US4455325A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method of inducing flow or densification of phosphosilicate glass for integrated circuits
Assignee: National Semiconductor Corp
•
Filing: 1983-01-07
•
Granted: 1984-06-19
•
Expires: 2003-01-07
Abstract
Abstract Phosphorus-doped silicon oxide glass is flowed on an integrated circuit by raising the pressure in which that integrated circuit is placed above atmospheric for a selected period of time and heating said phosphosilicate glass to a selected temperature sufficient to cause said glass to flow at said pressure. The atmosphere in which the device is placed includes moisture to enhance the flow of the glass at temperatures substantially beneath those at which dopants in the underlying integrated circuit move. The result is that the electrical characteristics of the integrated circuit are not substantially altered during glass flow.
Inventors
- 👤 Reda Razouk
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 00:49
CPC Classifications
H; H10; H10W; H10W20/00; H10W20/01; H10W20/031; H10W20/069; H10P; H10P95/00; H10W20/071; H10W20/092; H05; H05K; H05K1/00; H05K1/02; H05K1/03; H05K1/0306; H05K3/00; H05K3/22; H05K3/28
Claims Analysis
Total Claims: 10
Claim 1
Independent Claim
121 words
In the manufacture of an integrated circuit, the method of flowing a silicon oxide glass containing phosphorous, said glass being deposited on an underlying semiconductor material, said semiconductor material containing dopants, which method comprises: (a) raising the pressure acting on said glass, after said glass has been deposited on said semiconductor, above atmospheric pressure in an environment containing moisture for a selected period of time; (b) simultaneously heating said glass to a selected temperature less than 1000° C. for said time, said pressure, time and temperature being selected so as to prevent redistribution of the dopant within the semiconductor material but sufficient to cause said glass to flow and density; and (c) returning the resulting structure to atmospheric pressure and temperature.
Claim 2
Dependent Claim
121 words
In the manufacture of an integrated circuit, the method of flowing a silicon oxide glass containing phosphorous, said glass being deposited on an underlying semiconductor material, said semiconductor material containing dopants, which method comprises: (a) raising the pressure acting on said glass, after said glass has been deposited on said semiconductor, above atmospheric pressure in an environment containing moisture for a selected period of time; (b) simultaneously heating said glass to a selected temperature less than 1000° C. for said time, said pressure, time and temperature being selected so as to prevent redistribution of the dopant within the semiconductor material but sufficient to cause said glass to flow and density; and (c) returning the resulting structure to atmospheric pressure and temperature.
Claim 3
Dependent Claim
23 words
The method of claim 1 wherein said glass is raised to a selected pressure above ambient in an environment comprising moisture and oxygen.
Claim 4
Dependent Claim
24 words
The method of claim 1 wherein said glass is raised to a selected pressure above ambient in an environment comprising moisture and inert gas.
Claim 5
Dependent Claim
35 words
The method of claim 1 wherein said glass is raised to a pressure within a range of pressures sufficient that said glass flows at a temperature within the range of 750° C. to 1000° C.
Claim 6
Dependent Claim
17 words
The method of claim 4 wherein said glass is raised to a pressure of approximately 25 atmospheres.
Claim 7
Dependent Claim
23 words
The method of claim 4 wherein said glass is raised to a pressure of approximately 25 atmospheres and wherein said environment includes oxygen.
Claim 8
Dependent Claim
25 words
The method of claim 4 wherein said glass is raised to a pressure of approximately 25 atmospheres and wherein said environment includes an inert gas.
Claim 9
Dependent Claim
78 words
The method of claim 1 wherein the semiconductor material comprises silicon, and the method includes the additional step of first forming a via part way through said glass prior to raising the pressure, said via having a discernible edge between the sides of the via and the top of said glass, and simultaneously heating said glass and wherein the edges of said via are rounded by the flow of said glass resultant from the heating of said glass.
Claim 10
Dependent Claim
22 words
The method of claim 1 or 8 in which said glass contains from between about 6% to 9% by weight of phosphorous.
References Cited (Backward Citations)
US2634555A
Cited
US3224851A
Cited
US3328145A
Cited
US3490886A
Cited
US3625669A
Cited
US3825442A
Cited
US3819348A
Cited
US4059425A
Cited
US4068020A
Cited
US4271582A
Cited
US4221824A
Cited
US4194643A
Cited
US4251251A
Cited
US4349584A
Cited
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-19 | 1987-12-19 | 1988-06-19 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-19 | 1991-12-19 | 1992-06-19 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-19 | 1995-12-19 | 1996-06-19 | $7700.00 | Window Closed / Lapsed |