Heat resisting ethylene-propylene rubber and insulated conductor product thereof
Assignee: Vulkor Inc
•
Filing: 1981-08-03
•
Granted: 1984-07-10
•
Expires: 2001-08-03
Abstract
Abstract A crosslink curable ethylene-propylene rubber composition with improved resistance to heat shock, the cured rubber composition and electrical conductors insulated with said cured rubber composition. The improved rubber composition comprises a combination of ethylene-propylene rubbers of different structural orientation, and antioxidants.
Inventors
- 👤 Joseph E. Vostovich
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-31 00:33
CPC Classifications
H; H01; H01B; H01B7/00; H01B7/17; H01B7/29; H01B3/00; H01B3/18; H01B3/30; H01B3/44; H01B3/441
Claims Analysis
Total Claims: 15
Claim 1
Independent Claim
57 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber,
80
semi-crystalline
Ethylene-propylene rubber,
10-40
amorphous
Hydrated alumina filler
50-150
Zinc oxide 10-30
Paraffin 0-15
Polychloroprene 0-15
Antioxidant 2-8
Vinyl silane 0-5
Peroxide crosslink curing agent
2-8
______________________________________
Claim 2
Dependent Claim
57 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber,
80
semi-crystalline
Ethylene-propylene rubber,
10-40
amorphous
Hydrated alumina filler
50-150
Zinc oxide 10-30
Paraffin 0-15
Polychloroprene 0-15
Antioxidant 2-8
Vinyl silane 0-5
Peroxide crosslink curing agent
2-8
______________________________________
Claim 3
Dependent Claim
12 words
The crosslink cured product of the ethylene-propylene rubber composition of claim 1.
Claim 4
Dependent Claim
73 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, semi-crystalline
80
Ethylene-propylene rubber, amorphous
10-40
Hydrated alumina filler 50-150
Zinc oxide 10-30
Paraffin 0-15
Polychloroprene 0-15
Antioxidants - combination of a sterically
2-8
hindered di-tertiary butyl phenol with a
zinc salt of a mercaptoimidazole
Vinyl silane 0-5
Peroxide crosslink curing agent
2-8
______________________________________
Claim 5
Dependent Claim
73 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, semi-crystalline
80
Ethylene-propylene rubber, amorphous
10-40
Hydrated alumina filler 50-150
Zinc oxide 10-30
Paraffin 0-15
Polychloroprene 0-15
Antioxidants - combination of a sterically
2-8
hindered di-tertiary butyl phenol with a
zinc salt of a mercaptoimidazole
Vinyl silane 0-5
Peroxide crosslink curing agent
2-8
______________________________________
Claim 6
Dependent Claim
12 words
The crosslink cured product of the ethylene-propylene rubber composition of claim 3.
Claim 7
Dependent Claim
87 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, at least about
80
8 percent crystalline
Ethylene-propylene rubber, substantially
10- 50
amorphous
Hydrated alumina filler 50- 150
Zinc oxide 10- 30
Paraffin 0- 15
Polychloroprene 3- 15
Antioxidants - combination of a sterically
2- 8
hindered di-tertiary butyl phenol with a
zinc salt of a mercaptoimidazole
Vinyl silane 0.5- 5
Peroxide crosslink curing agent
2- 8
______________________________________
Claim 8
Dependent Claim
87 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, at least about
80
8 percent crystalline
Ethylene-propylene rubber, substantially
10- 50
amorphous
Hydrated alumina filler 50- 150
Zinc oxide 10- 30
Paraffin 0- 15
Polychloroprene 3- 15
Antioxidants - combination of a sterically
2- 8
hindered di-tertiary butyl phenol with a
zinc salt of a mercaptoimidazole
Vinyl silane 0.5- 5
Peroxide crosslink curing agent
2- 8
______________________________________
Claim 9
Dependent Claim
12 words
The crosslink cured product of the ethylene-propylene rubber composition of claim 5.
Claim 10
Dependent Claim
96 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, approximately
80
8 to 40 percent crystalline
Ethylene-propylene rubber, substantially
10- 40
amorphous
Hydrated alumina filler 50- 150
Zinc oxide 10- 30
Paraffin 0- 15
Polychloroprene 3- 15
Antioxidant - combination of a sterically
2- 8
hindered di-tertiary butyl phenol with a
zinc salt of a mercaptoimidazole in an
approximate weight ratio of 1 to 2
Vinyl silane 0.5- 5
Peroxide crosslink curing agent
2- 8
______________________________________
Claim 11
Dependent Claim
96 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, approximately
80
8 to 40 percent crystalline
Ethylene-propylene rubber, substantially
10- 40
amorphous
Hydrated alumina filler 50- 150
Zinc oxide 10- 30
Paraffin 0- 15
Polychloroprene 3- 15
Antioxidant - combination of a sterically
2- 8
hindered di-tertiary butyl phenol with a
zinc salt of a mercaptoimidazole in an
approximate weight ratio of 1 to 2
Vinyl silane 0.5- 5
Peroxide crosslink curing agent
2- 8
______________________________________
Claim 12
Dependent Claim
12 words
The crosslink cured product of the ethylene-propylene rubber composition of claim 7.
Claim 13
Dependent Claim
89 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, approximately
80
8 to 30 percent crystalline
Ethylene-propylene rubber,
20
substantially amorphous
Hydrated alumina filler 100
Zinc oxide 15
Paraffin 5
Polychloroprene 8
Antioxidants - combination of a sterically
6
hindered di-tertiray butyl phenol with a
zinc salt of a mercaptoimidazole in an
approximate weight ratio of 1 to 2
Vinyl silane 1.5
Di-cumyl peroxide crosslink curing agent
3
______________________________________
Claim 14
Dependent Claim
89 words
A curable ethylene-propylene rubber composition having improved resistance to heat shock and apt electrical and physical properties, comprising the combination in approximate parts by weight of: ______________________________________
Ethylene-propylene rubber, approximately
80
8 to 30 percent crystalline
Ethylene-propylene rubber,
20
substantially amorphous
Hydrated alumina filler 100
Zinc oxide 15
Paraffin 5
Polychloroprene 8
Antioxidants - combination of a sterically
6
hindered di-tertiray butyl phenol with a
zinc salt of a mercaptoimidazole in an
approximate weight ratio of 1 to 2
Vinyl silane 1.5
Di-cumyl peroxide crosslink curing agent
3
______________________________________
Claim 15
Dependent Claim
12 words
The crosslink cured product of the ethylene-propylene rubber composition of claim 9.
References Cited (Backward Citations)
US3562790A
Cited
US3378512A
Cited
US3468979A
Cited
US3862106A
Cited
US3700614A
Cited
US3806558A
Cited
US3835201A
Cited
US3904470A
Cited
US4031169A
Cited
US4066590A
Cited
US4125509A
Cited
US4202801A
Cited
US4303574A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-10 | 1988-01-09 | 1988-07-10 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-10 | 1992-01-09 | 1992-07-10 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-10 | 1996-01-09 | 1996-07-10 | $7700.00 | Window Closed / Lapsed |