Conductive high-pressure laminate and method of preparation

Claim 2

In a synthetic surface-covering laminate sheet material which comprises a plurality of cured, resin-saturated paper materials, including a top sheet material, laminated together under heat and pressure to form a hard thermoset resin laminate sheet material having a hard top surface suitable for use as a surface covering, the improvement which comprises: the laminate comprising one or more paper materials containing an electrically conductive, static-dissipating amount of a quaternary ammonium compound present in an amount to provide a laminate having a top surface resistivity of 10 9 ohms per square inch or less, when tested in accordance with ASTM-D257.

Claim 3

The laminate of claim 1 wherein the quaternary ammonium compound comprises from about 5 to 70 percent by weight of the cured resin paper material.

Claim 4

The laminate of claim 1 wherein the quaternary ammonium compound comprises a methyl-allyl quaternary ammonium halide present in an amount of from about 10 to 30 percent by weight of the resin cured top paper material.

Claim 5

The laminate of claim 1 wherein the quaternary ammonium compound comprises an alkyl-alkylene quaternary ammonium salt compound.

Claim 6

The laminate of claim 1 wherein the quaternary ammonium compound comprises an allyl-methyl quaternary ammonium halide compound.

Claim 7

The laminate of claim 1 wherein the quaternary ammonium compound comprises an n-alkyl, methyl, benzyl quaternary ammonium halide.

Claim 8

The laminate of claim 1 wherein the quaternary ammonium compound comprises an ethoxylated-alkyl quaternary ammonium halide.

Claim 9

The laminate of claim 1 wherein the quaternary ammonium compound comprises a dimethyl diallyl quaternary ammonium chloride.

Claim 10

The laminate of claim 1 wherein the top surface resistivity of the laminate is from about 10 8 ohms per square inch or less when tested in accordance with ASTM-D257.

Claim 11

The laminate of claim 1 wherein one or more of the paper materials have been treated with a treating solution comprising a curable formaldehyde resin, catalyst to cure the curable resin, on heating, and from about 10 to 25 parts of a quaternary ammonium compound per 100 parts of the resin solution.

Claim 12

The laminate of claim 10 wherein the quaternary ammonium compound in the treating solution comprises a methyl-unsaturated hydrocarbon quaternary ammonium salt compound.

Claim 13

The laminate of claim 10 wherein the quaternary ammonium compound comprises a dimethyl diallyl quaternary ammonium halide compound.

Claim 14

The laminate of claim 1 wherein the top paper material comprises a light-colored or transparent, cured, resin-saturated sheet material which includes an electrically conductive amount of a quaternary ammonium compound therein, and which sheet laminate includes a resin-saturated barrier sheet material below the top sheet material and laminated thereto in the sheet laminate.

Claim 15

The laminate of claim 13 wherein the resin-saturated barrier sheet material comprises a resin-saturated barrier paper sheet material which includes an electrically conductive amount of a quaternary ammonium compound therein.

Claim 16

The laminate of claim 1 wherein the top sheet material comprises a cured, melamine-formaldehyde saturated paper sheet material and which includes a cured, light-colored, resin-saturated barrier paper sheet material beneath the top sheet material, and which includes an electrically conductive, cured, resin-saturated sheet material below the barrier paper sheet material, wherein the conductive sheet material comprises a paper sheet material impregnated with electrically conductive particles.

Claim 17

The laminate material of claim 15 wherein the electrically conductive particles impregnated in the conductive paper sheet material comprise finely-divided carbon particles.

Claim 18

The laminate material of claim 15 which includes conductive means, to conduct static charge accumulated thereon to ground.

Claim 19

The laminate material of claim 1 which includes a plurality of cured phenol resin-impregnated paper sheet materials bonded in the sheet laminate and positioned beneath the top sheet material.

Claim 20

An electrically conductive surface covering which comprises a solid surface and a sheet laminate material of claim 1 bonded thereto and electrically conductive means extending from the laminate to ground.

Claim 21

A surface-covering laminate sheet material, which sheet material comprises in combination: (a) a melamine-formaldehyde resin-saturated paper topsheet material having an electrically conductive amount of a quaternary ammonium compound sufficient to provide a surface resistivity to the top surface of the top sheet of 10 9 ohms per square inch or less, when tested in accordance with ASTM-D257; (b) a resin-saturated light-colored barrier paper material beneath the top sheet material; (c) an electrically conductive resin-saturated paper material directly beneath the barrier sheet material and comprising an electrically conductive amount of carbon particles therein; (d) a plurality of resin-saturated paper sheet materials beneath the electrically conductive sheet materials; (e) the sheet materials bonded together under heat and pressure, to form a thermoset sheet laminate material having an electrically conductive top surface; and (f) electrically conductive means in electrical communication with laminate to provide a pathway to ground for static charges on the thermoset sheet laminate material.

Claim 22

A surface-covering laminate sheet material, which sheet material comprises in combination: (a) a melamine-formaldehyde resin-saturated paper topsheet material having an electrically conductive amount of a quaternary ammonium compound sufficient to provide a surface resistivity to the top surface of the top sheet of 10 9 ohms per square inch or less, when tested in accordance with ASTM-D257; (b) a resin-saturated light-colored barrier paper material beneath the top sheet material; (c) an electrically conductive resin-saturated paper material directly beneath the barrier sheet material and comprising an electrically conductive amount of carbon particles therein; (d) a plurality of resin-saturated paper sheet materials beneath the electrically conductive sheet materials; (e) the sheet materials bonded together under heat and pressure, to form a thermoset sheet laminate material having an electrically conductive top surface; and (f) electrically conductive means in electrical communication with laminate to provide a pathway to ground for static charges on the thermoset sheet laminate material.

Claim 23

The laminate of claim 20 wherein the quaternary ammonium compound comprises a methyl-allyl quaternary ammonium halide.

Claim 24

The laminate of claim 21 wherein the barrier sheet material includes an electrically conductive amount of a methyl-allyl quaternary ammonium halide.