different and are selected from CH 3 , C 2 H 5 , C 6-10 aryl groups and C 7-12 aralkyl groups.
Claim 2
Dependent Claim
266 words
An improved process for the selective hydrogenation of the carbon-carbon double bonds in a copolymer of a conjugated diene and one or more copolymerizable monomers which comprises hydrogenating said copolymer at a temperature of from about 40° to about 170° C. and at a pressure of hydrogen of from about 0.05 to about 7 MPa, the improvement being that said hydrogenation is carried out in the presence of (i) from about 0.05 to about 20 percent by weight of a catalyst which is a monovalent rhodium hydride complex of the general formula RhH(L 1 ) x in which x is 3 or 4 and L 1 is a first ligand compound, (ii) from about 1 to about 25 percent by weight of a second ligand compound L 2 and (iii) a solvent for said copolymer, said (i) and said (ii), the weights of said (i) and (ii) being based on the weight of said copolymer and the weight ratio of (ii):(i) being from about 0.1:1 to about 20:1, wherein L 1 and L 2 may be the same or different ligand compounds which when x is 4, are phosphorus compounds selected from 5-phenyl-5H-dibenzophosphole and compounds of the formula PR 1 R 2 R 3 and when x is 3, are arsenic or antimony compounds of the formula MR 1 R 2 R 3 wherein M is arsenic or antimony, and wherein R 1 , R 2 and R 3 may be the same or different and are selected from CH 3 , C 2 H 5 , C 6-10 aryl groups and C 7-12 aralkyl groups.
Claim 3
Dependent Claim
37 words
The process according to claim 1 which is a homogeneous solution hydrogenation process wherein said hydrogenation is carried out with said copolymer, said catalyst (i) and said second ligand compound (ii) being dissolved in said solvent (iii).
Claim 4
Dependent Claim
54 words
The process according to claim 2 wherein said solvent (iii) is selected from the group consisting of chlorobenzene, benzene, toluene, xylene, acetone, 1,1,2-trichloroethane, and mixtures thereof and wherein the concentration of said copolymer in the solution is from about 1 to about 20 percent by weight based on the total weight of said solution.
Claim 5
Dependent Claim
26 words
The process according to claim 2 wherein said L 1 and said L 2 are the same and are selected from trimethylphosphine, triethylphosphine, triphenylphosphine and triphenylarsine.
Claim 6
Dependent Claim
16 words
The process according to claim 4 wherein said L 1 and said L 2 are triphenylphosphine.
Claim 7
Dependent Claim
54 words
The process according to claim 2 wherein the amount of said second ligand compound (ii) is from about 3 to about 20 percent by weight, the amount of said catalyst (i) is from about 0.1 to about 15 percent by weight, and the weight ratio of (ii):(i) is from about 0.6:1 to about 10:1.
Claim 8
Dependent Claim
30 words
The process according to claim 2 wherein the pressure of hydrogen is from about 0.05 to about 3 MPa and the temperature is from about 80° to about 160° C.
Claim 9
Dependent Claim
40 words
The process according to claim 1 wherein said copolymer is hydrogenated in the form of an aqueous emulsion containing from about 3 to about 40 percent by dry weight of said copolymer based on the total weight of said emulsion.
Claim 10
Dependent Claim
57 words
The process according to claim 8 wherein said solvent (iii) is selected from mixtures of toluene with acetone and of chlorobenzene with acetone and wherein the amount of (iii) is such that the dry weight of said copolymer is from about 1 to about 20 percent based on the total weight of said copolymer and said (iii).
Claim 11
Dependent Claim
26 words
The process according to claim 8 wherein said L 1 and said L 2 are the same and are selected from trimethylphosphine, triethylphosphine, triphenylphosphine and triphenylarsine.
Claim 12
Dependent Claim
16 words
The process according to claim 10 wherein said L 1 and said L 2 are triphenylphosphine.
Claim 13
Dependent Claim
54 words
The process according to claim 8 wherein the amount of said second ligand compound (ii) is from about 10 to about 20 percent by weight, the amount of said catalyst (i) is from about 1 to about 2 percent by weight, and the weight ratio of (ii):(i) is from about 5:1 to about 15:1.
Claim 14
Dependent Claim
30 words
The process according to claim 8 wherein the pressure of hydrogen is from about 1.4 to about 4 MPa and the temperature is from about 80° to about 120° C.
Claim 15
Dependent Claim
73 words
The process according to claim 2 wherein said copolymer is selected from the group consisting of butadiene-(meth)acrylonitrile copolymers, isoprene-(meth)acrylonitrile copolymers, copolymers of butadiene with (meth)acrylonitrile and one or more monomers selected from itaconic acid, fumaric acid, (meth)acrylic acid, and maleic acid, and AB, ABA and ABCBA block copolymers wherein A may be one of butadiene or isoprene, B may be one of styrene or α-methylstyrene, and C may be a coupling agent residue.
Claim 16
Dependent Claim
73 words
The process according to claim 8 wherein said copolymer is selected from the group consisting of butadiene-(meth)acrylonitrile copolymers, isoprene-(meth)acrylonitrile copolymers, copolymers of butadiene with (meth)acrylonitrile and one or more monomers selected from itaconic acid, fumaric acid, (meth)acrylic acid, and maleic acid, and AB, ABA and ABCBA block copolymers wherein A may be one of butadiene or isoprene, B may be one of styrene or α-methylstyrene, and C may be a coupling agent residue.
Claim 17
Dependent Claim
21 words
The process according to claim 1 wherein from about 50 to about 99.95 percent of said carbon-carbon double bonds are hydrogenated.
Claim 18
Dependent Claim
29 words
The process according to claim 14 wherein said copolymer is a butadiene-acrylonitrile copolymer and wherein from about 95 to about 99.95 percent of said carbon-carbon double bonds are hydrogenated.
Claim 19
Dependent Claim
29 words
The process according to claim 15 wherein said copolymer is a butadiene-acrylonitrile copolymer and wherein from about 95 to about 99.95 percent of said carbon-carbon double bonds are hydrogenated.
Claim 20
Dependent Claim
29 words
The process according to claim 14 wherein said copolymer is a block copolymer and wherein from about 95 to about 99.95 percent of said carbon-carbon double bonds are hydrogenated.
Claim 21
Dependent Claim
29 words
The process according to claim 15 wherein said copolymer is a block copolymer and wherein from about 95 to about 99.95 percent of said carbon-carbon double bonds are hydrogenated.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-07 | 1988-02-06 | 1988-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-07 | 1992-02-06 | 1992-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-07 | 1996-02-06 | 1996-08-07 | $7700.00 | Window Closed / Lapsed |