Mixture of a thermoplastic polymer of an alkyl methacrylate and a graft polymer of methyl methacrylate onto crosslinked alkyl acrylate rubber
Assignee: Bayer AG
•
Filing: 1983-03-09
•
Granted: 1984-07-24
•
Expires: 2003-03-09
Abstract
Abstract The present invention relates to mixtures comprising (a) thermoplastic aromatic polycarbonates having Mw (weight average molecular weight) of 10,000 to 200,000, preferably 20,000 to 80,000 (determined by measuring the relative viscosity ηrel in CH 2 Cl 2 at 25° C. and a concentration of 0,5 g per 100 ml CH 2 Cl 2 (b) thermoplastic polymers of C 1 -C 4 --alkyl methacrylates having Mw (weight average moleculr weight) of 10,000 to 1,000,000 (measured in dimethylformamide at 25° C.) and (c) particulate graft polymers of methyl methacrylate onto a particulate, highly crosslinked alkyl acrylate-rubber which can optionally also contain a crosslinked diene rubber as an inner core, as well as to thermoplastic moulding compositions based on thermoplastic ABS resins or thermoplastic SAN resins which contain the three-component mixture (a)+(b)+(c).
Inventors
- 👤 Christian Lindner
- 👤 Karl-Heinz Ott
- 👤 Horst Peters
- 👤 Josef Buekers
- 👤 Dieter Neuray
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 05:24
CPC Classifications
C; C08; C08L; C08L69/00; Y; Y10; Y10S; Y10S525/00; Y10S525/902
Claims Analysis
Total Claims: 9
Claim 1
Independent Claim
167 words
Mixtures comprising (a) homopolycarbonates and copolycarbonates which are based on one or more diphenols selected from hydroquinone, resorcinol, dihydroxydiphenyls, bis-(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl) sulphides, bis-(hydroxyphenyl) ethers, bis-(hydroxyphenyl) ketones, bis-(hydroxyphenyl) sulphoxides, bis-(hydroxyphenyl) sulphones, α,α-bis-(hydroxyphenyl)-diisopropyl-benzenes, and compounds thereof which are halogenated in the nucleus, said polycarbonate having a weight average molecular weight of 10,000 to 200,000; (b) thermoplastic polymers of C 1 to C 4 -alkyl methacrylates having a weight average molecular weight of 10,000 to 1,000,000 measured in dimethylformamide at 25° C.; (c) particulate graft polymers of methyl methacrylate onto a particulate, highly crosslinked alkyl acrylate rubber wherein the weight ratio of grafted monomers:alkylate rubber base is between 20:80 and 80:20; characterized in that component (a) is present in amounts of 75 to 45 parts by weight, component (b) is present in amounts from 10 to 40 parts by weight and component (c) is present in amounts from 15 to 45 parts by weight, with the proviso that the sum of (a), (b) and (c) parts is 100 parts.
Claim 2
Dependent Claim
167 words
Mixtures comprising (a) homopolycarbonates and copolycarbonates which are based on one or more diphenols selected from hydroquinone, resorcinol, dihydroxydiphenyls, bis-(hydroxyphenyl)-alkanes, bis-(hydroxyphenyl)-cycloalkanes, bis-(hydroxyphenyl) sulphides, bis-(hydroxyphenyl) ethers, bis-(hydroxyphenyl) ketones, bis-(hydroxyphenyl) sulphoxides, bis-(hydroxyphenyl) sulphones, α,α-bis-(hydroxyphenyl)-diisopropyl-benzenes, and compounds thereof which are halogenated in the nucleus, said polycarbonate having a weight average molecular weight of 10,000 to 200,000; (b) thermoplastic polymers of C 1 to C 4 -alkyl methacrylates having a weight average molecular weight of 10,000 to 1,000,000 measured in dimethylformamide at 25° C.; (c) particulate graft polymers of methyl methacrylate onto a particulate, highly crosslinked alkyl acrylate rubber wherein the weight ratio of grafted monomers:alkylate rubber base is between 20:80 and 80:20; characterized in that component (a) is present in amounts of 75 to 45 parts by weight, component (b) is present in amounts from 10 to 40 parts by weight and component (c) is present in amounts from 15 to 45 parts by weight, with the proviso that the sum of (a), (b) and (c) parts is 100 parts.
Claim 3
Dependent Claim
46 words
Mixtures according to claim 1 characterised in that the particulate graft polymers (c) are prepared by polymerisation of 100 to 90.5% by weight of methyl methacrylate and 0 to 9.5% by weight of other, ethylenically unsaturated copolymerisable monomers, relative to the total weight of grafted monomers.
Claim 4
Dependent Claim
23 words
Mixtures according to claim 1 wherein component (c) further contains a crosslinked diene rubber as an inner core of the alkyl acrylate rubber.
Claim 5
Dependent Claim
49 words
Mixtures according to claim 3, characterised in that the weight ratio of the diene rubber core to the acrylate rubber shell is from 0.1:99.9 to 10:90, and the proportion of the second shell in the total graft polymer (c) can be from 30% by weight to 70% by weight.
Claim 6
Dependent Claim
28 words
Thermoplastic moulding compositions based on thermoplastic ABS resins or thermoplastic SAN resins, characterised in that they contain at least 60% by weight of the mixtures from claim 1.
Claim 7
Dependent Claim
73 words
Mixtures according to claim 1 wherein the diphenol on which the polycarbonate of component (a) is of the formula ##STR3## wherein each R is identical or different and is H, chloro or bromo and wherein X is a covalent bond, alkylene having 1 to 8 carbon atoms, alkylidene having 2 to 8 carbon atoms, cycloalkylene having 5 to 15 carbon atoms, cycloalkylidene having 5 to 15 carbon atoms, --SO 2 -- or ##STR4##
Claim 8
Dependent Claim
21 words
Mixtures according to claims 1 or 6 wherein component (b) is a copolymer or homopolymer of methyl methacrylate and ethyl methacrylate.
Claim 9
Dependent Claim
24 words
Mixtures according to claims 1 or 6 wherein the weight ratio of grafted monomers:alkylate rubber base in component (c) is between 40:60 and 60:40.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-24 | 1988-01-23 | 1988-07-24 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-24 | 1992-01-23 | 1992-07-24 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-24 | 1996-01-23 | 1996-07-24 | $7700.00 | Window Closed / Lapsed |