Nitrocellulose composition and process for producing the same

Claim 2

A nitrocellulose composition in the form of chips, which composition consists essentially of from 50 to 80 wt.% of nitrocellulose, less than 1 wt%. of water, and the balance is essentially a member selected from the group consisting of (1) a first organic solvent capable of dissolving nitrocellulose and polyurethane resin but which is nonreactive with isocyanate compounds, (2) a mixture of said first organic solvent with a second organic solvent which is miscible with said first organic solvent but which is immiscible with water, (3) a mixture of (1) and a binder resin for binding magnetic powder to a plastic film to make a magnetic tape, and (4) a mixture of (2) with a binder resin for binding magnetic powder to a plastic film to make a magnetic tape.

Claim 3

A nitrocellulose composition as claimed in claim 1, wherein said member is selected from the group consisting of (2) and (4), said first organic solvent is selected from the group consisting of acetate esters, ketones, and lactones, and said second organic solvent is a liquid hydrocarbon having a boiling point in the range of 80° C. to 150° C.

Claim 4

A nitrocellulose composition as claimed in claim 2, wherein said first organic solvent is selected from the group consisting of ethyl acetate, propyl acetate, butyl acetate, ethylene glycol monomethyl ether acetate, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, and gamma-butyrolactone, and said second organic solvent is toluene or xylene.

Claim 5

A nitrocellulose composition as claimed in claim 1, wherein said member is selected from the group consisting of (3) and (4), and said binder resin is polyurethane resin, said first organic solvent is selected from the group consisting of acetate esters, ketones, and lactones, and said second organic solvent is a liquid hydrocarbon having a boiling point in the range of 80° C. to 150° C.

Claim 6

A nitrocellulose composition as claimed in claim 4, wherein said first organic solvent is selected from the group consisting of ethyl acetate, propyl acetate, butyl acetate, ethylene glycol monomethyl ether acetate, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, and gamma-butyrolactone, and said second organic solvent is toluene or xylene.

Claim 7

A nitrocellulose composition as claimed in claim 1, wherein said member is (1), and said first organic solvent is selected from the group consisting of acetate esters, ketones and lactones.

Claim 8

A nitrocellulose composition as claimed in claim 6, wherein said first organic solvent is selected from the group consisting of ethyl acetate, propyl acetate, butyl acetate, ethylene glycol monomethyl ether acetate, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, and gamma-butyrolactone.

Claim 9

A process for producing a nitrocellulose composition in the form of chips, comprising the steps of: adding from 30 to 300 parts by weight of a first organic solvent to 100 parts of weight, calculated on a dry basis, of water-wetted nitrocellulose, said water-wetted nitrocellulose containing not more than 50 wt.% of water, and said first organic solvent being capable of dissolving nitrocellulose and polyurethane resin but being nonreactive with isocyanate compounds; mixing together said first organic solvent and said water-wetted nitrocellulose to form a doughlike mass; molding said mass into a molding having a large surface area; drying said mass at a temperature in the range of 30° C. to 55° C. to evaporate water from said mass until said mass consists essentially of 50 to 80 wt.% of nitrocellulose, less than 1 wt.% of water, and the balance comprises said first organic solvent; and cutting said mass to form said chips.

Claim 10

A process for producing a nitrocellulose composition in the form of chips, comprising the steps of: adding from 30 to 300 parts by weight of a first organic solvent to 100 parts of weight, calculated on a dry basis, of water-wetted nitrocellulose, said water-wetted nitrocellulose containing not more than 50 wt.% of water, and said first organic solvent being capable of dissolving nitrocellulose and polyurethane resin but being nonreactive with isocyanate compounds; mixing together said first organic solvent and said water-wetted nitrocellulose to form a doughlike mass; molding said mass into a molding having a large surface area; drying said mass at a temperature in the range of 30° C. to 55° C. to evaporate water from said mass until said mass consists essentially of 50 to 80 wt.% of nitrocellulose, less than 1 wt.% of water, and the balance comprises said first organic solvent; and cutting said mass to form said chips.

Claim 11

A process as claimed in claim 8, wherein said first organic solvent is selected from the group consisting of acetate esters, ketones and lactones.

Claim 12

A process as claimed in claim 8, wherein said first organic solvent is selected from the group consisting of ethyl acetate, propyl acetate, butyl acetate, ethylene glycol monomethyl ether acetate, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone and gamma-butyrolactone.

Claim 13

A process as claimed in claim 8, wherein said mass is molded by rolling or extrusion molding at normal room temperature to form a sheet or string.

Claim 14

A process as claimed in claim 8, wherein said organic solvent and said water-wetted nitrocellulose are mixed with a binder resin for binding magnetic powder to a plastic film to make a magnetic tape, whereby to form said doughlike mass.

Claim 15

A process as claimed in claim 12, wherein said binder resin is polyurethane.

Claim 16

A process as claimed in claim 8, wherein said first organic solvent and said water-wetted nitrocellulose are mixed with a second organic solvent which is miscible with said first organic solvent but which is immiscible with water, the amount of said second organic solvent being not greater than the amount of said first organic solvent, whereby to form said doughlike mass.

Claim 17

A process as claimed in claim 14, wherein said first organic solvent is selected from the group consisting of acetate esters, ketones, and lactones, and said second organic solvent is a liquid hydrocarbon having a boiling point in the range of 80° C. to 150° C.

Claim 18

A process as claimed in claim 14, wherein said first solvent is selected from the group consisting of ethyl acetate, propyl acetate, butyl acetate, ethylene glycol monomethyl ether acetate, methyl ethyl ketone, methyl isobutyl ketone, cyclohexanone, and gamma-butyrolactone, and said second solvent is toluene or xylene.

Claim 19

A process as claimed in claim 8, wherein the water content of said water-wetted nitrocellulose is 25 to 50 wt.%, and said mixing step is accomplished in a closed system.

Claim 20

A process according to claim 8, wherein said water-wetted nitrocellulose contains 25 to 50 wt.% water and contains 10.7 to 12.2 wt.% nitrogen, the amount of said organic solvent is 30 to 100 parts by weight to 100 parts by weight, on a dry basis, of said water-wetted nitrocellulose, said mixing step is carried out in a closed system for 20 to 90 minutes, and said drying step is conducted for 10 to 50 hours.