US4453987A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Method for producing edged tools
Assignee: Toyota Central R&D Labs Inc
•
Filing: 1982-04-06
•
Granted: 1984-06-12
•
Expires: 2002-04-06
Abstract
Abstract A method for producing an edged tool which has an excellent cutting ability and durability, which comprises immersing an edged-tool material in a molten-salt bath containing a carbide-forming element, such as a Va Group element, titanium, chromium or manganese, to form a carbide layer on the surface of the edged-tool material; heating the edged-tool material to a temperature not lower than the austenite-transformation temperature of the material in a non-oxidizing gas atmosphere for a predetermined period of time; and rapidly cooling the heated material to harden it. According to the improved method of the present invention, the edged tool (having an excellent cutting ability and durability) is produced without grinding the formed carbide layer on the surface thereof.
Inventors
- 👤 Tohru Arai
- 👤 Yoshihiko Sugimoto
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-24 00:23
CPC Classifications
C; C23; C23C; C23C10/00; C23C10/60; C21; C21D; C21D9/00; C21D9/18; C23C10/18; C23C10/20; C23C10/24; Y; Y10; Y10S; Y10S148/00; Y10S148/902; Y10S148/905; Y10T; Y10T428/00; Y10T428/12; Y10T428/12493; Y10T428/12535; Y10T428/12556; Y10T428/12569
Claims Analysis
Total Claims: 16
Claim 1
Independent Claim
108 words
A method for producing an edged tool without the need to grind a carbide layer, comprising the steps of: (a) immersing tool material with a cutting edge in a molten-salt bath comprising molten boric acid or borate and a carbide-forming element (to form a carbide layer on the surface of said tool material, said tool material being made of ferrous alloy containing at least 0.4 percent by weight of carbon); (b) heating said tool material to a temperature not lower than the austenite-transformation temperature of said material in a non-oxidizing gas atmosphere for a predetermined period of time; and (c) rapidly cooling and thus hardening said heated material.
Claim 2
Independent Claim
108 words
A method for producing an edged tool without the need to grind a carbide layer, comprising the steps of: (a) immersing tool material with a cutting edge in a molten-salt bath comprising molten boric acid or borate and a carbide-forming element (to form a carbide layer on the surface of said tool material, said tool material being made of ferrous alloy containing at least 0.4 percent by weight of carbon); (b) heating said tool material to a temperature not lower than the austenite-transformation temperature of said material in a non-oxidizing gas atmosphere for a predetermined period of time; and (c) rapidly cooling and thus hardening said heated material.
Claim 3
Dependent Claim
27 words
A method according to claim 1, wherein said carbide-forming element is a member selected from the group consisting of a Va Group element, titanium, chromium and manganese.
Claim 4
Dependent Claim
14 words
A method according to claim 2, wherein said carbide-forming element is in alloy form.
Claim 5
Dependent Claim
14 words
A method according to claim 2, wherein said carbide-forming element is in chloride form.
Claim 6
Dependent Claim
30 words
A method according to claim 2, wherein said carbide-forming element is in oxide form and said molten-salt bath further comprises a boron-supplying material wherein boron is not bound to oxygen.
Claim 7
Dependent Claim
19 words
A method according to claim 1, wherein said tool material has a cutting-edge angle of no more than 45°.
Claim 8
Dependent Claim
19 words
A method according to claim 6, wherein said cutting-edge angle of the tool material is not larger than 30°.
Claim 9
Dependent Claim
29 words
A method according to claim 1, wherein said non-oxidizing gas atmosphere is a member selected from the group consisting of nitrogen gas, argon gas, hydrogen gas and a vacuum.
Claim 10
Dependent Claim
29 words
A method according to claim 1, wherein the thickness of said carbide layer formed on the surface of the tool material is not in excess of about 5 microns.
Claim 11
Dependent Claim
21 words
A method according to claim 9, wherein said thickness of the formed carbide layer is from about 2 to 3 microns.
Claim 12
Dependent Claim
40 words
A ferrous-alloy tool containing at least 0.4 percent by weight of carbon and having a non-ground sharp and durable, in-situ formed, carbide-coated edge, the tool having a carbide layer, which does not exceed about 5 microns, on its sharp edge.
Claim 13
Dependent Claim
40 words
A ferrous-alloy tool containing at least 0.4 percent by weight of carbon and having a non-ground sharp and durable, in-situ formed, carbide-coated edge, the tool having a carbide layer, which does not exceed about 5 microns, on its sharp edge.
Claim 14
Dependent Claim
91 words
An edged tool having excellent cutting ability and durability comprising a sharp cutting edge having a cutting-edge angle of not more than 45° and being made of ferrous alloy containing at least 0.4 percent by weight of carbon, said edged tool having (a) no ground end surface adjacent to said sharp cutting edge and (b) a non ground carbide layer having a thickness of not more than 5 microns both on said sharp cutting edge and on an entire end surface of said edged tool adjacent to said sharp cutting edge.
Claim 15
Dependent Claim
91 words
An edged tool having excellent cutting ability and durability comprising a sharp cutting edge having a cutting-edge angle of not more than 45° and being made of ferrous alloy containing at least 0.4 percent by weight of carbon, said edged tool having (a) no ground end surface adjacent to said sharp cutting edge and (b) a non ground carbide layer having a thickness of not more than 5 microns both on said sharp cutting edge and on an entire end surface of said edged tool adjacent to said sharp cutting edge.
Claim 16
Dependent Claim
16 words
An edged tool having excellent cutting ability and durability prepared by the method of claim 1.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-12 | 1987-12-12 | 1988-06-12 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-12 | 1991-12-12 | 1992-06-12 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-12 | 1995-12-12 | 1996-06-12 | $7700.00 | Window Closed / Lapsed |