Chlorination of poly(vinyl chloride) in liquid chlorine, and chlorinated poly(vinyl chloride) composition
Assignee: Noveon IP Holdings Corp
•
Filing: 1982-09-16
•
Granted: 1984-07-10
•
Expires: 2002-09-16
Abstract
Abstract A process is disclosed for photochlorinating poly(vinyl chloride), ("PVC"), suspended in liquid chlorine ("Cl 2 ") which swells the PVC and permits chlorination to occur in a gel phase. PVC starting material is in the form of solid free-flowing macrogranules which are slurried in from about 5 to about 50 times their weight of liquid Cl 2 in a reaction zone maintained at a temperature in the range from about -50° C. to about 50° C., and a pressure sufficient to maintain the chlorine in its liquid state. Since liquid Cl 2 itself swells the PVC to provide a gel phase in which photochlorination occurs, no conventional chlorinated hydrocarbon swelling agents, catalytic materials and the like are necessary. The process may be operated as a batch process, or a continuous process. Typical chlorine content of PVC is about 56.7 percent by weight (% by wt.), and the product of chlorination is chlorinated poly(vinyl chloride), ("CPVC"). When formed, this CPVC is dissolved in the liquid Cl 2 to form a thick syrup-like solution. CPVC is recovered as a solid by evaporation of the liquid Cl 2 , or as a finely divided solid by adding a halogenated lower alkane slowly to the CPVC syrup. The solid CPVC is homogeneously chlorinated, and its morphology and spectra, especially its 13 C nmr spectra, differentiate it from prior art compositions.
Inventors
- 👤 Richard G. Parker
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-04 16:53
CPC Classifications
B; B01; B01J; B01J19/00; B01J19/18; B01J19/20; B01J19/08; B01J19/12; B01J19/122; B01J19/123; B01J19/1868; B01J19/1881; C; C08; C08F; C08F8/00; C08F8/18; C08F8/20; C08F8/22; B01J2219/00; B01J2219/00049; B01J2219/00051; B01J2219/00074; B01J2219/00087; B01J2219/00094
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
84 words
Solid chlorinated poly(vinyl chloride) ("CPVC") resin having (i) a chlorine content greater than 65 percent by weight, (ii) a determinable glass transition temperature, (iii) in a 13 C nuclear magnetic resonance spectrum of said CPVC, a first peak at about 41 ppm said first peak being greater than other peaks in the range from about 37 to about 45 ppm, and (iv) a second peak at about 63 ppm, said second peak being greater than other peaks in the range from about 57-70 ppm.
Claim 2
Dependent Claim
84 words
Solid chlorinated poly(vinyl chloride) ("CPVC") resin having (i) a chlorine content greater than 65 percent by weight, (ii) a determinable glass transition temperature, (iii) in a 13 C nuclear magnetic resonance spectrum of said CPVC, a first peak at about 41 ppm said first peak being greater than other peaks in the range from about 37 to about 45 ppm, and (iv) a second peak at about 63 ppm, said second peak being greater than other peaks in the range from about 57-70 ppm.
Claim 3
Dependent Claim
35 words
The solid chlorinated poly(vinyl chloride) resin of claim 1 wherein said chlorine content is at least 70 percent by weight, and said spectrum has no detectable syndiotactic peak in the range from about 45-50 ppm.
Claim 4
Dependent Claim
61 words
Solid chlorinated poly(vinyl chloride) resin having (i) a chlorine content greater than 65 percent by weight, (ii) a single solid phase having a determinable T g and a dielectric loss tangent at 1 kHz which is always less than 1.5×10 -2 in the temperature range from about 100° C. to about 225° C. when the Cl content is 70.5% by wt.
Claim 5
Dependent Claim
61 words
Solid chlorinated poly(vinyl chloride) resin having (i) a chlorine content greater than 65 percent by weight, (ii) a single solid phase having a determinable T g and a dielectric loss tangent at 1 kHz which is always less than 1.5×10 -2 in the temperature range from about 100° C. to about 225° C. when the Cl content is 70.5% by wt.
