US4452953A
Expired / Lapsed
US
⏱️ 0.0 years remaining
Process for the vapor phase chlorosulfonation of polyolefins in the presence of finely divided inorganic materials
Assignee: Goodrich Corp
•
Filing: 1982-07-28
•
Granted: 1984-06-05
•
Expires: 2002-07-28
Abstract
Abstract An improved vapor phase process for chlorosulfonation of polyethylene, particularly in a fluidized bed, is accomplished by treating a mixture of powdered polyethylene, and finely divided inorganic compounds having a dielectric constant of greater than about 40 and specific conductivity greater than 10-13 to less than 10-1 ( OMEGA -1 cm-1), such as titanium dioxide, with chlorine and sulfur dioxide, optionally under actinic light, at an initial temperature from about 20 DEG C. to about 70 DEG C. and raising the temperature of the reaction to at least about the crystalline melting point of the polyethylene and continuing the reaction until the polyethylene contains about 25 to 45 weight percent bound chlorine and 0.5 to 3 weight percent sulfur to provide improved vulcanizable elastomers. In the fluidized bed process, improvement is obtained in bed mixing and heat transfer, with minimum polymer deposition on reactor walls and polymer agglomeration, essentially eliminating channeling and bed breakdown.
Inventors
- 👤 George M. Benedikt
Bibliographic Details
Application Number
—
Jurisdiction
US
Data Source
google_patents
Last Synchronized
2026-10-26 22:41
CPC Classifications
C; C08; C08F; C08F8/00; C08F8/34; C08F8/38
Claims Analysis
Total Claims: 13
Claim 1
Independent Claim
184 words
In a vapor phase process for chlorosulfonating polyethylene with chlorine and sulfur dioxide, the improvement comprising conducting the chlorosulfonation reaction in a fluidized bed of powdered polyethylene and inorganic compounds consisting essentially of titanium compounds that are inert to chlorine and sulfur dioxide in the defined process, present in amounts from about 1 to 15 weight parts per 100 weight parts of polyethylene, having an average particle size of about 0.01 to 10 microns, a dielectric constant greater than about 40, and a specific conductivity (Ω -1 cm -1 ) value of greater than 10 -13 to less than 10 -1 in the temperature range of 20° to 140° C., at an initial reaction temperature of from about 20° C. to about 70° C., raising the reaction temperature to at least about the crystalline melting point of the polyethylene, the volume ratio of chlorine to sulfur dioxide being from about 20:1 to about 1:2, and continuing the reaction until the chlorosulfonated polyethylene contains greater than 25 weight percent to about 45 weight percent bound chlorine and about 0.5 to about 3 weight percent sulfur.
Claim 2
Dependent Claim
184 words
In a vapor phase process for chlorosulfonating polyethylene with chlorine and sulfur dioxide, the improvement comprising conducting the chlorosulfonation reaction in a fluidized bed of powdered polyethylene and inorganic compounds consisting essentially of titanium compounds that are inert to chlorine and sulfur dioxide in the defined process, present in amounts from about 1 to 15 weight parts per 100 weight parts of polyethylene, having an average particle size of about 0.01 to 10 microns, a dielectric constant greater than about 40, and a specific conductivity (Ω -1 cm -1 ) value of greater than 10 -13 to less than 10 -1 in the temperature range of 20° to 140° C., at an initial reaction temperature of from about 20° C. to about 70° C., raising the reaction temperature to at least about the crystalline melting point of the polyethylene, the volume ratio of chlorine to sulfur dioxide being from about 20:1 to about 1:2, and continuing the reaction until the chlorosulfonated polyethylene contains greater than 25 weight percent to about 45 weight percent bound chlorine and about 0.5 to about 3 weight percent sulfur.
Claim 3
Dependent Claim
122 words
The process of claim 1 wherein the polyethylene contains less than 10 weight percent copolymerized alpha olefins containing 3 to 6 carbon atoms, has a density from about 0.92 to about 0.97, a crystalline melting point of about 100° C. to about 140° C., a melt index of 0.01 to less than 30 and a particle size from about 50 to 800 microns, the inorganic compound is selected from the group consistng of finely divided titanium dioxide, barium titanate, lead titanate and barium-lead titanate-niobate, having a dielectric constant greater than 80, present in amounts from about 1 to 10 weight parts, and the reaction temperature is raised to about 100° C. to about 150° C. to complete the chlorosulfonation of the polyethylene.
Claim 4
Dependent Claim
77 words
The process of claim 2 wherein the polyethylene is polyethylene, has a melt index from 0.2 to 18, a particle size from 100 to 600 microns and an average particle size range of 200 to 300 microns, and the volume ratio of chlorine to sulfur dioxide is from 4:1 to 1:2, and the titanium compound is titanium dioxide or barium titanate having a particle size of 0.5 to 2 microns, conducted in the presence of actinic light.
