Coatings prepared from prepolymers and aromatic diamines having at least one alkyl substituent in an ortho position to each amino group

Claim 2

A process for the production of elastic coatings by coating any substrates with a solvent-free or low solvent coating composition, containing, as binder, a two-component system of (i) a polyisocyanate component and (ii) a hardener component, characterized in that (i) has an isocyanate content of from 1 to 20% by weight and comprises of at least one prepolymer containing free isocyanate groups based on 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane and one or more polyalkylene ether polyols having an (average) hydroxyl functionality of from 2 to 3, (ii) comprises to an extent of at least 50 equivalent percent of polyamines selected from the group consisting of (a) at least one diprimary aromatic diamine having at least one alkyl substituent with 2 to 3 carbon atoms in an ortho-position to each amino group and optionally also methyl substituents in further ortho-positions to the amino groups, (b) reaction products of such diamines with a sub-equivalent amount of either a prepolymer containing free isocyanate groups based on an organic diisocyanate having a molecular weight of from 168 to 300 and at least one polyalkylene ether polyol having an (average) hydroxyl functionality of 2 to 3 or of a mixture of such a prepolymer with up to 500 isocyanate equivalent percent, based on the isocyanate groups of said prepolymer, of said diisocyanate and (c) mixtures of (a) and (b) and to an extent of up to 50 equivalent percent of dihydric or trihydric alcohols having primary hydroxyl groups and in that (i) and (ii) being used in quantitative proportions corresponding to an NCO/NH 2 equivalent ratio in the range of from 0,5:1 to 1,5:1.

Claim 3

The process of claim 1, further characterized in that from 0.1 to 5% by weight, based on the sum of (i)+(ii), of a carboxylic acid anhydride are incorporated in said coating composition.

Claim 4

The process of claim 1 wherein said low solvent coating composition contains up to 15% of lacquer solvents, said percent being relative to the weight of the coating.

Claim 5

A process for coating moist concrete comprising preparing a mixture of (i) a polyisocyanate component and (ii) a hardener component wherein (i) has an isocyanate content of from 1 to 20% by weight and comprises of at least one prepolymer containing free isocyanate groups based on 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane and one or more polyalkylene ether polyols having an (average) hydroxyl functionality of from 2 to 3, and wherein (ii) comprises to an extent of at least 50 equivalent percent of polyamines selected from the group consisting of (a) at least one diprimary aromatic diamine having at least one alkyl substituent with 2 to 3 carbon atoms in an ortho-position to each amino group and optionally also methyl substituents in further ortho-positions to the amino groups, (b) reaction products of such diamines with a sub-equivalent amount of either a prepolymer containing free isocyanate groups based on an organic diisocyanate having a molecular weight of from 168 to 300 and at least one polyalkylene ether polyol having an (average) hydroxyl functionality of 2 to 3 or of a mixture of such a prepolymer with up to 500 isocyanate equivalent percent, based on the isocyanate groups of said prepolymer, of said diisocyanate and (c) mixtures of (a) and (b) and to an extent of up to 50 equivalent percent of dihydric or trihydric alcohols having primary hydroxyl groups and wherein (i) and (ii) are used in quantitative proportions corresponding to an NCO/NH 2 equivalent ratio in the range of from 0.5:1 to 1.5:1, and applying said mixture to the moist concrete surface before it has reacted sufficiently to have lost its fluidity.

Claim 6

A process for coating moist concrete comprising preparing a mixture of (i) a polyisocyanate component and (ii) a hardener component wherein (i) has an isocyanate content of from 1 to 20% by weight and comprises of at least one prepolymer containing free isocyanate groups based on 1-isocyanato-3,3,5-trimethyl-5-isocyanatomethylcyclohexane and one or more polyalkylene ether polyols having an (average) hydroxyl functionality of from 2 to 3, and wherein (ii) comprises to an extent of at least 50 equivalent percent of polyamines selected from the group consisting of (a) at least one diprimary aromatic diamine having at least one alkyl substituent with 2 to 3 carbon atoms in an ortho-position to each amino group and optionally also methyl substituents in further ortho-positions to the amino groups, (b) reaction products of such diamines with a sub-equivalent amount of either a prepolymer containing free isocyanate groups based on an organic diisocyanate having a molecular weight of from 168 to 300 and at least one polyalkylene ether polyol having an (average) hydroxyl functionality of 2 to 3 or of a mixture of such a prepolymer with up to 500 isocyanate equivalent percent, based on the isocyanate groups of said prepolymer, of said diisocyanate and (c) mixtures of (a) and (b) and to an extent of up to 50 equivalent percent of dihydric or trihydric alcohols having primary hydroxyl groups and wherein (i) and (ii) are used in quantitative proportions corresponding to an NCO/NH 2 equivalent ratio in the range of from 0.5:1 to 1.5:1, and applying said mixture to the moist concrete surface before it has reacted sufficiently to have lost its fluidity.