Claim 6
Dependent Claim
66 words
The solid chlorinated poly(vinyl chloride) resin of claim 3 additionally characterized by the following: at 65% Cl, having a T g =130° C. and about 3.0 mol % CCl 2 carbons; at 68% Cl, having a T g =157° C. and about 6.0 mol % CCl 2 carbons; and, at 70.5% Cl, having a T g =194° C. and about 13.1 mol % CCl 2 carbons.
Claim 7
Dependent Claim
34 words
The solid chlorinated poly(vinyl chloride) resin of claim 3 which resin at 65% Cl having a T g =130° C., has a second heat of melting ΔHm 2 in the range from 0.0-0.25 kJ/Kg.
Claim 8
Dependent Claim
207 words
In a process for photochlorinating poly(vinyl chloride) homopolymer macrogranules to obtain homogeneously chlorinated `chlorinated poly(vinyl chloride) resin` ("CPVC") including suspending said homopolymer having a chlorine content in the range from about 56% to 57% by weight, in liquid chlorine present in an amount at least five times the weight of said homopolymer, for a period of time sufficient to absorb said liquid chlorine into said macrogranules, swelling said macrogranules at solid-liquid interfaces within and around said macrogranules to produce a gel phase by the action of said liquid chlorine, photo-illuminating said gel phase until said homopolymer is converted to homogeneously chlorinated CPVC having at least 65% by weight of chlorine, and the mol ratio of PVC present in a sequence of 3 or more vinyl chloride units, to the mols of total vinyl chloride units, is always less than 3.0, obtaining a solution of said homogeneously chlorinated CPVC in liquid chlorine, and recovering solid homogeneously chlorinated CPVC from said solution, the improvement comprising, (a) adding a halogenated lower alkane to said solution in an amount sufficient to dissolve said liquid chlorine, so as to (b) precipitate said solid homogeneously chlorinated CPVC, and, (c) separating said solid homogeneously chlorinated CPVC from said liquid chlorine and halogenated lower alkane.
Claim 9
Dependent Claim
207 words
In a process for photochlorinating poly(vinyl chloride) homopolymer macrogranules to obtain homogeneously chlorinated `chlorinated poly(vinyl chloride) resin` ("CPVC") including suspending said homopolymer having a chlorine content in the range from about 56% to 57% by weight, in liquid chlorine present in an amount at least five times the weight of said homopolymer, for a period of time sufficient to absorb said liquid chlorine into said macrogranules, swelling said macrogranules at solid-liquid interfaces within and around said macrogranules to produce a gel phase by the action of said liquid chlorine, photo-illuminating said gel phase until said homopolymer is converted to homogeneously chlorinated CPVC having at least 65% by weight of chlorine, and the mol ratio of PVC present in a sequence of 3 or more vinyl chloride units, to the mols of total vinyl chloride units, is always less than 3.0, obtaining a solution of said homogeneously chlorinated CPVC in liquid chlorine, and recovering solid homogeneously chlorinated CPVC from said solution, the improvement comprising, (a) adding a halogenated lower alkane to said solution in an amount sufficient to dissolve said liquid chlorine, so as to (b) precipitate said solid homogeneously chlorinated CPVC, and, (c) separating said solid homogeneously chlorinated CPVC from said liquid chlorine and halogenated lower alkane.
Claim 10
Dependent Claim
51 words
The process of claim 6 wherein recovering said solid homogeneously chlorinated CPVC from solution comprises, (a) adding a sufficient amount of a halogenated lower alkane to said solution to precipitate substantially all said homogeneously chlorinated CPVC as solid, and, (b) separating precipitated solid from said halogenated lower alkane and liquid chlorine.
Claim 11
Dependent Claim
20 words
The process of claim 7 wherein said halogenated lower alkane is selected from the group consisting of dichlorodifluoromethane and trichlorotrifluoroethane.
References Cited (Backward Citations)
US4147859A
Cited
US4350798A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-10 | 1988-01-09 | 1988-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-10 | 1992-01-09 | 1992-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-10 | 1996-01-09 | 1996-07-10 | $7700.00 | Window Closed / Lapsed |