Metal diffusion
Assignee: Alloy Surfaces Co Inc
•
Filing: 1981-03-10
•
Granted: 1984-08-07
•
Expires: 2001-03-10
Abstract
Abstract Very good masking of pack diffusion aluminizing on any metal to keep portions from being diffusion coated, is effected by localized coating the lowest layer of which is depletion-reducing masking powder that can have same composition as substrates, mixed with non-contaminating film-former such as acrylic resin. The upper coating layer can be of non-contaminating particles like nickel of Cr 2 O 3 that upon aluminizing or chromizing become coherently held together to form a secure sheath. Such sheath can also be used for holding localized diffusion-coating layer in place. Film-former can be dissolved in volatile solvent, preferably methyl chloroform, in which masking powder or sheath-forming powder is suspended. Chromizing can be performed before aluminizing for greater effects. Aluminized cases are stripped from superalloys by alternating dips in fluoride-containing and fluoride-free aqueous nitric acid.
Inventors
- 👤 Alfonso L. Baldi
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-05 00:03
CPC Classifications
C; C23; C23C; C23C10/00; C23C10/04; C23C10/02; C23C10/28; C23C10/34; C23C10/58; H; H05; H05K; H05K2201/00; H05K2201/02; H05K2201/0203; H05K2201/0206; H05K2201/0209; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24802; Y10T428/24851; Y10T428/24893; Y10T428/24909; Y10T428/24917
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
49 words
In the method of applying a diffusion coating to a limited portion of the surface of a substrate, the improvement according to which the limited surface portion is delineated by applying a delineating coating and then holding the delineating coating in place by applying over it a sheath-forming layer.
Claim 2
Dependent Claim
49 words
In the method of applying a diffusion coating to a limited portion of the surface of a substrate, the improvement according to which the limited surface portion is delineated by applying a delineating coating and then holding the delineating coating in place by applying over it a sheath-forming layer.
Claim 3
Dependent Claim
22 words
The combination of claim 1 in which the delineating coating is a coating that causes diffusion metallizing on the surface it coats.
Claim 4
Dependent Claim
23 words
The combination of claim 1 in which the delineating coating is a masking coating that inhibits diffusion metallizing on the surface it coats.
Claim 5
Dependent Claim
26 words
The combination of claim 1 in which the sheath-forming layer is essentially powdered nickel and a resin binder that is driven off at diffusion coating temperatures.
Claim 6
Dependent Claim
40 words
The combination of claim 4 in which the sheath-forming layer is deposited from dispersion in a chloroform solvent in which the binder is dissolved and which also contains a dispersing aid that helps disperse the powdered nickel in the solution.
Claim 7
Dependent Claim
20 words
The combination of claim 1 in which the coating held in place by the sheath-forming layer, contains inert refractory diluent.
Claim 8
Dependent Claim
74 words
A metal workpiece having a portion of its surface covered with an adherent layer of a resin-binder-containing first powder mixture, that layer being in turn covered with an adherent layer of a second powder mixture, the first mixture being one that has a selective diffusion coating effect on the surface it covers, and the second mixture being one that is converted by a diffusion coating treatment to a coherent sheath encasing the first mixture.
Claim 9
Dependent Claim
74 words
A metal workpiece having a portion of its surface covered with an adherent layer of a resin-binder-containing first powder mixture, that layer being in turn covered with an adherent layer of a second powder mixture, the first mixture being one that has a selective diffusion coating effect on the surface it covers, and the second mixture being one that is converted by a diffusion coating treatment to a coherent sheath encasing the first mixture.
Claim 10
Dependent Claim
28 words
The combination of claim 1 in which the pre-coating includes a resin binder that adherently holds the pre-coating on the substrate until the diffusion coating heat is applied.
Claim 11
Dependent Claim
34 words
The combination of claim 1 in which the delineating coating or the sheath-forming coating, or both, includes a resin binder that adherently holds them on the substrate until the diffusion coating heat is applied.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-08-07 | 1988-02-06 | 1988-08-07 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-08-07 | 1992-02-06 | 1992-08-07 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-08-07 | 1996-02-06 | 1996-08-07 | $7700.00 | Window Closed / Lapsed |