Patent US4758677A successfully refreshed from Google Patents.
US4457977A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Metallized plastic articles
Assignee: Dow Chemical Co
•
Filing: 1981-09-30
•
Granted: 1984-07-03
•
Expires: 2001-09-30
Abstract
Abstract A surface of a plastic article is metallized without substantial pinholes, holidays and the like by initially coating the surface with an aqueous colloidal dispersion of an organic polymer, particularly a barrier polymer such as polyvinylidene chloride, treating the organic polymer coating to make it metallizable and subsequently overcoating the treated organic polymer coating with a metal to form a thin metal layer adherent to the organic polymer layer. The resulting metallized plastic article which can optionally be treated with an additional amount of an aqueous colloidal dispersion of an organic polymer or metal is essentially impermeable to atmospheric gases and other vapors.
Inventors
- 👤 Wilhelm E. Walles
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-11-03 09:00
CPC Classifications
C; C23; C23C; C23C14/00; C23C14/02; C08; C08J; C08J7/00; C08J7/04; C08J7/042; C08J7/0423; C08J7/048; C23C14/06; C23C14/14; C23C14/20; Y; Y10; Y10T; Y10T428/00; Y10T428/13; Y10T428/1352; Y10T428/1355; Y10T428/1359; Y10T428/31504; Y10T428/31678; Y10T428/31692; Y10T428/31699; Y10T428/31855; Y10T428/31909; Y10T428/31913; Y10T428/3192; Y10T428/31928
Claims Analysis
Total Claims: 11
Claim 1
Independent Claim
88 words
A diffusion barrier structure comprising a substrate of an organic plastic material having an adherent continuous coating of an organic polymer which exhibits a permeance to gases of the atmosphere of less than 0.4 cc-mm/m 2 -atm-day deposited on the surface thereof, wherein said coating has a coating weight from about 60 to about 2500 micrograms per square centimeter, said organic polymer having a water-wettable surface which has a continuous metal layer having a total weight from about 20 to 10 μg/cm 2 deposited thereon and adherent thereto.
Claim 2
Dependent Claim
88 words
A diffusion barrier structure comprising a substrate of an organic plastic material having an adherent continuous coating of an organic polymer which exhibits a permeance to gases of the atmosphere of less than 0.4 cc-mm/m 2 -atm-day deposited on the surface thereof, wherein said coating has a coating weight from about 60 to about 2500 micrograms per square centimeter, said organic polymer having a water-wettable surface which has a continuous metal layer having a total weight from about 20 to 10 μg/cm 2 deposited thereon and adherent thereto.
Claim 3
Dependent Claim
40 words
The diffusion barrier structure of claim 1 wherein the metal layer is coated with an organic polymer which adheres to the metal layer, said organic polymer being applied to the metal layer in the form of an aqueous colloidal dispersion.
Claim 4
Dependent Claim
16 words
The diffusion barrier structure of claim 1 wherein the organic polymer is a vinylidene chloride copolymer.
Claim 5
Dependent Claim
12 words
The diffusion barrier structure of claim 1 wherein the metal is silver.
Claim 6
Independent Claim
121 words
A method for preparing a diffusion barrier structure, said method comprising the steps of (1) applying an organic polymer which exhibits a permeance to gases of the atmosphere of less than 0.4 cc-mm/m 2 -atm-day to at least one surface of an organic plastic substrate to provide an essentially continuous coating adherent to the plastic substrate of the organic polymer, wherein said coating has a coating weight from about 60 to about 2500 micrograms per square centimeter, (2) rendering a surface of the organic polymer coating water-wettable and (3) metallizing the water-wettable surface of the organic polymer coating at conditions sufficient to provide a metal layer having a total weight from about 20 to 10 μg/cm 2 adherent to said coating.
Claim 7
Independent Claim
121 words
A method for preparing a diffusion barrier structure, said method comprising the steps of (1) applying an organic polymer which exhibits a permeance to gases of the atmosphere of less than 0.4 cc-mm/m 2 -atm-day to at least one surface of an organic plastic substrate to provide an essentially continuous coating adherent to the plastic substrate of the organic polymer, wherein said coating has a coating weight from about 60 to about 2500 micrograms per square centimeter, (2) rendering a surface of the organic polymer coating water-wettable and (3) metallizing the water-wettable surface of the organic polymer coating at conditions sufficient to provide a metal layer having a total weight from about 20 to 10 μg/cm 2 adherent to said coating.
Claim 8
Dependent Claim
104 words
The method of claim 5 wherein the organic polymer is a polymer of vinylidene chloride, the organic polymer coating has a weight in the range from about 60-2500 micrograms per square centimeter, the surface of said organic polymer coating is rendered water-wettable by contacting said surface with sulfur trioxide, and the water-wettable surface is metallized by contacting the water-wettable surface with an aqueous solution of a water-soluble salt of a metal which solution further contains a reducing agent which is capable of reducing the metal such that a metal layer weighing from about 20-1000 micrograms per square centimeter is deposited on said water-wettable surface.
Claim 9
Dependent Claim
37 words
The method of claim 6 wherein the water-wettable surface of the organic polymer is coated with a tin compound having a coating weight of about 0.5 to 50 micrograms per square centimeter prior to the metallization thereof.
Claim 10
Dependent Claim
12 words
The method of claim 6 wherein the metal is silver or copper.
Claim 11
Dependent Claim
25 words
The method of claim 8 wherein the diffusion barrier structure has a permeance to oxygen of no more than about 0.0085 cc/100 in 2 /day/atm.
References Cited (Backward Citations)
US3467540A
Cited
US3488166A
Cited
US3625751A
Cited
US4049904A
Cited
GB1284805A
Cited
US3616190A
Cited
US3916048A
Cited
US3828960A
Cited
US4015049A
Cited
US4089993A
Cited
US4310578A
Cited
US4345005A
Cited
US4357383A
Cited
US4311742A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-07-03 | 1988-01-02 | 1988-07-03 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-07-03 | 1992-01-02 | 1992-07-03 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-07-03 | 1996-01-02 | 1996-07-03 | $7700.00 | Window Closed / Lapsed |