Method of forming coatings, coatings so formed and articles coated thereby
Assignee: AHI Operations Ltd
•
Filing: 1983-07-22
•
Granted: 1984-07-17
•
Expires: 2003-07-22
Abstract
Abstract A method of coating articles, a coating and a coated article wherein a bitumen primer layer is applied to a base sheet material and while the bitumen primer layer is still wet a layer of a barrier material of a consistency, composition and thickness is applied to the primer layer such that the bitumen primer layer does not bleed through the barrier layer and the barrier layer adheres to the bitumen primer layer. A coating of stone chips is then applied to the barrier layer in a manner such that the stone chips are partially embedded at least in the barrier layer so that the stone chips are held in position on curing of the bitumen primer and barrier layer but the stone chips are not completely covered by the barrier layer.
Inventors
- 👤 Graham T. Jones
- 👤 Warren S. Dow
- 👤 Geoffrey L. Wearne
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-02 13:26
CPC Classifications
E; E04; E04D; E04D13/00; E04D13/002; B; B05; B05D; B05D5/00; B05D5/02; B05D7/00; B05D7/50; B05D7/52; B05D7/54; B05D7/542; D; D06; D06N; D06N5/00; E04D3/00; E04D3/24; E04D3/30; E04D5/00; E04D5/10; E04D7/00; E04D7/005; Y; Y10; Y10T; Y10T428/00; Y10T428/24; Y10T428/24355; Y10T428/24364; Y10T428/24372; Y10T428/24421; Y10T428/2443; Y10T428/25; Y10T428/259; Y10T428/31504; Y10T428/31815
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
170 words
A coated article comprising a base sheet material comprising an uncoated galvanized sheet metal tile and a composite coating comprising a bitumen primer layer applied as an emulsion to said base sheet material, an ultraviolet opaque barrier layer applied to said bitumen primer layer while said bitumen primer layer has a water content of between 20% and 40% by weight, said barrier material being of a consistency, composition and thickness such that the bitumen primer layer does not bleed through the barrier layer and the barrier layer adheres to the bitumen primer layer and a coating of stone chips applied to the barrier layer in a manner such that the stone chips are partially embedded at least in the barrier layer, said barrier layer having a viscosity and surface tension which permits capillarization by said barrier layer around said chips to occur so that the stone chips are held in position on curing of the bitumen primer layer but the stone chips are not completely covered by the barrier layer.
Claim 2
Dependent Claim
170 words
A coated article comprising a base sheet material comprising an uncoated galvanized sheet metal tile and a composite coating comprising a bitumen primer layer applied as an emulsion to said base sheet material, an ultraviolet opaque barrier layer applied to said bitumen primer layer while said bitumen primer layer has a water content of between 20% and 40% by weight, said barrier material being of a consistency, composition and thickness such that the bitumen primer layer does not bleed through the barrier layer and the barrier layer adheres to the bitumen primer layer and a coating of stone chips applied to the barrier layer in a manner such that the stone chips are partially embedded at least in the barrier layer, said barrier layer having a viscosity and surface tension which permits capillarization by said barrier layer around said chips to occur so that the stone chips are held in position on curing of the bitumen primer layer but the stone chips are not completely covered by the barrier layer.
Claim 3
Dependent Claim
14 words
An article as claimed in claim 1 wherein said article comprises a roofing tile.
Claim 4
Dependent Claim
22 words
An article as claimed in claim 1 wherein the composite coating is finally covered with a layer of transparent or translucent material.
Claim 5
Dependent Claim
44 words
A coated article as claimed in claim 1, wherein said barrier layer is formed from a material other than the material which forms the bitumen primer layer and is applied as an emulsion having a water content of between 40% and 50% by weight.
Claim 6
Independent Claim
165 words
A method of coating articles, said method comprising the steps of applying to a base sheet material comprising an uncoated galvanized sheet metal tile, a bitumen primer layer as an emulsion and while the bitumen primer layer has a water content of between 20% and 40% by weight applying a layer of an ultraviolet-opaque barrier material of a consistency, composition and thickness such that the bitumen primer layer does not bleed through the barrier layer and the barrier layer adheres to the bitumen primer layer and applying a coating of stone chips to the barrier layer in a manner such that the stone chips are partially embedded at least in the barrier layer, said barrier layer having a viscosity and surface tension which permits capillarization by said barrier layer around said chips to occur so that the stone chips are held in position on curing of the bitumen primer layer and barrier layer but the stone chips are not completely covered by the barrier layer.
Claim 7
Independent Claim
165 words
A method of coating articles, said method comprising the steps of applying to a base sheet material comprising an uncoated galvanized sheet metal tile, a bitumen primer layer as an emulsion and while the bitumen primer layer has a water content of between 20% and 40% by weight applying a layer of an ultraviolet-opaque barrier material of a consistency, composition and thickness such that the bitumen primer layer does not bleed through the barrier layer and the barrier layer adheres to the bitumen primer layer and applying a coating of stone chips to the barrier layer in a manner such that the stone chips are partially embedded at least in the barrier layer, said barrier layer having a viscosity and surface tension which permits capillarization by said barrier layer around said chips to occur so that the stone chips are held in position on curing of the bitumen primer layer and barrier layer but the stone chips are not completely covered by the barrier layer.
Claim 8
Dependent Claim
19 words
A method as claimed in claim 5 wherein said bitumen primer layer comprises a polymer modified bitumen emulsion layer.
Claim 9
Dependent Claim
15 words
A method as claimed in claim 5 wherein said barrier layer comprises an acrylic emulsion.
Claim 10
Dependent Claim
43 words
A method as claimed in claim 5, wherein said barrier layer is formed from a material other than the material which forms the bitumen primer layer and is applied as an emulsion having a water content of between 40% and 50% by weight.
References Cited (Backward Citations)
US4267221A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-17 | 1988-01-16 | 1988-07-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-17 | 1992-01-16 | 1992-07-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-17 | 1996-01-16 | 1996-07-17 | $7700.00 | Window Closed / Lapsed |