US4460623A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of varistor capacitance reduction by boron diffusion
Assignee: General Electric Co
•
Filing: 1981-11-02
•
Granted: 1984-07-17
•
Expires: 2001-11-02
Abstract
Abstract Diffusing boron-containing glass, such as bismuth borosilicate glass, into conventional sintered zinc oxide based varistor material reduces varistor material intrinsic capacitance. In the method, a layer of glass powder is screen-printed, painted, or otherwise applied to the varistor material surface. Upon firing, a portion of the glass diffuses into the material, while the remainder creates an insulating layer on the varistor material surface which may be removed by grinding. The varistor material may then be annealed to restore varistor electrical properties which may have been degraded by mechanical damage caused by the grinding. Device electrodes are attached by conventional means.
Inventors
- 👤 Lionel M. Levinson
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-08 17:10
CPC Classifications
H; H01; H01C; H01C7/00; H01C7/10; H01C7/105; H01C7/108; H01C7/112; H01C7/102
Claims Analysis
Total Claims: 7
Claim 1
Independent Claim
99 words
A method of decreasing the intrinsic capacitance of sintered ZnO based varistor material comprising the steps of: applying a boron-containing glass which is substantially free of electrically conductive material to a surface of said sintered ZnO based varistor material; heating said ZnO based varistor material having said boron-containing glass applied thereto at a temperature of between about 500° C. and about 1200° C. to diffuse a sufficient amount of said boron-containing glass into said ZnO based varistor material to effect a decrease in the intrinsic capacitance thereof; and removing undiffused boron-containing glass from said surface, after said heating step.
Claim 2
Independent Claim
99 words
A method of decreasing the intrinsic capacitance of sintered ZnO based varistor material comprising the steps of: applying a boron-containing glass which is substantially free of electrically conductive material to a surface of said sintered ZnO based varistor material; heating said ZnO based varistor material having said boron-containing glass applied thereto at a temperature of between about 500° C. and about 1200° C. to diffuse a sufficient amount of said boron-containing glass into said ZnO based varistor material to effect a decrease in the intrinsic capacitance thereof; and removing undiffused boron-containing glass from said surface, after said heating step.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein, prior to said step of applying said powdered boron-containing glass, said varistor material surface is ground flat.
Claim 4
Dependent Claim
12 words
The method of claim 2 wherein said glass comprises bismuth borosilicate glass.
Claim 5
Dependent Claim
76 words
The method of claim 3 wherein said ZnO varistor comprises about 1.0 mole percent each of Bi 2 O 3 and NiO, about 0.5 mole percent each of Co 2 O 3 , MnO 2 , and Cr 2 O 3 , about 0.1 mole percent each of SiO 2 and BaCO 3 , about 0.2 mole percent H 3 BO 3 , about 5 mole percent Sb 2 O 3 , the remainder being ZnO.
Claim 6
Independent Claim
103 words
A method of decreasing the intrinsic capacitance of sintered ZnO based varistor material comprising the steps of: applying a boron-containing compound which is substantially free of electrically conductive material to a surface of said sintered ZnO based material; heating said sintered ZnO based varistor material having said boron-containing compound applied thereto at a temperature of between about 500° C. and about 1200° C. to diffuse sufficient boron from said compound into said sintered ZnO based material to a sufficient predetermined depth therein to effect a decrease in the intrinsic capacitance thereof; and removing undiffused boron-containing compound from said surface, after said heating step.
Claim 7
Independent Claim
103 words
A method of decreasing the intrinsic capacitance of sintered ZnO based varistor material comprising the steps of: applying a boron-containing compound which is substantially free of electrically conductive material to a surface of said sintered ZnO based material; heating said sintered ZnO based varistor material having said boron-containing compound applied thereto at a temperature of between about 500° C. and about 1200° C. to diffuse sufficient boron from said compound into said sintered ZnO based material to a sufficient predetermined depth therein to effect a decrease in the intrinsic capacitance thereof; and removing undiffused boron-containing compound from said surface, after said heating step.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-17 | 1988-01-16 | 1988-07-17 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-17 | 1992-01-16 | 1992-07-17 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-17 | 1996-01-16 | 1996-07-17 | $7700.00 | Window Closed / Lapsed |