Claim 5
Dependent Claim
21 words
The process of claim 3 wherein the titanium compound is rutile titanium dioxide with a particle size of about 0.2±0.05 microns.
Claim 6
Dependent Claim
20 words
The process of claim 3 wherein the inorganic compound is barium titanate with a particle size of about 0.2 ±0.05.
Claim 7
Dependent Claim
182 words
A process for vapor phase chlorosulfonation or polyethylene with chlorine and sulfur dioxide comprising mixing a finely divided inorganic compound that is inert to chlorine and sulfur dioxide in the defined process, has a dielectric constant of greater than about 40, a specific conductivity (Ω -1 cm -1 ) value of greater than 10 -13 to less than 10 -1 , and an average particle size of about 0.01 to 10 microns, having the general formual ABO 3 wherein A is Na, K, Rb, Ca, Bi, Sr, Ba, Pb, Gd; and B is Ti, Sn, Zr, Nb, Ta, W, and mixtures thereof, present in amounts from about 1 to 15 weight parts per 100 weight parts of polyethylene, with powdered polyetheylene and chlorosulfonating the polyethylene at an initial temperature between about 20° C. and 70° C., raising the temperature to at least about the crystalline melting point of the polyethylene and continuing the reaction to provide chlorosulfonated, vulcanizable polyethylene elastomers, containing greater than 25 weight percent to about 45 weight percent bound chlorine and about 0.5 to about 3 weight percent sulfur.
Claim 8
Dependent Claim
182 words
A process for vapor phase chlorosulfonation or polyethylene with chlorine and sulfur dioxide comprising mixing a finely divided inorganic compound that is inert to chlorine and sulfur dioxide in the defined process, has a dielectric constant of greater than about 40, a specific conductivity (Ω -1 cm -1 ) value of greater than 10 -13 to less than 10 -1 , and an average particle size of about 0.01 to 10 microns, having the general formual ABO 3 wherein A is Na, K, Rb, Ca, Bi, Sr, Ba, Pb, Gd; and B is Ti, Sn, Zr, Nb, Ta, W, and mixtures thereof, present in amounts from about 1 to 15 weight parts per 100 weight parts of polyethylene, with powdered polyetheylene and chlorosulfonating the polyethylene at an initial temperature between about 20° C. and 70° C., raising the temperature to at least about the crystalline melting point of the polyethylene and continuing the reaction to provide chlorosulfonated, vulcanizable polyethylene elastomers, containing greater than 25 weight percent to about 45 weight percent bound chlorine and about 0.5 to about 3 weight percent sulfur.
Claim 9
Dependent Claim
139 words
A process of claim 6 wherein the chlorosulfonate ion reaction is conducted in a fluidized bed, the polyethylene contains less than 10 weight percent copolymerized alpha olefins containing 3 to 6 carbon atoms, has a density from about 0.91 to about 0.97, a crystalline melting point of about 100° C. to about 140° C., a melt index of 0.01 to less than 30 and a particle size from about 50 to 800 microns, the inorganic compound is selected from the group consisting of titanium dioxide, barium titanate, lead titanate, and barium-lead titanate-niobate, having an average particle size of about 0.05 to 2 microns, the volume ratio of chlorine to sulfur dioxide is from about 20:1 to about 2:1, and the reaction temperature is raised from about 100° C. to about 120° C. to complete the chlorosulfonation of the polyethylene.
Claim 10
Dependent Claim
67 words
The process of claim 7 where in the polyethylene is polyethylene, has a melt index from 0.2 to 18, a particle size from 100 to 600 microns and an average particle size range of about 200 to 300 microns, and the volume ratio of chlorine to sulfur dioxide is from about 4:1 to 1:1 and the titanium compound is titanium dioxide or barium titanate, under actinic light.
Claim 11
Dependent Claim
21 words
The process of claim 8 wherein the inorganic compound is rutile titanium dioxide with a particle size of about 0.2±0.05 microns.
Claim 12
Dependent Claim
20 words
The process of claim 8 wherein the inorganic compound is barium titanate with a particle size of about 0.2±0.05 microns.
Claim 13
Dependent Claim
13 words
A process of claim 6 wherein the inorganic compound is a titanium compound.
References Cited (Backward Citations)
USPTO Annuity & Maintenance Windows
| Annuity Stage | Window Opens | Payment Deadline | Surcharge Period Until | Estimated Fee | Status |
|---|---|---|---|---|---|
| 3.5 Years (Year 4) | 1987-06-05 | 1987-12-05 | 1988-06-05 | $2000.00 | Window Closed / Lapsed |
| 7.5 Years (Year 8) | 1991-06-05 | 1991-12-05 | 1992-06-05 | $3760.00 | Window Closed / Lapsed |
| 11.5 Years (Year 12) | 1995-06-05 | 1995-12-05 | 1996-06-05 | $7700.00 | Window Closed / Lapsed |